Quick wax remover and preparing method thereof

A wax remover and fast technology, applied in the field of fast wax remover and its preparation, can solve the problems of slow wax dissolution cleaning speed, high cleaning temperature, impact, etc., and achieve the effect of not easy to decompose, strong cleaning power and wide applicability

Inactive Publication Date: 2018-10-12
YANGJIANG WEIYI POLISHING MATERIAL
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The solvent dissolution cleaning method has adverse effects on users and the surrounding environment
Water-based wax removal water is cleaned in water above 80°C through the action of surfactants, builders and other ingredients. Currently, commonly used surfactants

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0022] Example 1

[0023] In parts by weight, add 45 parts of ceric acid and 25 parts of lauric acid to the reactor in turn, start stirring, gradually increase the temperature, and control the heating rate at 1-3℃ / min. When the temperature reaches 75-80℃, go to the reactor Add a mixture of 25 parts of aniline and 25 parts of ethylenediamine until the dripping is complete, and react at a constant temperature for 1.5 hours, then increase the temperature to 130°C, add 5 parts of potassium hydroxide as a catalyst, and catalyze the reaction for 0.5 hours. 1 hour, then cool to room temperature, and pack it.

Example Embodiment

[0024] Example 2

[0025] In parts by weight, add 20 parts of lignin acid, 20 parts of oleic acid, and 10 parts of stearic acid in the reactor, start stirring, and gradually increase the temperature. The temperature increase rate is controlled at 1-3℃ / min. When the temperature reaches 75- At 80°C, add dropwise a mixture of 10 parts methylamine and 10 parts alkylaniline to the reaction kettle until the dripping is complete, react at a constant temperature for 1.5 hours, then heat up to 130°C, and add 2 parts of sodium hydroxide as Catalyst, catalyze reaction for 0.5 hour, heat preservation and maturation for 1 hour, then cool to room temperature and pack it.

Example Embodiment

[0026] Example 3

[0027] In parts by weight, add 30 parts of lignin acid, 15 parts of capric acid, and 15 parts of stearic acid to the reaction kettle, start stirring, and gradually increase the temperature. The temperature increase rate is controlled at 1-3℃ / min. When the temperature reaches 75- At 80°C, add dropwise a mixture of 15 parts of diisopropylamine and 25 parts of alkylaniline into the reaction kettle until the dripping is complete, react at a constant temperature for 1.5 hours, then heat to 130°C, and add 1 part of sodium hydroxide Use 2 parts of potassium hydroxide as a catalyst, catalyze the reaction for 0.5 hours, heat and mature for 1 hour, then cool to room temperature, and pack it.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a quick wax remover. The quick wax remover comprises the following raw materials in part by weight, 50-70 parts of straight-chain fatty acid and 30-50 parts of amine organic alkali. The quick wax remover has the beneficial effects that the wax remover prepared by using the similarity and intermiscibility principle, can be used alone, and can also be combined with an alkyl glycoside active agent to prepare wax removing water, the wax removal speed can be increased, and even the quick wax remover can be soaked in room-temperature water soluble working solution to remove wax; the quick wax remover is high in washing performance, residual dirt such as polishing wax and grease on the surface of a metal piece can be quickly and thoroughly removed, and the substrate of themetal piece cannot be damaged; (2) the quick wax remover is wide in applicability, and can be widely used in the washing process of metal, petrochemical, automobile, papermaking and other industries;(3) the quick wax remover is high in stability, unlikely to volatilize, unlikely to decompose, unlikely to burn, and safe to use; and (4) rinsing is convenient, a water film is not broken after the quick wax remover is rinsed with water, rinsing is easy, and residue is avoided.

Description

technical field [0001] The invention relates to a wax remover, in particular to a quick wax remover and a preparation method thereof. Background technique [0002] After the hardware workpiece is polished, especially after polishing with a burlap wheel and polishing wax, it is necessary to clean the wax dirt adhering to the surface of the workpiece before entering the next process. Polishing wax mainly plays the role of grinding and brightening. It has two forms: solid and liquid. The main components are abrasive, stearic acid wax, binder, anti-pressure and wear-resistant agent and other components. When high temperature is generated during polishing, the wax is adsorbed on the surface of the workpiece through van der Waals force and electrostatic force in the molten state, so the surface of the workpiece needs to be cleaned before subsequent processes. [0003] Domestic wax removal technologies mainly include solvent dissolution cleaning method and water-based wax removal ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23G1/00
CPCC23G1/00
Inventor 盘茂东
Owner YANGJIANG WEIYI POLISHING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap