Graphene anion bone shell porcelain tea set and preparation method thereof

A technology of negative ion bone and graphene, which is applied in the field of graphene negative ion bone china tea set and its preparation, can solve the problems of poor heat resistance and cold resistance, insufficient toughness, and easy breakage of the tea set, and achieve the goal of not easy to break, fine and smooth texture, good heat resistance

Inactive Publication Date: 2018-10-19
浙江纳巍健康科技有限公司
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in actual use, it is true that the heat resistance and cold resistance of the tea set are poor, and it is easy to break in the state of rapid heat and rapid cooling, and the toughness is not enough; moreover, the tea set itself is relatively fragile, and it is easy to break if it falls accidentally

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] The invention provides a graphene negative ion bone china tea set. The blank of the tea set includes the following components in weight ratio: 1 part of graphene, 1 part of carbon nanotube, 1 part of diatomite, 400 parts of kaolin, and 50 parts of feldspar , 20 parts of bone char, 1 part of spodumene, 1 part of pyrophyllite, 1 part of deep-sea shell powder, 1 part of quartz, and 1 part of silicon nitride.

[0038] Among them, graphene (two-dimensional carbon material) is a honeycomb planar film formed by carbon atoms in the form of Sp2 hybridization, also known as monoatomic layer graphite. It is the nanomaterial with the thinnest strength, the highest electrical conductivity and the strongest thermal conductivity found at present, and it is also known as the king of materials. The carrier mobility of graphene at room temperature is about 15000 cm 2 / (vs) is more than 10 times that of silicon material; the carrier mobility of graphene reaches 250000cm at low temperatur...

Embodiment 2

[0048] The invention provides a graphene negative ion bone china tea set, the blank of the tea set includes the following components by weight: 20 parts of graphene, 30 parts of carbon nanotubes, 200 parts of diatomite, 600 parts of kaolin, and 100 parts of feldspar , 400 parts of bone char, 40 parts of spodumene, 80 parts of pyrophyllite, 400 parts of deep sea shell powder, 100 parts of quartz, and 40 parts of silicon nitride.

[0049] The exterior of the tea set blank is coated with black glaze, and the black glaze includes the following components by weight: 335 parts of Wujin soil, 333 parts of Yaoli glaze fruit, and 30 parts of cobalt oxide.

[0050] The exterior of the tea set blank is coated with white glaze, which includes the following components by weight: 550 parts of feldspar, 300 parts of quartz, 150 parts of limestone, and 100 parts of Suzhou clay.

[0051] The exterior of the tea set blank is coated with azure glaze, which includes the following components by we...

Embodiment 3

[0053] The invention provides a graphene negative ion bone china tea set, the blank of the tea set includes the following components by weight: 10 parts of graphene, 20 parts of carbon nanotubes, 100 parts of diatomite, 500 parts of kaolin, and 80 parts of feldspar , 200 parts of bone char, 20 parts of spodumene, 40 parts of pyrophyllite, 200 parts of deep-sea shell powder, 50 parts of quartz, and 20 parts of silicon nitride.

[0054] The exterior of the tea set blank is coated with black glaze, and the black glaze includes the following components by weight: 240 parts of Wujin soil, 240 parts of Yaoli glaze fruit, and 18 parts of cobalt oxide.

[0055] The exterior of the tea set blank is coated with white glaze, which includes the following components by weight: 500 parts of feldspar, 275 parts of quartz, 125 parts of limestone, and 70 parts of Suzhou clay.

[0056] The outside of the tea set blank is coated with azure glaze, which includes the following components by weight...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
diameteraaaaaaaaaa
glossaaaaaaaaaa
Login to view more

Abstract

The invention discloses a graphene anion bone shell porcelain tea set. A preform body of the tea set is prepared from the following components in parts by weight: 1 to 20 parts of graphene, 1 to 30 parts of carbon nano tube, 1 to 200 parts of kieselguhr, 400 to 600 parts of kaoline, 50 to 100 parts of feldspar, 20 to 400 parts of bone black, 1 to 50 parts of spodumene, 1 to 80 parts of pyrophyllite, 1 to 400 parts of deep sea shell powder, 1 to 100 parts of quartz, and 1 to 40 parts of silicon nitride. By adopting the technical scheme, the graphene anion bone shell porcelain tea set has good heat resistance and cold resistance and is not afraid of quick-heating or snap-chilling; a tea cup is fine and smooth in texture, better in toughness, not easy to break, and not easy to fracture when falling down; in addition, the tea set can release negative ions and does not contain hazardous substances such as lead, cadmium, arsenic and mercury; the contents of negative oxygen ions released by the tea set and negative ions of hydroxide radical in tea soup are more, so that a health care effect is achieved on a human body.

Description

technical field [0001] The invention relates to the technical field of tea set production, in particular to a graphene anion bone china tea set and a preparation method thereof. Background technique [0002] China is the birthplace of world tea culture. According to textual research, about 3,000 years ago, the Shu Kingdom in Cuba began to grow tea. Wang Bao, a native of Sichuan in the Western Han Dynasty, recorded in his document "Tong Yue" that "there are all utensils for cooking tea" and that he went to Wuyang to buy tea. A complete celadon urn was unearthed from a tomb in the late Eastern Han Dynasty in Huzhou, a tea town. What attracts attention is the word "Tu" engraved on the shoulder of the celadon urn, so it is believed to be a utensil for storing tea in the Han Dynasty. The Tang Dynasty was the heyday of tea culture. During the Tang Dynasty, Emperor Zong began to set up an "official roasting" institution in Guzhu Mountain, Changxing, Zhejiang Province, which speci...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/135C04B33/36C04B41/86C03C8/00A47G19/22
CPCA47G19/2205C03C8/00C04B33/1355C04B33/36C04B41/5022C04B41/86C04B2235/3203C04B2235/3208C04B2235/3418C04B2235/3463C04B2235/3472C04B2235/3873C04B2235/425C04B2235/5288C04B41/4539C04B41/0072Y02P40/60
Inventor 吴瑛吴春金齐留明
Owner 浙江纳巍健康科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap