Sunscreen heat-resistance hollow side windshield for vehicle

A glass and hollow technology, which is applied in the field of hollow sunscreen and heat-resisting vehicle side glass, can solve the problems of poor heat-resisting effect, unbearable human body, affecting driving, etc. long effect

Inactive Publication Date: 2019-01-04
景有超
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the car glass on the market has poor heat resistance effect, especially in summer, when the ultraviolet rays are strong, driving outside for a long time will damage the skin, which is unbearable for the human body and harmful to health.
In addition, when the weather conditions are not good, the front glass of the car is prone to fogging, which affects driving and even safety.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0013] A hollow sunscreen and heat-resisting car sideshield glass, the glass is a hollow double-layer structure, and the glass is prepared from the following components in parts by weight: 3-13 parts of quartz sand, 2-10 parts of sodium hydroxide, limestone 1-7 parts, 2-8 parts of glass fiber, 15-25 parts of silicon dioxide, 2-8 parts of zinc oxide, 3-13 parts of sodium carbonate, 2-12 parts of anti-ultraviolet agent, 2-5 parts of magnesium oxide, 1-5 parts of solid agent.

[0014] Further, the reinforcing agent is polyethylene glycol diacrylate methyl ester, polyethylene glycol diacrylate ethyl ester or polyethylene glycol diacrylate propyl ester.

[0015] Further, the silica is 1000-1200 mesh silica.

[0016] Further, the anti-ultraviolet agent is prepared from phenyl salicylate, nano titanium dioxide and antioxidant.

[0017] Further, the sodium hydroxide purity is 99.5%.

Embodiment 2

[0019] A hollow sunscreen and heat-resisting vehicle sideshield glass, the glass is a hollow double-layer structure, and the glass is prepared from the following components in parts by weight: 3 parts of quartz sand, 2 parts of sodium hydroxide, 1 part of limestone, glass 2 parts of fiber, 15 parts of silicon dioxide, 2 parts of zinc oxide, 3 parts of sodium carbonate, 2 parts of anti-ultraviolet agent, 2 parts of magnesium oxide, 1 part of reinforcing agent.

[0020] Further, the reinforcing agent is polyethylene glycol diacrylate methyl ester, polyethylene glycol diacrylate ethyl ester or polyethylene glycol diacrylate propyl ester.

[0021] Further, the silica is 1000 mesh silica.

[0022] Further, the anti-ultraviolet agent is prepared from phenyl salicylate, nano titanium dioxide and antioxidant.

[0023] Further, the sodium hydroxide purity is 99.5%.

Embodiment 3

[0025] A hollow sunscreen and heat-resisting vehicle sideshield glass, the glass is a hollow double-layer structure, and the glass is prepared from the following components in parts by weight: 13 parts of quartz sand, 10 parts of sodium hydroxide, 7 parts of limestone, glass 8 parts of fiber, 25 parts of silicon dioxide, 8 parts of zinc oxide, 13 parts of sodium carbonate, 12 parts of anti-ultraviolet agent, 5 parts of magnesium oxide, and 5 parts of reinforcing agent.

[0026] Further, the reinforcing agent is polyethylene glycol diacrylate methyl ester, polyethylene glycol diacrylate ethyl ester or polyethylene glycol diacrylate propyl ester.

[0027] Further, the silica is 1200 mesh silica.

[0028] Further, the anti-ultraviolet agent is prepared from phenyl salicylate, nano titanium dioxide and antioxidant.

[0029] Further, the sodium hydroxide purity is 99.5%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
purityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a sunscreen heat-resistance hollow side windshield for a vehicle, and belongs to the technical field of glass materials. The windshield is of a hollow dual-layer structure andis prepared from, by weight, 3-13 parts of quartz sand, 2-10 parts of sodium hydroxide, 1-7 parts of limestone, 2-8 parts of glass fibers, 15-25 parts of silicon dioxide, 2-8 parts of zinc oxide, 3-13parts of sodium carbonate, 2-12 parts of anti-ultraviolet agent, 2-5 parts of magnesium oxide and 1-5 parts of reinforcing agent. The prepared windshield for the vehicle has the advantages of being high in structural strength, long in service life and the like; in the using process, the situation that the windshield is broken cannot occur, the structural strength of the material of the windshieldis improved, and the service life is prolonged; the windshield has high strength, and can resist strong impact, effectively stop sun illumination to protect the skin against hurt, and effectively prevent fog to improve safety for driving.

Description

technical field [0001] The invention relates to a glass material, in particular to a hollow sunscreen and heat-resisting vehicle sideshield, which belongs to the technical field of glass materials. Background technique [0002] Automobile glass is indispensable in the accessories of automobile body, and mainly plays a protective role. There are three main types of automotive glass: laminated glass, tempered glass and area tempered glass, which can withstand strong impact. Automobile glass is divided into four types according to its location: front windshield, side window glass, rear windshield glass and sunroof glass. The national mandatory regulations for the front windshield must be laminated glass, the side window glass is tempered glass, and the rear windshield is generally tempered glass with electric heating wire. The current automotive glass on the market has poor heat resistance, especially in summer, when the ultraviolet rays are strong, and driving outside for a ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C14/00C03C4/08C03C6/04
CPCC03C1/00C03C4/085C03C14/00
Inventor 景有超
Owner 景有超
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com