A kind of nano-cellulose reinforced composite photocatalyst and its preparation method and application

A nanocellulose and photocatalyst technology, applied in the field of material chemistry, can solve the problems of complex catalyst preparation process, difficult to achieve synergistic promotion, and limited modification effect, so as to promote catalytic degradation efficiency, excellent degradation performance, and increase activity site effect

Active Publication Date: 2021-03-16
CENTRAL SOUTH UNIVERSITY OF FORESTRY AND TECHNOLOGY
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But commonly used Ag-doped modified g-C 3 N 4 The preparation process of the composite catalyst is complicated, and Ag is easy to lose during the high-temperature calcination process, which greatly limits its modification effect, and it is difficult to achieve a synergistic promotion effect by doping with a single non-metal element or metal element

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of nano-cellulose reinforced composite photocatalyst and its preparation method and application
  • A kind of nano-cellulose reinforced composite photocatalyst and its preparation method and application
  • A kind of nano-cellulose reinforced composite photocatalyst and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] A preparation method of nanocellulose reinforced composite photocatalyst of the present invention, comprising the following steps:

[0044] (1) Get 20g TEMPO oxidized nanocellulose suspension (CNFs, the solid content of cellulose nanofibrils is 0.01wt%, the aspect ratio of nanofibers is about 300-600) and 0.04g silver nitrate, stir and fully dissolve;

[0045] (2) Get 20g of urea and dissolve it in the above-mentioned mixed solution, fully stir and dissolve;

[0046] (3) Place the mixed solution obtained in step (2) in a blast drying oven, and dry at 70° C. for 12 hours to obtain a precursor substance;

[0047] (4) Cover the crucible containing the precursor material with a lid, wrap a layer of tinfoil and place it in a muffle furnace. Calcinate at 550°C for 4 hours in an air atmosphere with a heating rate of 15°C / min. After natural cooling, Nanocellulose-reinforced composite photocatalyst Ag / CNFs / g-C can be obtained 3 N 4 , its XRD pattern and SEM photo are as follo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing a nanocellulose-enhanced composite photocatalyst, which includes the following steps: (1) Dissolve silver nitrate and urea in a suspension of nanocellulose, and then dry to obtain a precursor substance; (2) Nanocellulose-reinforced composite photocatalytic materials can be obtained by calcining the precursor material at 450-600°C in an oxygen or air atmosphere. The invention also discloses the nanocellulose reinforced composite photocatalyst prepared by the method and its application. The present invention innovatively utilizes the abundant carboxyl and hydroxyl groups on the nanocellulose chains and their intertwined network structure to react with Ag. + With strong chemical adsorption and physical entanglement, Ag + Fixed on the surface of carbonized nitrogen to reduce Ag + At the same time, carbon doping is achieved, and C and Ag synergistically significantly promote the catalytic degradation efficiency of carbonized nitrogen.

Description

technical field [0001] The invention belongs to the field of material chemistry, in particular to a nanocellulose-reinforced composite photocatalyst Ag / CNFs / g-C 3 N 4 And its preparation method and application. Background technique [0002] Increasingly serious environmental pollution and energy shortage have become two major problems restricting the development of human society. Finding clean energy and effectively improving environmental pollution are important issues to be solved urgently. Solar energy is considered to be the first choice to replace fossil energy due to its non-polluting, cheap, and huge reserves. Semiconductor catalysts can efficiently convert solar energy into chemical energy, and can be used for catalytic degradation of pollutants in water and photocatalytic hydrogen production. [0003] Carbonized nitrogen (g-C 3 N 4 ) is responsive to visible light, and is used for catalytic production of clean energy and photocatalytic degradation of organic po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J27/24B01J35/00B01J37/08C02F1/30C02F101/30
CPCC02F1/30B01J27/24B01J37/08B01J37/084C02F2305/10C02F2101/30B01J35/39
Inventor 吴义强卿彦田翠花罗莎李新功赵星李贤军
Owner CENTRAL SOUTH UNIVERSITY OF FORESTRY AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com