Aloe fiber spunlace non-woven mask substrate fabric and preparation method thereof

An aloe fiber, non-woven technology, applied in non-woven fabrics, textiles and papermaking, pharmaceutical formulations, etc., can solve the problems of high price and high cost, and achieve the effect of wide range of uses, moderate cost and fine texture

Inactive Publication Date: 2018-12-18
ZHONGYUAN ENGINEERING COLLEGE
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the price is expensive and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A kind of preparation method of aloe fiber spunlace nonwoven facial mask base cloth, the steps are as follows:

[0047] Utilizing the above technological process, equipment and technical measures, etc., the aloe fiber spunlace nonwoven mask base fabric has been developed, wherein, it is made of the raw materials with the following weight ratio: the weight content of aloe fiber accounts for 70%, viscose The weight content of fiber accounts for 10%, and the weight content of polyester fiber accounts for 20%. The performance index of the spunlace nonwoven mask base fabric is: the actual weight is 49.12g / m 2 , average thickness 0.36mm; longitudinal strength 61.0N, transverse strength 47.75N, longitudinal and transverse strength ratio 1.28:1; longitudinal elongation at break 22.88%, transverse elongation at break 37.75%, longitudinal and transverse elongation at break ratio 0.61:1 ; Longitudinal tear strength 8.0N, transverse tear strength 8.63N, longitudinal and transverse...

Embodiment 2

[0049] A kind of preparation method of aloe fiber spunlace nonwoven facial mask base cloth, the steps are as follows:

[0050] Using the above technological process, equipment and technical measures, etc., the aloe fiber spunlace non-woven mask base fabric has been developed, wherein it is made of the following raw materials in the weight ratio: the weight content of aloe fiber accounts for 80%, viscose The weight content of fiber accounts for 10%, and the weight content of polyester fiber accounts for 10%. The performance index of the spunlace nonwoven mask base fabric is: the actual weight is 65.67g / m 2 , average thickness 0.47mm; longitudinal strength 91.4N, transverse strength 87.67N, ratio of longitudinal and transverse strength 1.04:1; longitudinal elongation at break 21.73%, transverse elongation at break 35.6%, ratio of longitudinal and transverse elongation at break 0.61:1 ; Longitudinal tear strength 11.74N, transverse tear strength 13.0N, longitudinal and transvers...

Embodiment 3

[0052] A kind of preparation method of aloe fiber spunlace nonwoven facial mask base cloth, the steps are as follows:

[0053] Using the above technological process, equipment and technical measures, etc., aloe fiber spunlace nonwoven mask base fabric has been developed, wherein, it is made of the following raw materials in weight ratio: the weight content of aloe fiber accounts for 100%, viscose The weight content of fiber is 0%, and the weight content of polyester fiber is 0%. The performance index of the spunlace nonwoven mask base fabric is: the actual weight is 48.6g / m 2 , average thickness 0.35mm; longitudinal strength 65.08N, transverse strength 51.08N, longitudinal and transverse strength ratio 1.27:1; longitudinal elongation at break 20.25%, transverse elongation at break 35.75%, longitudinal and transverse elongation at break ratio 0.57:1 ; Longitudinal tear strength 6.75N, transverse tear strength 7.08N, longitudinal and transverse tear strength ratio 0.95:1. The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The average thicknessaaaaaaaaaa
Longitudinal strengthaaaaaaaaaa
Lateral forceaaaaaaaaaa
Login to View More

Abstract

The invention provides an aloe fiber spunlace non-woven mask substrate fabric and a preparation method thereof. The mask substrate fabric comprises, by weight, 10-100% of aloe fiber, 0-50% of Amicor antibacterial fiber, 0-90% of viscose fiber and 0-90% of polyester fiber. Compared with the prior art, the fiber processed spunlace non-woven mask substrate fabric has the advantages that a product canbe self-decomposed after the product is used for one time, no pollution is caused on the environment, the chemical resistance is good, the mask substrate fabric is clean and hygienic and does not contain chemical preparations and impurities, the quality is fine, delinting is not caused, the mask substrate fabric has the advantages of skin beautifying, health protection, skin cleaning, skin caring, skin moisturizing, moistening and the like, the use of the mask substrate fabric is extensive, and the mask substrate fabric is suitable for developing masks with functions of skin moisturizing, skin protecting, skin cleaning, moistening, whitening,refreshing, smoothing, fineness and smoothness, whitening and health-protection and splash relieving.

Description

technical field [0001] The invention relates to the field of health-care spunlace fabrics for medical textiles, in particular to an aloe fiber spunlace nonwoven mask base fabric and a preparation method thereof. Background technique [0002] The process principle of the spunlace technology is that the pre-wetted fiber web enters the spunlace area, and the water spray holes of the water spray plate of the spunlace head spray out multiple fine water jets, which shoot vertically at the fiber web. The water jet displaces a part of the surface fibers in the fiber web, including the vertical movement to the opposite side of the fiber web. When the water jet penetrates the fiber web, it is rebounded by the screen curtain or the drum, and scatters to the fiber web in different directions. negative side. Under the double action of the direct impact of the water jet and the rebound of the water flow, the fibers in the fiber web are displaced, interspersed, entangled, and entangled, f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D04H1/4382D04H1/4266D04H1/435D04H1/4258D04H1/492A61Q19/08A61Q19/02A61Q19/00A61K8/9794A61K8/97A61K8/02
CPCA61K8/0212A61K8/97A61K8/9794A61Q19/00A61Q19/005A61Q19/02A61Q19/08D04H1/4258D04H1/4266D04H1/435D04H1/4382D04H1/492
Inventor 赵博
Owner ZHONGYUAN ENGINEERING COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com