Preparation method of composite film

A composite membrane and thin film technology, applied in the field of composite membranes, can solve the problems of difficulty in preparing MOF, weak interaction, complicated steps, etc., and achieve the effects of easy scale-up operation, mild conditions, and good application prospects.

Active Publication Date: 2018-09-14
NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
View PDF1 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the weak interaction between MOF and support, it is difficult to nucleate and grow on the support surface, so it is difficult to prepare dense MOF
The secondary growth method introduces seeds on the surface of the carrier in advance, and then synthesizes and prepares the MOF film. This is a meth

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of composite film
  • Preparation method of composite film
  • Preparation method of composite film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] In this example, the ZIF-8-organosilicon composite film is constructed based on the metal-organic framework ZIF-8, and the preparation method is as follows:

[0041] (1) Preparation of ZIF-8-organosilicon precursor solution

[0042] (1-1) Synthesis of ZIF-8

[0043] The preparation of ZIF-8 adopts the reported synthesis method, specifically: 258mg of zinc nitrate and 263mg of dimethylimidazole were dissolved in 20mL of methanol respectively to obtain two solutions; then, these two solutions were mixed and stirred again A milky white solution was obtained in 5 minutes; the milky white solution was left to age for 24 hours, the product obtained was washed with methanol for 4 to 5 times, and finally the product was dried in an oven at 80 degrees for 24 hours to obtain ZIF-8.

[0044] The SEM picture of the ZIF-8 that above-mentioned makes is as figure 1 As shown, the average particle size of the molecular sieve is about 50nm.

[0045] (1-2) Synthesis of organosilicon pr...

Embodiment 2

[0058] In this example, the CAU-1-organosilicon composite film is constructed based on the metal-organic framework CAU-1, and the preparation method is as follows:

[0059] (1) Preparation of CAU-1-organosilicon precursor solution

[0060] (1-1) Synthesis of CAU-1

[0061] The preparation of CAU-1 adopts the reported synthesis method, specifically: add aluminum trichloride hexahydrate and 0.874g of aminoterephthalic acid into a 70mL polytetrafluoroethylene-lined kettle, and then add 60mL of React in methanol at 125°C for 5 hours, wash the product with methanol for 3 to 5 times, and finally dry it in a vacuum oven at 150°C for 48 hours to obtain CAU-1.

[0062] The SEM image of CAU-1 prepared above is as follows Figure 6 As shown, the average particle size of CAU-1 is about 50nm.

[0063] (1-2) Synthesis of organosilicon precursor solution

[0064] Mix 0.0206g of concentrated hydrochloric acid, 2.0394g of absolute ethanol and 6g of deionized water to obtain a hydrochloric ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Average particle sizeaaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a preparation method of a composite film. By the preparation method, an MOF material is combined with an organosilicone precursor material to form an MOF-organosilicone composite film on the surface of a carrier through high-temperature roasting. The composite film is continuous and compact, integrates the advantages of high throughput and a strong carrier binding force of organosilicone and the advantage of strong molecular sieving capacity of the MOF material, solves the problem of a weak bonding force between the composite film prepared based on MOF material and the carrier, and shows relatively high molecular sieving capacity and H2 permeation flux, and has a relatively good application prospect in the field of gas separation, gas purification and the like.

Description

technical field [0001] The present invention relates to the field of composite membranes, in particular to a preparation method for constructing organic-inorganic hybrid composite membranes based on metal-organic framework materials. Gas selective permeability. Background technique [0002] Metal-organic frameworks (MOFs) are a class of porous materials with specific topological structures and regular pore sizes formed by the connection of metal centers or metal clusters with organic ligands in the form of coordination bonds. Compared with other porous materials, MOFs have a larger specific surface area, and their structure, porosity, and pore structure can also be adjusted with different metals or ligands, and functional modification can also be performed. These excellent properties This makes MOFs materials have good potential application value in the fields of adsorption and separation, catalysis and sensors. [0003] The preparation methods of MOF membrane mainly inclu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01D69/12B01D67/00B01D53/22
CPCB01D53/228B01D67/0079B01D69/12B01D53/22B01D67/00
Inventor 陈亮杜红斌孔春龙张秋菊
Owner NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap