Efficient breathing humidifying type diatom ooze and preparation method thereof

A technology of diatom mud and humidity control, which is applied in the field of interior wall decoration wall materials, can solve the problems of molecular sieve structure damage, more closed cells of diatom earth, and lower performance of diatom mud breathing and humidity control, etc., to achieve structural integrity, breathing Powerful humidity control function and excellent breath humidity control performance

Pending Publication Date: 2018-10-09
山东泥工坊环保科技有限公司
View PDF7 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When the existing diatom mud wall material is produced, the diatomite raw material adopts calcined diatomite as the main filler. The high temperature causes the original molecular sieve structure to be damaged to a lesser extent, and the porosity of diatomite is closed due to calcination. There are many pores, and due to the low existing industry standards and technical limitations, the content of diatomite is generally between 15% and 30%, which greatly reduces the respiratory and humidity control performance of diatom mud products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Efficient breathing humidifying type diatom ooze and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] The raw materials of the following weight components are selected: 61 parts of diatomite, 12 parts of zeolite powder, 15 parts of dolomite powder, 3 parts of white clay, 1.2 parts of rutile titanium dioxide, 0.4 part of hydroxypropyl methylcellulose ether, and 0.2 parts of nano-titanium dioxide 4 parts, 4 parts of imported redispersible rubber powder, 0.2 parts of antifungal agent.

[0034] Among them, the diatomite is water-selected non-combustible diatomite, the content of silicon dioxide in it is 94%, and the mesh number of diatomite is 255 mesh.

[0035] Among them, the zeolite powder is staphilite, the crystal form is single crystal or single crystal combination, and the mesh number is 600 mesh.

[0036] Among them, the viscosity specification of hydroxypropyl methylcellulose ether is 80000mPa.s.

[0037] Among them, the mesh number of dolomite powder is 800 mesh.

[0038] Step 1. First, use a dry powder high-speed mixer to pre-mix 3 parts of dolomite powder, 0.4...

Embodiment 2

[0042] The raw materials of the following weight components are selected: 62 parts of diatomite, 11 parts of zeolite powder, 16 parts of dolomite powder, 5 parts of white clay, 1.4 parts of rutile titanium dioxide, 0.3 part of hydroxypropyl methylcellulose ether, and 0.3 parts of nano-titanium dioxide 5 parts of imported redispersible rubber powder and 0.2 parts of antifungal agent.

[0043] Among them, the diatomite is water-selected non-combustible diatomite, the content of silicon dioxide in it is 92%, and the mesh number range of the diatomite is 300 mesh.

[0044] Among them, the zeolite powder is staphilite, the crystal form is single crystal or single crystal combination, and the mesh number is 500 mesh.

[0045] Among them, the viscosity specification of hydroxypropyl methylcellulose ether is 60000mPa.s.

[0046] Among them, the mesh number of dolomite powder is 800 mesh.

[0047] Step 1. First, use a dry powder high-speed mixer to pre-mix 3 parts of dolomite powder,...

Embodiment 3

[0051] The raw materials of the following weight components are selected: 64 parts of diatomite, 15 parts of zeolite powder, 18 parts of dolomite powder, 5 parts of white clay, 1.5 parts of rutile titanium dioxide, 0.5 part of hydroxypropyl methylcellulose ether, and 0.3 parts of nano-titanium dioxide 5 parts of imported redispersible rubber powder and 0.2 parts of antifungal agent.

[0052] Among them, the diatomite is water-selected non-combustible diatomite, the content of silicon dioxide in it is 96%, and the mesh number of diatomite is 2755 mesh.

[0053] Among them, the zeolite powder is staphilite, the crystal form is single crystal or single crystal combination, and the mesh number is 700 mesh.

[0054] Among them, the viscosity specification of hydroxypropyl methylcellulose ether is 100000mPa.s.

[0055] Among them, the mesh number of dolomite powder is 800 mesh.

[0056] Step 1. First, use a dry powder high-speed mixer to pre-mix 3 parts of dolomite powder, 0.5 par...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses efficient breathing humidifying type diatom ooze and a preparation method thereof, and relates to the technical field of an interior decoration wall material. The efficient breathing humidifying type diatom ooze is prepared from the following raw materials in parts by weight: 60 to 65 parts of diatomite, 10 to 15 parts of zeolite powder, 15 to 18 parts of dolomite powder, 3to 5 parts of white clay, 1 to 1.5 parts of rutile type titanium dioxide, 0.3 to 0.5 part of hydroxypropyl methylcellulose ether, 0.2 to 0.3 part of nanometer titanium dioxide, 4 to 5 parts of imported redispersible rubber powder and 0.2 part of a mildewproof agent. Water concentration diatomite serves as a main raw material and is not calcined, the molecular sieve structure of the diatomite is integrated, the activity is higher, the breathing humidifying property is better, the mass ratio content of the water concentration diatomite is up to 60 percent or more through formula adjustment andis far higher than that of other products of the same industry, powder is prevented from being removed through dry rubbing, high construction performance is maintained, the breathing humidifying performance is strong, and the defect of low hygroscopic capacity of the diatomite under the condition of moderate humidity is remedied by adding microporous zeolite powder with a certain ratio.

Description

technical field [0001] The invention belongs to the technical field of interior wall decoration wall materials, and in particular relates to a high-efficiency breathing and humidity-regulating diatom mud and a preparation method thereof. Background technique [0002] Diatom mud wall material is a kind of dry powder interior wall decoration coating material prepared with inorganic gelling substance as the main bonding material and diatom material as the main functional filler. It has the functions of eliminating formaldehyde, purifying air, adjusting humidity, releasing negative oxygen ions, fire retardant, wall self-cleaning, sterilization and deodorization, etc. Because diatom mud is healthy and environmentally friendly, it is not only very decorative, but also functional. It is a new generation of indoor and outdoor decoration materials that replace wallpaper and latex paint. When the existing diatom mud wall material is produced, the diatomite raw material adopts calcine...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00C04B14/08C04B14/04
CPCC04B14/047C04B14/08C04B28/001C04B14/26C04B14/305C04B24/383C04B2103/0057C04B2103/67
Inventor 韩明涛
Owner 山东泥工坊环保科技有限公司