Preparation method of antiskid glazed tile

A technology for glazed tiles and preparation steps, applied in the field of preparation of anti-slip glazed tiles, can solve the problem that the anti-slip performance cannot be further improved, and achieve the effects of improving the anti-slip performance, increasing the friction force, and improving the roughness

Inactive Publication Date: 2018-09-21
万玉梅
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The technical problem mainly solved by the present invention is: Aiming at the problem that the anti-skid performance of traditional glazed tiles cannot be further improved, a preparation method of anti-skid glazed tiles is provided

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0023] In parts by weight, iron ore slag, copper slag, and mica slag are placed in a ball mill for ball milling, and a 120-mesh sieve is passed to obtain a slag mixture; in parts by weight, 10 parts of Suzhou soil, 8 parts of talcum powder, 60 parts of wollastonite and 30 parts of Kuancheng soil are ball milled in a ball mill and passed through a 180-mesh sieve to obtain a mixed powder; in parts by weight, 30 parts of straw, 30 parts of cotton stalk and 30 parts of walnut shell are placed in a pulverizer Grinding in medium and passing through a 120-mesh sieve to obtain mixed slag; in parts by weight, 20 parts of mixed slag, 5 parts of secondary sedimentation tank sludge, and 40 parts of water are placed in a fermentation kettle at a temperature of 35 ° C and a rotation speed of Under the condition of 200r / min, ferment for 8 days to obtain the fermented mixed solution; in parts by weight, 30 parts of mixed powder, 20 parts of fermented mixed solution, and 60 parts of water are p...

example 2

[0025] In parts by weight, 10 parts of Suzhou soil, 8 parts of talcum powder, 60 parts of wollastonite, and 30 parts of Kuancheng soil are placed in a ball mill for ball milling, and a 180-mesh sieve is passed to obtain a mixed powder; 30 parts of stalks, 30 parts of cotton stalks, 30 parts of walnut shells are placed in a pulverizer and pulverized, and passed through a 120-mesh sieve to obtain mixed slag; in parts by weight, 20 parts of mixed slag, 5 parts of secondary sedimentation tank sludge, 40 parts of water are placed in a fermentation tank, and fermented for 8 days at a temperature of 35°C and a rotating speed of 200r / min to obtain a fermentation mixture; in parts by weight, 30 parts of mixed powder and 20 parts of fermentation mixture, Put 60 parts of water in the mixer, stir and mix for 50 minutes at a speed of 200r / min to obtain a mixed slurry, then place the mixed slurry in a compression molding machine, and mold it under a pressure of 5MPa. The adobe is obtained, ...

example 3

[0027] In parts by weight, iron ore slag, copper slag, and mica slag are placed in a ball mill for ball milling, and a 120-mesh sieve is passed to obtain a slag mixture; in parts by weight, 10 parts of Suzhou soil, 8 parts of talcum powder, 60 parts of wollastonite and 30 parts of Kuancheng soil are ball milled in a ball mill and passed through a 180-mesh sieve to obtain a mixed powder; in parts by weight, 30 parts of mixed powder and 60 parts of water are placed in a mixer, Under the condition of 200r / min, stir and mix for 50min to obtain a mixed slurry, then place the mixed slurry in a compression molding machine, and mold it under a pressure of 5MPa to obtain a brick, then place the brick in an oven, Under the condition of 110°C, dry to constant weight to obtain dry bricks; in parts by weight, 5 parts of slag mixture, 40 parts of clay, 10 parts of bacterial cellulose, 10 parts of bauxite, 5 parts of phospholipid, 60 parts of Put a portion of water in a mixer, and stir and m...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of an antiskid glazed tile, and belongs to the technical field of building materials. The method comprises the steps that Suzhou clay, talcum powder, wollastonite and kuancheng soil are mixed, ball-milled and screened to obtain mixed powder; straw, cotton stalk, walnut shells are mixed, smashed and screened to obtain mixed shred residues; the mixed shred residues, secondary sedimentation tank sludge and water are mixed and fermented to obtain a fermentation mixing solution; the mixed powder, the fermentation mixing solution and water are stirred andmixed, and compression molding and drying are performed to obtain a dry green brick; the slag mixture, clay, bacterial cellulose, bauxite, phospholipid and water are stirred and mixed to obtain modified glaze; the modified glaze is applied to the surface of the dried green brick, nitrogen is charged for a high-temperature reaction, and step-by-step cooling, calcination and cooling are performed to obtain the antiskid glazed tile. The antiskid glazed tile has the excellent anti-skid performance.

Description

technical field [0001] The invention discloses a preparation method of an anti-slip glazed tile, which belongs to the technical field of building materials. Background technique [0002] Glazed tiles are a widely used building material product. By glazing and firing on the surface of the adobe, a rich decorative effect can be obtained, and the glaze is anti-fouling and easy to clean, especially suitable for kitchen and bathroom decoration with heavy water vapor and more stains. For printing series products, the printing layer can also be protected from abrasion by glaze. However, glazed products are mostly flat decorations, and the smooth and flat glazed surface is not non-slip, so it is not suitable for ground paving. For this reason, people set anti-slip lines with concave-convex lines on the mold, so that the stamped bricks also have corresponding lines, but after glazing, the anti-slip lines will become blurred, and this method cannot form dense anti-slip protrusio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C03C8/18C04B41/86
CPCC03C8/18C04B41/5022C04B41/86
Inventor 万玉梅朱冬梅
Owner 万玉梅
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com