Novel hot dip coating low-cost low-energy-consumption aluminum tin alloy containing Ti and Y

An aluminum-tin alloy and hot-dip plating technology, which is applied in the field of alloys, can solve problems such as high energy consumption, low product output, and backward technology, and achieve the effect of delaying corrosion

Inactive Publication Date: 2018-09-28
GUANGZHOU YUZHI TECH CO LTD
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of the existing hot-plating production lines have disadvantages such as backward technology, low product output, poor product quality, high production cost, high energy consumption, weak environmental protection measures, and often cause serious environmental pollution. Such production lines are difficult to meet the needs of my country's national economic take-off

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A new type of low-cost and low-energy hot-dip aluminum-tin alloy containing Ti and Y. In terms of weight percentage, the composition of the alloy is Na: 0.3wt.%, Ti: 1.5wt.%, Ca: 0.4wt.%, Sn: 15.0wt.%, Y: 0.2wt.%, Yb: 0.3wt.% ,P:0.1wt.%, the balance is aluminum. The preparation method of the above-mentioned novel hot-dip plating low-cost and low-energy-consumption aluminum-tin alloy containing Ti and Y includes the following steps: adding the above-mentioned raw materials into an argon-protected induction furnace, and using a silicon carbide crucible; The raw materials are added to the induction furnace protected by the atmosphere, and a silicon carbide crucible is used; the alloy solution is formed by induction heating to 600-700 degrees, and the electromagnetic stirring effect is fully stirred for about 10 minutes; the alloy liquid is kept at 600-700 degrees and left standing After 10 minutes, it is cast into the same level equipment as the hot top for semi-continuou...

Embodiment 2

[0019] A new type of low-cost and low-energy hot-dip aluminum-tin alloy containing Ti and Y. In terms of weight percentage, the composition of the alloy is Na:0.5wt.%, Ti:1.8wt.%, Ca:0.8wt.%, Sn:22.0wt.%, Y:0.4wt.%, Yb:0.5wt.% ,P:0.2wt.%, the balance is aluminum. The preparation method of the above-mentioned novel hot-dip plating low-cost and low-energy-consumption aluminum-tin alloy containing Ti and Y includes the following steps: adding the above-mentioned raw materials into an argon-protected induction furnace, and using a silicon carbide crucible; The raw materials are added to the induction furnace protected by the atmosphere, and a silicon carbide crucible is used; the alloy solution is formed by induction heating to 600-700 degrees, and the electromagnetic stirring effect is fully stirred for about 10 minutes; the alloy liquid is kept at 600-700 degrees and left standing After 10 minutes, it is cast into the same level equipment as the hot top for semi-continuous cast...

Embodiment 3

[0022] A new type of low-cost and low-energy hot-dip aluminum-tin alloy containing Ti and Y. In terms of weight percentage, the composition of the alloy is Na: 0.4wt.%, Ti: 1.6wt.%, Ca: 0.5wt.%, Sn: 18.0wt.%, Y: 0.3wt.%, Yb: 0.4wt.% ,P:0.1wt.%, the balance is aluminum. The preparation method of the above-mentioned novel hot-dip plating low-cost and low-energy-consumption aluminum-tin alloy containing Ti and Y includes the following steps: adding the above-mentioned raw materials into an argon-protected induction furnace, and using a silicon carbide crucible; The raw materials are added to the induction furnace protected by the atmosphere, and a silicon carbide crucible is used; the alloy solution is formed by induction heating to 600-700 degrees, and the electromagnetic stirring effect is fully stirred for about 10 minutes; the alloy liquid is kept at 600-700 degrees and left standing After 10 minutes, it is cast into the same level equipment as the hot top for semi-continuou...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a novel hot dip coating low-cost low-energy-consumption aluminum tin alloy containing Ti and Y. The alloy comprises the ingredients of, in percentage by weight, 0.3-0.5% of Na,1.5-1.8% of Ti, 0.4-0.8% of Ca, 15.0-22.0 % of Sn, 0.2-0.4% of Y, 0.3-0.5% of Yb, 0.1-0.2% of P and the balance aluminum. By means of the hot dip coating aluminum tin alloy, the key problems that thetechnology in the present hot dip coating alloy field lags behind, product quality is poor, the product cost is high, energy consumption is large, and the like are solved, and in the near future, thealloy will be applied to more fields more widely.

Description

technical field [0001] The invention relates to the technical field of alloys, in particular to an aluminum-tin alloy. Background technique [0002] Reinforced concrete refers to a composite material formed by adding steel mesh, steel plates or fibers to concrete. Corrosion of steel bars and freeze-thaw cycles of concrete can damage the structure of concrete. When rebar corrodes, the rust spreads, cracking the concrete and losing the bond between the rebar and concrete. When water penetrates the concrete surface and enters the interior, the frozen and condensed moisture expands in volume, and after repeated freeze-thaw cycles, cracks are formed in the concrete microscopically and continue to deepen, thereby crushing the concrete and causing permanent and irreversible damage to the concrete damage. Corrosion of steel bars in highway bridges is relatively common, which seriously threatens the safety and durability of highway bridge structures. [0003] Corrosion of steel b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C22C21/00C22C1/02C23C2/12C23C2/40
CPCC22C21/003C22C1/026C23C2/12C23C2/40
Inventor 杨长江
Owner GUANGZHOU YUZHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com