TA16 titanium alloy wire processing process

A technology of titanium alloy wire and processing technology, which is applied in the field of titanium alloy processing, can solve the problems of high cost, time-consuming and labor-intensive manual grinding, and long working hours, so as to reduce working hours, improve yield, and ensure grain size and roughness Effect

Inactive Publication Date: 2018-08-21
SHAANXI XINGSHENG NEW MATERIALS CO LTD
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This patent has the following disadvantages compared with the traditional titanium alloy wire processing technology: first, a large number of pickling processes are used, which causes great pollution to the environment; second, manual grinding is time-consuming and laborious; third, the yield of titanium alloy wire is low , long working hours, high cost, difficult to meet the growing domestic market demand

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] The invention will be described in further detail below in conjunction with specific embodiments.

[0014] A kind of TA16 titanium alloy wire material processing technique of the present invention, the concrete steps that comprise are:

[0015] (1) Squaring: Squaring the TA16 titanium alloy ingot of Φ455×2100mm to 150×150mm, then grinding, then cutting to 85×85mm, and finally grinding to obtain a white skin square with a single weight of 30-35Kg . The weight of a single disc in the present invention is 30-35Kg, which is the most suitable single weight for the power selection of the wire drawing machine, and is obtained from the comprehensive consideration of multiple links such as handling, drawing, and heating.

[0016] (2) Rolling: The 85×85mm square white skin is rolled into a black skin wire rod with a diameter of Φ10.0mm and a unit weight of 30Kg.

[0017] (3) Rounding at high temperature: heat the Φ10.0mm black-skinned wire to 800°C, round it to a Φ9.5mm disc, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a TA16 titanium alloy wire processing process. The TA16 titanium alloy wire processing process comprises the following steps of: extracting, rolling, high-temperature rounding,high-temperature drawing and room-temperature drawing, thereby obtaining the TA16 titanium alloy wire with a diameter being Phi 1.0 mm. According to the TA16 titanium alloy wire processing process disclosed by the invention, the high-temperature rounding step is increased, so that ovality of the rolled wire is reduced through a wire rod with a diameter being Phi 9.5 mm while a rolled back-skin wire is heated to a high temperature being about 800 DEG C, and therefore, the yield is increased; the skin of the high-temperature rounded wire is pulled off through a centerless lathe, and skin of thehigh-temperature drawn wire is pulled off through high-temperature wire drawing, so that surface defects can be effectively reduced, and the surface grain size and roughness of the wire are ensured;and compared with a conventional process, the TA16 titanium alloy wire processing process has the advantages of cancelling a plurality of acid-floating and manual-grinding processes in a white-skin wire processing process as well as a process of performing acid-alkaline washing while the wire is drawn to be 3.0 mm, so that the environmental protection purpose is realized, and working hours can bereduced by 1 / 3.

Description

technical field [0001] The invention relates to the technical field of titanium alloy processing, in particular to a TA16 titanium alloy wire processing technology. Background technique [0002] In the traditional titanium alloy wire processing technology, in the white skin wire processing stage, in order to ensure that the surface defects of the wire are cleaned up, multiple stages of acid bleaching and manual grinding are required, and when the wire diameter is drawn to 3.0mm, another Acid and alkali cleaning to ensure a good surface of the wire. For example, the Chinese invention patent with the publication number CN103480685A published on January 1, 2014 is called a processing method of TC18 alloy wire, including vacuum melting, upsetting forging, precision forging, heat treatment, rolling, annealing, and rounding , Mechanical peeling, pickling and grinding, multiple vacuum annealing and stretching. This patent has the following disadvantages compared with the traditio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B21C37/04
CPCB21C37/047
Inventor 李敏
Owner SHAANXI XINGSHENG NEW MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products