High-performance diamond saw blade and preparation method thereof

A diamond saw blade, high-performance technology, used in metal sawing equipment, metal processing equipment, tool manufacturing of sawing machine devices, etc., can solve the problem of diamond saw blade delay, achieve good compatibility, broad application prospects, comprehensive Excellent performance

Active Publication Date: 2019-01-11
泉州市华兴超硬工具有限公司
View PDF9 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the late development and development of diamond saw blades in my country, there is a large gap with developed countries in terms of the quality, type and manufacturing technology of diamond saw blades, so it is of great significance to produce high-performance diamond saw blades.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-performance diamond saw blade and preparation method thereof
  • High-performance diamond saw blade and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] refer to figure 1 , a high-performance diamond saw blade, including a substrate 1 and a cutter head 2, the cutter head 2 includes a first cutting area 21 and a second cutting area 22; the first cutting area includes the following raw materials by weight: polycrystalline 8 parts of diamond particles, 48 ​​parts of iron powder, 25 parts of copper powder, 4 parts of zinc powder, 2 parts of tin powder, 1.5 parts of nickel powder, 2 parts of cobalt powder, 1.5 parts of manganese powder, 2.5 parts of tungsten carbide and titanium carbide mixture powder, 0.4 part of lanthanum nickel five powder; the second cutting area includes the following raw materials in parts by weight: 10 parts of polycrystalline diamond and boron carbide mixture particles, 45 parts of iron powder, 27 parts of copper powder, 4 parts of zinc powder, and 2 parts of tin powder , 1.5 parts of nickel powder, 2 parts of cobalt powder, 1.5 parts of manganese powder, 2.5 parts of titanium carbide powder, and 0.4...

Embodiment 2

[0042] refer to figure 1 , a high-performance diamond saw blade, comprising a substrate 1 and a cutter head 2, the cutter head 2 includes a first cutting area and a second cutting area; the first cutting area includes the following raw materials by weight: polycrystalline diamond particles 14 parts, 55 parts of iron powder, 32 parts of copper powder, 6 parts of zinc powder, 3 parts of tin powder, 2.5 parts of nickel powder, 3 parts of cobalt powder, 2 parts of manganese powder, 5 parts of tungsten carbide and titanium carbide mixture powder, lanthanum nickel 0.7 parts of five powders; the second cutting area includes the following raw materials by weight: 16 parts of polycrystalline diamond and boron carbide mixture particles, 50 parts of iron powder, 33 parts of copper powder, 6 parts of zinc powder, 3 parts of tin powder, nickel 2.5 parts of cobalt powder, 3 parts of cobalt powder, 2 parts of manganese powder, 4 parts of titanium carbide powder, and 0.7 part of lanthanum nic...

Embodiment 3

[0056] refer to figure 1 , a high-performance diamond saw blade, including a substrate and a cutter head, the cutter head includes a first cutting zone and a second cutting zone; the first cutting zone includes the following raw materials by weight: 10.5 parts of polycrystalline diamond particles, 51 parts of iron powder, 30 parts of copper powder, 5.5 parts of zinc powder, 2.5 parts of tin powder, 2.1 parts of nickel powder, 2.6 parts of cobalt powder, 1.7 parts of manganese powder, 3.8 parts of tungsten carbide and titanium carbide mixture powder, lanthanum nickel five powder 0.65 part; the second cutting area includes the following raw materials by weight: 15 parts of polycrystalline diamond and boron carbide mixture particles, 48 ​​parts of iron powder, 31.5 parts of copper powder, 4.5 parts of zinc powder, 2.5 parts of tin powder, 1.9 parts of nickel powder , 2.7 parts of cobalt powder, 1.6 parts of manganese powder, 3.5 parts of titanium carbide powder, and 0.6 part of l...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high-performance diamond saw blade and a preparation method thereof. A tool bit of the high-performance diamond saw blade comprises a first cutting area and a second cuttingarea. The first cutting area comprises, by weight part, 8-14 parts of polycrystalline diamond particles, 48-55 parts of iron powder, 25-32 parts of copper powder, 4-6 parts of zinc powder, 2-3 parts of tin powder, 1.5-2.5 parts of nickel powder, 2-3 parts of cobalt powder, 1.5-2 parts of manganese powder, 2.5-5 parts of tungsten carbide and titanium carbide mixture powder and 0.4-0.7 part of lanthanum pentanickel powder. The second cutting area comprises, by weight part, 10-16 parts of polycrystalline diamond and boron carbide mixture particles, 45-50 parts of iron powder, 27-33 parts of copper powder, 4-6 parts of zinc powder, 2-3 parts of tin powder, 1.5-2.5 parts of nickel powder, 2-3 parts of cobalt powder, 1.5-2 parts of manganese powder, 2.5-4 parts of titanium carbide powder and 0.4-0.7 part of lanthanum pentanickel powder. The high-performance diamond saw blade is excellent in comprehensive performance.

Description

technical field [0001] The invention relates to a diamond saw blade, in particular to a high-performance diamond saw blade and a preparation method thereof. Background technique [0002] Diamond saw blades are currently the most consumed diamond tools in the world. They are widely used in the processing of stone, glass, ceramics, and cast iron materials, as well as in the construction of houses, roads, and bridges. With the continuous improvement of the production technology of diamond saw blades and the continuous reduction of production costs, its application fields are still expanding, and the demand is also constantly expanding. With my country's accession to WTO and the development of global economic integration, my country's diamond saw blade industry has also ushered in great opportunities and challenges, and at the same time, China is now the largest market in the world. However, due to the late development and development of diamond saw blades in my country, there ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F9/04B22F3/02B22F3/10B22F5/00C22C26/00C22C30/06C22C38/16C22C38/14C22C38/12C22C38/10C22C38/08C22C38/04B23D61/02B23D65/00
CPCB22F3/02B22F3/1007B22F5/00B22F9/04B22F2005/001B22F2009/041B22F2998/10B23D61/028B23D65/00C22C26/00C22C30/06C22C38/002C22C38/005C22C38/008C22C38/04C22C38/105C22C38/12C22C38/14C22C38/16C22C2026/006
Inventor 黄共华
Owner 泉州市华兴超硬工具有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com