Pattern type powder coating and preparation method thereof

A powder coating and pattern technology, applied in powder coatings, polyester coatings, epoxy resin coatings, etc., can solve the problem of high cost and achieve the effect of reducing the production cost of raw materials, good effect and low process cost

Active Publication Date: 2018-12-28
WUHU INST OF TECH
View PDF3 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Relatively speaking, the cost is higher

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Pattern type powder coating and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0012] In order to achieve the above object, the present invention provides a kind of preparation method of pattern type powder coating, described preparation method comprises the following steps: (1) polyester resin, epoxy resin, curing agent, pigment filler, defoamer and pigment Mix evenly; (2) Extrude the uniformly mixed material in an extruder, cool, tablet and pulverize; (3) Add a leveling agent to the pulverized material, mix it uniformly and then grind it.

[0013] Through the above-mentioned technical scheme, the present invention does not add patterning agent (texture agent), reduces purchase management and raw material production cost; Only need to change the addition amount of leveling agent and its addition order in preparation process, do not change the preparation of powder coating The main process can get the patterned powder coating; when the workshop uses this production line to produce flat products of the same color, it can omit the complicated steps of washi...

Embodiment 1

[0031] (1) Put 150Kg polyester resin, 150Kg epoxy resin, 80Kg precipitated barium sulfate, 26Kg light calcium carbonate, 20Kg titanium dioxide, 3Kg iron black powder, 1.50Kg benzoin, 0.90Kg imidazole into the mixing tank, stir for 20 minutes and mix Uniform;

[0032] (2) The mixed material is extruded through the extruder, the temperature of the machine cavity is 105°C, the temperature of the extruder head is 110°C, the average residence time of the material is not more than 30 seconds, cooling, tablet crushing, cooling tablet crushing;

[0033] (3) Add 1.50Kg leveling agent to the pulverized material, and then mix; the material after mixing again enters the pulverizer and grinds to 80 microns.

Embodiment 2

[0035] A kind of preparation method of decorative pattern type powder coating, described preparation method comprises the following steps:

[0036] (1) Mix 90kg of polyester resin with the corresponding amount of epoxy resin, imidazole, pigment filler, benzoin and pigment; the mass ratio of polyester resin to epoxy resin is 90:10;

[0037] The total mass of polyester resin and epoxy resin, the mass ratio of pigments and fillers to benzoin is 100:38:0.4; the mass ratio of epoxy resin to imidazole is 100:5; the epoxy equivalent of epoxy resin is 700; acid value It is 60mg KOH / g, and the number average molecular weight is 2600;

[0038] (2) Extrude the uniformly mixed material in an extruder, wherein the temperature of the cavity is 100°C, the temperature of the extruder head is 120°C, the average residence time of the material is not more than 30 seconds, cooled, tableted and pulverized;

[0039] (3) Add leveling agent in the pulverized material, the mass ratio of the total mas...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
acid valueaaaaaaaaaa
acid valueaaaaaaaaaa
Login to View More

Abstract

The invention discloses a pattern type powder coating and a preparation method thereof. The preparation method comprises the following steps: step (1) of evenly mixing a polyester resin, an epoxy resin, a curing agent, a pigment filler, an antifoaming agent and a pigment; step (2) of extruding the evenly mixed materials from an extruder, and performing cooling, pressed into pieces and smashing; step (3) of adding a leveling agent in the smashed materials, evenly mixing the materials and grinding the materials. The pattern type powder coating can be prepared without adding a pattern agent and can be completed under existing production conditions, and there is no need to add any device; existing overall production processes are not changed; and the powder spray curing conditions of the pattern type powder coating do not need to be changed. The novel process for preparing the pattern type powder coating is low in cost and good in effect.

Description

technical field [0001] The invention relates to a powder coating, in particular to a patterned powder coating and a preparation method thereof. Background technique [0002] The preparation process of a typical patterned powder coating is as follows: mixing resin, pigment, leveling agent, patterning agent, etc., melting, extruding, tableting, crushing, milling, sieving and other processes to obtain the finished product. In this process, the leveling agent and the pattern agent are added at the same time, and the effect of the added pattern agent is used during film formation to cause the coating film to change the flow state of the coating film around the particle of the pattern agent, forming an uneven pattern. That is to use the leveling agent to help the coating film leveling, and at the same time use the patterning agent to make the leveling of the coating film uneven and produce patterns. The pattern agent is used in the raw material formula, and when this production l...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D167/00C09D163/00C09D7/61C09D7/63C09D5/03
CPCC08K2003/2241C08K2003/265C08K2003/3045C09D5/033C09D163/00C09D167/00C08L63/00C08K13/02C08K3/30C08K3/26C08K3/22C08K5/3445C08L67/00
Inventor 吴为亚樊陈莉冯光峰余家俊贾静思
Owner WUHU INST OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com