Recyclable artificial turf

A technology of artificial turf and turf, which is applied in the manufacture of rayon, single-component polyolefin rayon, textiles and papermaking, etc. It can solve the problems of physical property degradation, incompatibility of components, and difficulty in industrialization, etc. The effect of low temperature, favorable promotion and simple operation

Active Publication Date: 2018-11-16
无锡市桑丽人造草坪地毯有限公司
View PDF9 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The incomplete polyolefin and incomplete ethylene polymer material containing EVA used in this patent can be used as the adhesive layer of artificial turf. Although it can be recycled to a certain extent, there are also several problems. First, EVA contains vinyl acetate. , the elasticity and strength retention rate after recycling will be severely reduced, and what is more fatal is the incompatibility of components. After recycling and granulation, the physical properties are severely reduced and there is almost no use value.
Second, there must be additional equipment, which is to install a T-shaped film head on the extruder. This is non-standard equipment, and it is difficult to balance investment and return.
Third, it is difficult to industrialize how to smoothly extrude the 4-meter-wide T-shaped polyolefin film layer and cooperate with the lawn to fuse and coagulate into rolls

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] A recyclable artificial turf, the preparation method comprising the steps of:

[0034] (1) Preparation of grass fiber: the components are as follows in parts by weight: 70 parts of linear low-density polyethylene LLDPE, 30 parts of organic phthalocyanine green or organic yellow 151 pigments as colorants, and 0.5 parts of dispersant. The components are mixed and stirred evenly in a two-roller plastic mixer, then heated to 190°C, and granulated by an extrusion granulator, the green or yellow masterbatch with a particle diameter of 3mm; and then calculated by weight: linear 80 parts of low-density polyethylene LLDPE, 15 parts of homopolymer PP polypropylene resin, 3 parts of lubricant stearic acid, 1 part of anti-aging agent phosphite or thioester, 0.5 parts of the above green or yellow masterbatch; The above raw materials are mixed and placed in wire drawing equipment to obtain straight or curved wires, and a base cloth is set under the grass fibers;

[0035] (2) Raw mat...

Embodiment 2

[0043] A recyclable artificial turf, the preparation method comprising the steps of:

[0044] (1) Preparation of grass fiber: each component by weight parts is: 68 parts of linear low density polyethylene LLDPE, 25 parts of coloring material containing organic phthalocyanine green or organic yellow 151 pigment, 2 parts of dispersant, each The components are mixed and stirred evenly in a two-roller plastic mixer, then heated to 180°C, and granulated by an extrusion granulator, the green or yellow masterbatch with a particle diameter of 4mm; and then calculated by weight: linear 78 parts of low-density polyethylene LLDPE, 145 parts of homopolymer PP polypropylene resin, 2 parts of lubricant stearic acid, 2 parts of anti-aging agent phosphite or thioester, 2 parts of the above green or yellow masterbatch; The above raw materials are mixed and placed in wire drawing equipment to obtain straight or curved wires, and a base cloth is set under the grass fibers;

[0045] (2) Lawn adh...

Embodiment 3

[0053] A recyclable artificial turf, the preparation method comprising the steps of:

[0054] (1) Preparation of grass fiber: each component by weight parts is: 68 parts of linear low density polyethylene LLDPE, 25 parts of coloring material containing organic phthalocyanine green or organic yellow 151 pigment, 2 parts of dispersant, each The components are mixed and stirred evenly in a two-roller plastic mixer, then heated to 180°C, and granulated by an extrusion granulator, the green or yellow masterbatch with a particle diameter of 4mm; and then calculated by weight: linear 78 parts of low-density polyethylene LLDPE, 145 parts of homopolymer PP polypropylene resin, 2 parts of lubricant stearic acid, 2 parts of anti-aging agent phosphite or thioester, 2 parts of the above green or yellow masterbatch; The above raw materials are mixed and placed in wire drawing equipment to obtain straight or curved wires, and a base cloth is set under the grass fibers;

[0055] (2) Raw mate...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
viscosityaaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a recyclable artificial turf. The recyclable artificial turf comprises grass fibers, bottom cloth and an adhesive layer; the bottom cloth is arranged under the grass fibers; the adhesive layer is arranged under the bottom cloth; during preparation, firstly, components of glue water in weight parts are 95-100 parts of aqueous polyolefin dispersion, 0.5-1 parts of thickeningagents, 1-5 parts of deionized water and 2-3 parts of pigment fillers; secondly, the turf is correspondingly coated for two times, coated and dried; and thirdly, the turf is perforated and cut to obtain the recyclable artificial turf. According to the recyclable artificial turf, the preparation method is simple, the steps are easy to operate, the wire drawing performances, such as breaking strength, elongation, wire drawing section and appearance, of the prepared recyclable artificial turf satisfy requirements of manufacturing the artificial turf through wire redrawing, and better water resistance is realized.

Description

technical field [0001] The invention relates to a recyclable artificial turf, which belongs to the technical field of artificial turf preparation. Background technique [0002] After the existing traditional artificial turf tufting is manufactured, the last back coating process is carried out, usually using styrene-butadiene latex or polyurethane emulsion to coat and bake, so that the grass fibers are more firmly embedded in the base fabric and the pulling out of the grass fibers is increased. force. Grass silk is generally made of polyethylene PE or polypropylene PP plastic wire drawing, and the base fabric is woven from polypropylene PP plastic. When artificial turf needs to be recycled after several years of use, people will encounter great challenges and difficulties. First, polyethylene PE or polypropylene PP plastics and styrene-butadiene latex or polyurethane emulsion are two completely different chemical substances, and their structures and properties are quite dif...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): E01C13/08D01F6/46D01F1/10C09D123/00
CPCC09D123/00D01F1/10D01F6/46E01C13/08C08L1/284
Inventor 徐小军罗哲文
Owner 无锡市桑丽人造草坪地毯有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com