Orange red powder coating taking modified composite pigment yellow as raw material

A technology of composite pigments and powder coatings, applied in powder coatings, polyester coatings, epoxy resin coatings, etc., can solve the problems of affecting the modification effect, low bonding stability, and inability to control the particle size of inorganic cores. The effect of preventing secondary aggregation

Inactive Publication Date: 2018-11-02
ANHUI HUAHUI SUYE TECH SHARE CO LTD
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Most of these inorganic substances use inorganic nano-materials such as sepiolite and palygorskite, but the combination stability of such inorganic substances and organic pigments is not high in the encapsulation modification, and they are prone to separation, which affects the modification effect
In addition, when using inorganic nano-materials for modification, the particle size of the inorganic core cannot be controlled. When the particle size of the inorganic core is small, the composite pigment particles will also undergo secondary aggregation during the preparation process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] (1) put 16.2gFeCl 3 , 24.2gFe(NO 3 ) 3 Add it into purified water, stir at 50-60°C until completely dissolved, add 4g NaOH, stir at 80-90°C for 1 hour, a large amount of colloids are precipitated in the solution, cool to room temperature, centrifugally filter to obtain ferric hydroxide colloid, and then transfer to -10°C environment Sealed and frozen for 2 hours, and made into fine powder by ultra-fine pulverizer, and finally made into nano-powder by nano-grinder;

[0021] (2) Take 50 mL of water, 3.6 g of 30% hydrochloric acid solution, add 3.6 g of 3,3-dichlorobenzidine under stirring, continue stirring for 3 minutes, add 0.4 g of aminotriacetic acid, heat up to 90 ° C, stop heating, and stir After cooling to 40°C, 6.4 g of 30% hydrochloric acid was added, and the temperature was lowered to 0°C. Then add 6.4g of 30% sodium nitrite solution to carry out the diazotization reaction. The reaction process is completed within 2 minutes. After the reaction is completed, d...

Embodiment 2

[0028] (1) put 16.2gFeCl 3 , 24.2gFe(NO 3 ) 3 Add it into purified water, stir at 50-60°C until completely dissolved, add 4g NaOH, stir at 80-90°C for 1 hour, a large amount of colloids are precipitated in the solution, cool to room temperature, centrifugally filter to obtain ferric hydroxide colloid, and then transfer to -10°C environment Sealed and frozen for 2 hours, and made into fine powder by ultra-fine pulverizer, and finally made into nano-powder by nano-grinder;

[0029] (2) Take 50 mL of water, 3.6 g of 30% hydrochloric acid solution, add 3.6 g of 3,3-dichlorobenzidine under stirring, continue stirring for 3 minutes, add 0.4 g of aminotriacetic acid, heat up to 90 ° C, stop heating, and stir After cooling to 40°C, 6.4 g of 30% hydrochloric acid was added, and the temperature was lowered to 0°C. Then add 6.4g of 30% sodium nitrite solution to carry out the diazotization reaction. The reaction process is completed within 2 minutes. After the reaction is completed, d...

Embodiment 3

[0056]Utilize embodiment 1, embodiment 2 to make the orange-red powder coating that is raw material with modified composite pigment yellow, and set without adding catalyst PdCl 2 Comparative example 1, the comparative example 2 that uses non-ionic surfactant OP-10 instead, the comparative example 3 that makes orange-red powder coating with 8323 yellow as raw material, and embodiment 1-2, comparative example 1-3 are carried out The relevant paint performance testing results are shown in Table 1.

[0057] Table 1 Performance testing of powder coatings

[0058] Test items

[0059] In Table 1, taking Comparative Example 2 as the standard product, the test data in Examples 1-2 and Comparative Examples 1-3 are all detected on the basis of the standard product. It can be found from the data in the table that the performance of the powder coating prepared by the modified and compounded pigment has been greatly improved.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses orange red powder coating taking modified composite pigment yellow as a raw material and relates to the technical field of coating. Aiming at disadvantages of an existing organic pigment, a manner combining inorganic core coating and surfactant treatment is adopted and is used for carrying out compound modification on organic pigment. The orange red powder coating disclosedby the invention takes ferric hydroxide colloid with positive charges as an inorganic core, and organic pigment molecules are adsorbed at the periphery of the inorganic core very well by utilizing attraction of positive and negative charges and high-adsorption performance of the surface of the colloid, so that first-time modification is realized. Then the ferric hydroxide colloid is transformed into transparent iron yellow alpha-FeOOH through a catalyst PdCl2 and second-time modification of the organic pigment is realized under the action of disodium methylenedinaphthalenesulfonate and sodiumdodecyl sulfate.

Description

Technical field: [0001] The invention relates to the technical field of coatings, in particular to an orange powder coating made from modified composite pigment yellow. Background technique: [0002] Organic pigments have a wide spectrum, bright colors, bright hues and various varieties, and are widely used in coatings, inks and plastics. However, the light stability, heat stability, solvent resistance, migration resistance, hiding power and other properties of most organic pigments are often inferior to those of inorganic pigments. Therefore, when organic pigments are used in coatings, there are often phenomena such as easy fading, easy floating, and weak tinting strength. It is particularly necessary to modify organic pigments so that they can better meet the use requirements. [0003] The diameter of ferric hydroxide colloidal particles is generally between 1nm and 100nm, which determines that the colloidal particles have a huge surface area and strong adsorption force. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09B35/021C09B35/10C09D167/00C09D163/00C09D5/03C09D7/61C09D7/41
CPCC08K2003/2241C08K2003/2265C09B35/021C09B35/10C09D5/033C09D5/035C09D167/00C08L63/00C08K3/22C08K3/04C08K5/235
Inventor 费邦忠周正华查全达吴和平费邦能
Owner ANHUI HUAHUI SUYE TECH SHARE CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com