Bamboo charcoal latex mattress

A bamboo charcoal and latex technology, applied in the field of latex mattresses, can solve the problems of heavy odor and general softness and comfort of mattresses, and achieve the effects of improving service life, improving softness and comfort, and keeping the air fresh.

Inactive Publication Date: 2019-01-04
安徽玉然经编科技有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the current mattresses are generally soft and comfortable, and the peculiar smell is relatively heavy.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0015] A bamboo charcoal latex mattress, made of the following components by weight: 95 parts of natural latex, 5 parts of bamboo charcoal, 1.2 parts of sulfur, 6 parts of 2,4-dichlorobenzoyl peroxide modified hydrogel, hydroxy 2.5 parts of fluorosilicone oil, 3.2 parts of white carbon black, 1.12 parts of vinyl-containing polysiloxane, 0.5 parts of flame retardant, and 2.8 parts of nano zinc oxide.

[0016] Further, the preparation method of the 2,4-dichlorobenzoyl peroxide modified hydrogel is:

[0017] Put polyvinyl alcohol and hyaluronic acid into distilled aqueous solution, stir at 85°C to form a uniform solution, then adjust the temperature to 50°C, then add sodium silicate with 10% polyvinyl alcohol mass and continue stirring for 30 minutes, then add polyvinyl alcohol mass 0.35% 2,4-dichlorobenzoyl peroxide, heated to 68°C under the protection of an inert gas, reacted for 2 hours, then discharged, dried until the moisture content reached 15%, and the product was obtaine...

Embodiment 2

[0024] A bamboo charcoal latex mattress, made of the following components by weight: 95 parts of natural latex, 8 parts of bamboo charcoal, 1.2 parts of sulfur, 7 parts of 2,4-dichlorobenzoyl peroxide modified hydrogel, hydroxyl 2.5 parts of fluorosilicone oil, 3.2 parts of white carbon black, 1.12 parts of vinyl-containing polysiloxane, 0.5 parts of flame retardant, and 2.8 parts of nano zinc oxide.

[0025] Further, the preparation method of the 2,4-dichlorobenzoyl peroxide modified hydrogel is:

[0026] Put polyvinyl alcohol and hyaluronic acid into distilled aqueous solution, stir at 85°C to form a uniform solution, then adjust the temperature to 50°C, then add sodium silicate with 10% polyvinyl alcohol mass and continue stirring for 30 minutes, then add polyvinyl alcohol mass 0.35% 2,4-dichlorobenzoyl peroxide, heated to 68°C under the protection of an inert gas, reacted for 2 hours, then discharged, dried until the moisture content reached 15%, and the product was obtain...

Embodiment 3

[0033] A bamboo charcoal latex mattress, made of the following components by weight: 95 parts of natural latex, 6 parts of bamboo charcoal, 1.2 parts of sulfur, 6.7 parts of 2,4-dichlorobenzoyl peroxide modified hydrogel, hydroxy 2.5 parts of fluorosilicone oil, 3.2 parts of white carbon black, 1.12 parts of vinyl-containing polysiloxane, 0.5 parts of flame retardant, and 2.8 parts of nano zinc oxide.

[0034] Further, the preparation method of the 2,4-dichlorobenzoyl peroxide modified hydrogel is:

[0035] Put polyvinyl alcohol and hyaluronic acid into distilled aqueous solution, stir at 85°C to form a uniform solution, then adjust the temperature to 50°C, then add sodium silicate with 10% polyvinyl alcohol mass and continue stirring for 30 minutes, then add polyvinyl alcohol mass 0.35% 2,4-dichlorobenzoyl peroxide, heated to 68°C under the protection of an inert gas, reacted for 2 hours, then discharged, dried until the moisture content reached 15%, and the product was obtai...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a bamboo charcoal latex mattress, and relates to the technical field of latex mattresses. The bamboo charcoal latex mattress is prepared from natural latex, bamboo charcoal, sulfur, 2,4-dichlorobenzoyl peroxide modified hydrogel, hydroxyl fluorosilicone oil, white carbon black, polysiloxane containing vinyl, fire retardant and nano zinc oxide. The bamboo charcoal latex mattress has the advantages of achieving high elasticity and excellent flexing resistance, shock resistance and creep-resistant performance of a coating and being natural and free of harm, capable of being naturally degraded, environmentally friendly and the like.

Description

technical field [0001] The invention belongs to the technical field of latex mattresses, in particular to a bamboo charcoal latex mattress. Background technique [0002] Natural latex is a thermoplastic synthetic resin of the rubber type. It is widely used in modern households due to its high elasticity, excellent film resistance, shock resistance and creep resistance, as well as natural harmlessness, natural decomposition and environmental protection. application is becoming more and more widespread. But the soft comfort of present mattress is general, and peculiar smell is heavier. Contents of the invention [0003] The purpose of the invention is to provide a kind of bamboo charcoal latex mattress to existing problem. [0004] The present invention is achieved through the following technical solutions: [0005] A bamboo charcoal latex mattress, made of the following components by weight: 95 parts of natural latex, 5-8 parts of bamboo charcoal, 1.2 parts of sulfur, 2,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L7/02C08L83/08C08L83/07C08L29/04C08L5/08C08K13/02C08K3/04C08K5/14C08K3/36C08K3/22
CPCC08L7/02C08K2003/2224C08K2003/2296C08K2201/011C08L2201/06C08L2205/035C08L83/08C08L83/04C08L29/04C08L5/08C08K13/02C08K3/04C08K5/14C08K3/36C08K3/22
Inventor 张明
Owner 安徽玉然经编科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com