Cationic binder emulsion for pigment dyeing as well as preparation method and application thereof

A cationic adhesive and paint dyeing technology, applied in the field of textile printing and dyeing, to achieve the effect of excellent fastness index, good adhesion and shortening the process flow

Inactive Publication Date: 2018-11-16
XINGTAI POLYTECHNIC COLLEGE
View PDF3 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] At present, the paint dyeing binders reported in a large number of literature and patents are all anionic, and there are relatively few studies on the introduction of cationic groups.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] Preparation of a cationic binder emulsion for paint dyeing

[0032] Place the four-neck flask equipped with reflux condenser, stirrer and dropping funnel in a constant temperature water bath, add 1g of emulsifier into distilled water at 60°C, stir evenly, and then add the initiator aqueous solution dropwise according to the formula Add the mixed liquid of 8g cross-linking monomer, 10g soft monomer, 8g hard monomer and 5g cationic monomer dropwise within 10 minutes. After reacting for 3 hours, quickly raise the temperature to 90°C, and quickly add 3g comonomer Stir for 5 minutes, quickly cool down to 35°C, adjust pH to 6 with citric acid, cool down to 0°C, keep warm for 30 minutes, and filter out.

[0033] The soft monomer is a mixture of butyl acrylate, heptyl acrylate, amyl acrylate or hexyl acrylate and butadiene;

[0034] Described hard monomer is the mixture of methyl methacrylate and acrylonitrile and vinyl acetate;

[0035] The crosslinking monomer is a mixture ...

Embodiment 2

[0042] Preparation of a cationic binder emulsion for paint dyeing

[0043] Place the four-neck flask equipped with a reflux condenser, agitator and dropping funnel in a constant temperature water bath, add 1.5g of emulsifier into distilled water at 65°C, stir evenly, and then add 0.05g of emulsifier dropwise according to the formula The mixed liquid of initiator aqueous solution, 10g cross-linking monomer, 12g soft monomer, 10g hard monomer and 7g cationic monomer is added dropwise within 30 minutes. After 3.5 hours of reaction, the temperature is rapidly raised to 95°C, and 5g is quickly added Stir the comonomer for 10 minutes, quickly cool down to 36°C, adjust the pH to 6.2 with citric acid, cool down to 1°C, keep the reaction for 30 minutes, and filter out.

[0044] The soft monomer is butyl acrylate, a mixture of butyl acrylate and butadiene;

[0045] The hard monomer is a mixture of methyl methacrylate and vinyl acetate;

[0046] The crosslinking monomer is a mixture of...

Embodiment 3

[0052] Preparation of a cationic binder emulsion for paint dyeing

[0053] Place the four-neck flask equipped with a reflux condenser, agitator and dropping funnel in a constant temperature water bath, add 2g of emulsifier into distilled water at 70°C, stir evenly, and then add 0.5g of emulsifier dropwise according to the formula to initiate The mixed liquid of aqueous solution of agent, 12g of cross-linking monomer, 15g of soft monomer, 15g of hard monomer and 9g of cationic monomer is added dropwise within 50 minutes. Stir the monomer for 15 minutes, quickly cool down to 37°C, adjust the pH to 6.5 with citric acid, cool down to 3°C, keep warm for 30 minutes, and filter out.

[0054] The soft monomer is a mixture of heptyl acrylate, hexyl acrylate and butadiene;

[0055] Described hard monomer is the mixture of methyl methacrylate and acrylonitrile and vinyl acetate;

[0056] The crosslinking monomer is a mixture of acrylic acid and maleic acid with hydroxypropyl methacryla...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
color fastnessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a cationic binder emulsion for pigment dyeing as well as a preparation method and application thereof. The binder emulsion is generated by carrying out reaction on the following components: a soft monomer, a hard monomer, a cross-linking monomer, a cationic monomer, a comonomer, a composite emulsifier of a cationic surfactant and a nonionic emulsifier and an initiator. Thepreparation method comprises the following steps of adding a mixture of the soft monomer, the hard monomer and the cross-linking monomer and an initiator aqueous solution into the emulsifier and distilled water for reaction, carrying out rapid heating, rapidly adding the comonomer, carrying out rapid cooling, adjusting the pH value, carrying out cooling, carrying out heat preservation reaction, and carrying out filtering so as to obtain the cationic binder emulsion. According to the cationic binder emulsion as well as the preparation method and application thereof, water-based latex not only is simple and convenient in preparation method, but also can be used for pigment dyeing for textiles.

Description

technical field [0001] The invention relates to the technical field of textile printing and dyeing, in particular to a cationic binder emulsion for paint dyeing, a preparation method and application thereof. Background technique [0002] The key to paint dyeing is to improve the feel of paint-dyed fabrics, rubbing fastness, adhesion to rolls during pad dyeing, and the depth of color and level dyeing of exhaust dyeing. The solution to these problems depends on the development of paint color paste, adhesives and other technologies. [0003] Adhesives are synthetic polymer compounds, which are polymerized from monomers and are generally made into water dispersions, emulsions and solvents. Adhesives for paint dyeing are required to have cross-linkable or self-cross-linkable groups, and after being dyed with pigments to form a colorless, transparent, strong adhesive, elastic and tough film. [0004] The quality of paint dyeing depends largely on the nature of the binder. Adhe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/18C08F236/06C08F220/14C08F220/46C08F218/08C08F220/06C08F222/02C08F220/20C08F226/02C08F236/08D06P1/52
CPCC08F218/08C08F220/06C08F220/14C08F220/18C08F220/1804C08F220/1806C08F220/1807C08F220/20C08F220/46C08F222/02C08F226/02C08F236/06C08F236/08D06P1/5257
Inventor 王明友
Owner XINGTAI POLYTECHNIC COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap