Nano-titania and styrene-acrylic emulsion composite thermal insulation coating

A technology of nano-titanium dioxide and styrene-acrylic emulsion, which is applied in the direction of reflection/signal coatings, etc., to achieve the effect of improving service life, reducing heat accumulation, and preventing ultraviolet rays

Inactive Publication Date: 2018-09-07
FOSHAN KANGDONG LIGHTING TECH CO LTD
View PDF0 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the existing thermal insulation coatings are single-function thermal insulation coatings, and there is no qualified, high-safety, high-reflection, high-radiation water-based acrylic thermal insulation coating for sale.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Nano-titania and styrene-acrylic emulsion composite thermal insulation coating

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A nano-titanium dioxide styrene-acrylic emulsion composite heat-insulating coating, its raw materials include the following components by weight: 50 parts of styrene-acrylic emulsion, 10 parts of xonotlite active slurry, 5 parts of hollow glass beads, 3 parts of nano-titanium dioxide, 5 parts of diatomite, 8 parts of titanium dioxide, 8 parts of heat-reflecting insulation powder, 3 powders of mica powder, 3 parts of alumina powder, 0.5 parts of antifungal agent, 0.4 parts of wetting agent, 0.9 parts of dispersing agent, and 0.1 part of wetting agent 0.3 parts of defoamer, 1.0 parts of coalescent, 0.5 parts of thickener, 1 part of leveling agent, 20 parts of deionized water.

[0027] The preparation method of the xonotlite active slurry is to calcinate calcium carbide slag at a temperature of 800°C for 3 hours, then digest it with boiling water, and then according to the CaO and SiO2 material ratio of 1.5:1, water to solid phase Add the prepared calcium raw material, sil...

Embodiment 2

[0038]A kind of nano-titanium dioxide styrene-acrylic emulsion composite thermal insulation coating, its raw material comprises the following components by weight: 60 parts of styrene-acrylic emulsion, 20 parts of xonotlite active slurry, 8 parts of hollow glass microspheres, 5 parts of nano-titanium dioxide, 10 parts of diatomite, 12 parts of titanium dioxide, 12 parts of heat-reflecting heat insulating powder, 6 powders of mica powder, 6 powders of alumina powder, 0.8 parts of antifungal agent, 0.8 parts of wetting agent, 1.5 parts of dispersing agent, and 0.3 parts of wetting agent 0.8 parts of defoamer, 2.5 parts of film-forming aid, 0.8 parts of thickener, 3 parts of leveling agent, 50 parts of deionized water.

[0039] The preparation method of the xonotlite active slurry is to calcinate calcium carbide slag at a temperature of 1000°C for 2 hours, then digest it with boiling water, and then according to the CaO and SiO2 material ratio of 1.5:1, water and solid phase Add ...

Embodiment 3

[0050] A kind of nano-titanium dioxide styrene-acrylic emulsion composite thermal insulation coating, its raw material comprises the following components by weight: 55 parts of styrene-acrylic emulsion, 15 parts of xonotlite active slurry, 6 parts of hollow glass microspheres, nanometer TiO 4 parts, 8 parts of diatomite, 9 parts of titanium dioxide, 9 parts of heat-reflecting insulation powder, 5 parts of mica powder, 5 parts of alumina powder, 0.6 parts of antifungal agent, 0.6 parts of wetting agent, 1.2 parts of dispersing agent, and 0.2 parts of wetting agent 0.6 parts of defoamer, 1.5 parts of film-forming aid, 0.7 parts of thickener, 2 parts of leveling agent, and 35 parts of deionized water.

[0051] The preparation method of the xonotlite active slurry is to calcinate calcium carbide slag at a temperature of 900° C. for 2.5 hours, then digest it with boiling water, and then according to the ratio of CaO and SiO2 to 1.5:1, water to solid The mass ratio of the phases is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention provides a nano-titania and styrene-acrylic emulsion composite thermal insulation coating. The composite thermal insulation coating comprises raw materials in parts by weight as follows:50-60 parts of styrene-acrylic emulsion, 10-20 parts of active xonotlite slurry, 5-8 parts of hollow glass beads, 3-5 parts of nano-titania, 5-10 parts of diatomite, 8-12 parts of titanium dioxide, 8-12 parts of heat reflection thermal insulation powder, 3-6 parts of mica powder, 3-6 parts of alumina powder, 0.5-0.8 parts of a mildew preventive, 0.4-0.8 parts of a wetting agent, 0.9-1.5 parts ofa dispersing agent, 0.1-0.3 parts of a humectant, 0.3-0.8 parts of a defoamer, 1.0-2.5 parts of a coalescing agent, 0.5-0.8 parts of a thickener, 1-3 parts of a leveling agent and 20-50 parts of deionized water.

Description

technical field [0001] The invention relates to a heat-insulating coating, in particular to a nano-titanium dioxide styrene-acrylic emulsion composite heat-insulating coating and a preparation method thereof. Background technique [0002] "Heat insulation coating": refers to a functional water-based coating developed in recent years that blocks, reflects, and radiates near-infrared heat from the sun to insulate and cool the roof, save energy and reduce consumption. It has heat insulation, waterproof, antirust, anticorrosion , short construction period and quick effect, fully replace the water spray system, thermal insulation cotton, foam sponge, interlayer iron sheet, etc. There are three main types of thermal insulation coatings in terms of characteristics and principles, insulating conductive thermal insulation coatings, reflective thermal insulation coatings and radiant heat insulation coatings. In addition to the above three types of heat insulation coatings, a heat insu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/14C09D5/33
CPCC09D125/14C08K3/34C08K7/28C08K2003/2241C08K2201/011C09D5/004
Inventor 邓雪
Owner FOSHAN KANGDONG LIGHTING TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com