Handle rubber material for baseball bat

A technology for baseball bats and handles, applied in the field of polyurethane materials, which can solve the problems of wear resistance and poor anti-skid hand feeling, and achieve the effects of soft hand feeling, good support and excellent tear resistance

Inactive Publication Date: 2018-10-02
TIANCHANG ZHENGMU ALUMINUM TECH
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Yet wear-resisting, non-slip, poor handfeeling performance using strips of cloth, adhesive tape or rubber as the wrapping material of the baseball bat handle cannot satisfy people's needs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A handle rubber material for baseball bats, the raw materials of which in parts by weight include: 20 parts by weight of a surface layer material and 60 parts of a foamed bottom material; wherein the raw material of the surface layer material by weight includes: a water-based polycarbonate with a solid content of 40% Type polyurethane resin 19.1 parts, polyurethane thickener 0.35 parts, polyoxyethylene polyoxypropanol amine ether 0.24 parts, fatty acid ester sulfate 0.2 parts, hand-feeling agent 0.11 parts; foam base material raw materials by weight include: solid content It is 53.6 parts of 30% water-based polyether polyurethane resin, 1.3 parts of polyacrylate thickener, 2 parts of nano white carbon black, 2 parts of microsphere foaming powder, and 1.1 parts of carbodiimide.

Embodiment 2

[0017] A handle rubber material for baseball bats, the raw materials of which in parts by weight include: 40 parts by weight of surface layer material and 80 parts of foamed bottom material; wherein, in parts by weight, the raw material of surface layer material includes: waterborne polycarbonate with a solid content of 60% Type polyurethane resin 37.32 parts, polyurethane thickener 1.1 parts, polydimethylsiloxane 0.47 parts, polyoxyethylene alkyl phenol ether 0.5 parts, hand-feeling agent 0.61 parts; foam base material raw materials by weight include: solid content It is 68.33 parts of 60% water-based polyether polyurethane resin, 2.28 parts of polyacrylate thickener, 3.42 parts of nano diatomaceous earth, 3.42 parts of microsphere foaming powder, and 2.55 parts of aziridine.

Embodiment 3

[0019] A handle rubber material for baseball bats, the raw materials of which in parts by weight include: 25 parts by weight of a surface layer material and 75 parts of a foamed bottom material; wherein, in parts by weight, the raw material of the surface layer material includes: a water-based polycarbonate with a solid content of 45% Type polyurethane resin 23.5 parts, polyurethane thickener 0.59 parts, polyoxyethylene polyoxypropanolamine ether 0.28 parts, fatty acid ester sulfate 0.28 parts, hand-feeling agent 0.35 parts; foam base material raw materials by weight include: solid content It is 65.22 parts of 40% water-based polyether polyurethane resin, 1.96 parts of polyacrylate thickener, 2.93 parts of nano white carbon black, 2.93 parts of microsphere foaming powder, and 1.96 parts of carbodiimide.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a handle rubber material for a baseball bat. The handle rubber material for the baseball bat comprises the following raw materials: a surface layer material and a foaming bottom layer material, wherein the surface layer material comprises the following raw materials: water-based polycarbonate type polyurethane resin, a polyurethane thickening agent, a defoaming agent, a wetting agent and a hand feeling agent; and the foaming bottom layer material comprises the following raw materials: water-based polycarbonate type polyurethane resin, a polyacrylic ester thickening agent, fillers, a foaming agent and a crosslinking agent. The handle rubber material has the characteristics of excellent wear resistance, air permeability and moisture permeability as well as good hand feeling, has a good air-permeable and moisture-permeable effect, and is applicable to the baseball bat.

Description

Technical field [0001] The invention relates to the technical field of polyurethane materials, in particular to a handle rubber material for baseball bats. Background technique [0002] A baseball bat is a bat used by a batter to hit the ball in a baseball game. It has a cylindrical shape with a smooth surface and no cross-section joints. At present, the commonly used baseball bats are made of metal materials. The two ends of the metal bats must be sealed. The length of the bat must not exceed 1.07 meters. The diameter of the thickest part must not exceed 7 cm. 2.45 cm. To make it easier to hold the stick, it can be wrapped with cloth, tape or rubber from one end of the grip to a length of 45.7 cm. However, the use of cloth strips, tape or rubber as the wrapping material of the baseball bat handle has poor wear resistance, non-slip resistance, and poor feel, which cannot meet people's needs. Summary of the invention [0003] Based on the technical problems existing in the backg...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B32B27/40B32B27/06B32B27/20B32B27/18C08L75/04C08L71/02C08L83/04C08K5/41C08L75/08C08L33/04C08K7/26C08K3/36C08J9/32
CPCB32B27/065B32B27/18B32B27/20B32B27/40B32B2266/0278B32B2307/554B32B2307/5825B32B2307/724B32B2307/726B32B2307/744C08J9/0061C08J9/0071C08J9/32C08J2375/08C08J2433/04C08K3/36C08K7/26C08K2201/011C08L75/04C08L2205/025C08L2205/035C08L71/02C08L83/04C08K5/41
Inventor 周良正
Owner TIANCHANG ZHENGMU ALUMINUM TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com