A method for preparing zeolite granular material from washed coal gangue

A technology for granular materials and coal gangue, which is applied in the field of solid waste resource utilization and water treatment materials, can solve the problems of complex preparation process, shortage, secondary pollution, etc. Effect

Active Publication Date: 2021-09-17
中科华鹿(合肥)环保科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the resource utilization rate of coal gangue in my country is still less than 40%, which leads to the long-term accumulation of coal gangue in coal mines and cities, and has a serious impact on the urban landscape environment, atmospheric environment and ecological environment.
[0006] However, the above-mentioned existing methods for resource utilization of washed coal gangue to prepare environmentally friendly materials all have the problems of complex preparation process, high production cost, and secondary pollution, which restricts the industrial application of technical methods

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing zeolite granular material from washed coal gangue
  • A method for preparing zeolite granular material from washed coal gangue
  • A method for preparing zeolite granular material from washed coal gangue

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] (1) After the washed coal gangue is crushed by a roller crusher and passed through a 10mm sieve (the photo is shown in figure 1 As shown in (a), calcined in a muffle furnace at 650 ° C for 1 h to basically oxidize the organic matter and transform kaolinite into metakaolinite.

[0030] (2) The calcined ash is selectively crushed and sieved to obtain porous particles with a particle size of 3 to 5 mm (the photo is as follows: figure 1 As shown in (b), the SEM image is as figure 2 shown).

[0031] (3) Prepare a sodium hydroxide solution with a mass concentration of 15%, weigh the particles according to the mass volume ratio of the particles to the sodium hydroxide solution 1g:2mL, and put them into a reaction vessel.

[0032] (4) Put the reaction vessel into a water bath and raise the temperature to 90°C, keep it warm for 24 hours. During the reaction, use a pump to pump the solution from the bottom of the reactor to the top of the reactor, so that the solution in the r...

Embodiment 2

[0036] (1) After crushing 10kg of washed coal gangue with a roller crusher and passing through a 10mm sieve, it was calcined in a muffle furnace at 800°C for 1 hour to oxidize and decompose organic matter and transform kaolinite into metakaolinite.

[0037] (2) The calcined ash is processed in a drum type jar mill for 1 hour to be selectively crushed, and sieved to obtain particles with a particle size greater than 2 mm;

[0038] (4) preparation mass concentration is the sodium hydroxide solution of 10%, according to the ratio batching of particle and sodium hydroxide solution mass volume ratio 1g:3mL, puts into reaction container and seals;

[0039] (5) Put the reaction vessel into the oven, set the temperature at 95°C, and keep it warm for 12 hours. During the reaction, pump the solution from the bottom of the reactor and transport it to the top of the reactor, so that the solution in the reactor flows through the particles in a seepage manner. Material, to achieve liquid mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing zeolitic granular materials from washed coal gangue, which comprises crushing and screening the ash after the washed coal gangue is calcined at 650-900°C, and adding the obtained granular materials into sodium hydroxide solution , make the active silicon-aluminum components in the particles react with sodium hydroxide, and crystallize and grow 4A zeolite on the surface of the particles, which is the zeolite granular material. The zeolite particle material prepared by washing coal gangue in the present invention, the synthetic zeolite is mainly distributed on the surface of the particle, and the speed of adsorbing pollutants is fast, can be widely used in the infiltration material of polluted rainwater treatment in the sponge city construction and the infiltration of artificial wetlands. Filter material and artificial submerged filter filler have the advantages of wide source of raw materials, comprehensive utilization of waste, and low preparation cost.

Description

technical field [0001] The invention belongs to the technical field of solid waste resource utilization and water treatment materials, and specifically relates to a method for resource utilization of coal gangue to obtain water pollution control materials. Background technique [0002] Coal gangue is an industrial solid waste with a large amount and a wide range, accounting for more than 20% of the total industrial solid waste in the country. In the process of coal development, an average of about 150kg of coal gangue is produced per ton of coal. At present, the resource utilization rate of coal gangue in my country is still less than 40%, which leads to the long-term accumulation of coal gangue in coal mines and cities, which has a serious impact on the urban landscape environment, atmospheric environment and ecological environment. [0003] The current method to reduce coal gangue emissions is to backfill the stope, and the way to dispose of coal mines on the spot is to f...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01B39/18
CPCC01B39/18C01P2004/03
Inventor 魏星陈赫然陈天虎
Owner 中科华鹿(合肥)环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap