Metal chromium waterborne mirror-like silver pigment and manufacturing method thereof

A manufacturing method, mirror silver technology, applied in the field of ink and coating, can solve the problems of non-corrosion resistance and water resistance of mirror surface aluminum, and achieve the effect of smooth surface, overcoming non-corrosion resistance, and uniform thickness

Inactive Publication Date: 2019-01-18
深圳市崯彩特殊金属颜料有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The present invention aims to provide a metal chromium water-based mirror silver pigment with chromium as the material, while retaining the same mirror effect, it overcomes the problems that the existing mirror aluminum is not resistant to water and corrosion, thereby expanding the application field of the mirror silver pigment To water and UV systems, to meet the needs of environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] The metal chromium water-based mirror silver pigment has a dark gray paste-like fluid appearance, and is composed of metal chromium flake particles, dispersants and auxiliary agents; the metal chromium mirror silver pigment is composed of the following ingredients in weight percentage:

[0040] Metal chromium flake particles 15%, dispersant 84%, auxiliary agent 1%.

[0041] In this embodiment, the metal chromium flake particles have a thickness of 10-12 nm and a particle size (d50) of 5-6 μm; the metal chromium flakes are made of high-purity chromium targets with a purity greater than 99.9%.

[0042] In this embodiment, the dispersant is propylene glycol methyl ether acetate with a purity greater than 99.5%; the auxiliary agent is an anti-sedimentation agent.

[0043] The manufacture method of this metallic chromium water-based specular silver pigment:

[0044] (1) Coat a PET film with a thickness of 16 μm on a coating machine with a transparent resin layer with a thic...

Embodiment 2

[0057] The metal chromium water-based mirror silver pigment has a light gray paste-like fluid appearance, and is composed of metal chromium flake particles, a dispersant and an auxiliary agent; the metal chromium mirror silver pigment is composed of the following ingredients by weight percentage:

[0058] Metal chromium flake particles 25%, dispersant 74.5%, auxiliary agent 0.5%.

[0059] In this embodiment, the metal chromium flake particles have a thickness ranging from 22 to 25 nm and a particle size (d50) of 9 to 10 μm; the metal chromium flakes are made of high-purity chromium targets with a purity greater than 99.9%.

[0060] In this embodiment, the dispersant is propylene glycol methyl ether with a purity greater than 99.5%; the auxiliary agent is an anti-sedimentation agent.

[0061] The manufacture method of this metallic chromium water-based specular silver pigment:

[0062] (1) Coat a PET film with a thickness of 12 μm on a coating machine with a transparent resin ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Particle sizeaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to a metal chromium waterborne mirror-like silver pigment and a manufacturing method thereof. The pigment contains the following components in percentage by weight: 10%-30% of metal chromium slice particles, 70%-88% of a dispersing agent and 0-2% of an aid. The manufacturing method comprises the following steps: (1) coating a plastic film base material with a resin layer witha thickness of 1-1.2 microns; (2) depositing metal chromium on the surface of the resin layer by virtue of a continuous winding type magnetron sputtering method, so as to form a nano-chromium film; and (3) crushing a mixed solution containing a solvent, resin and a fine chromium slice, filtering, adding the aid, adjusting the sold content, so as to obtain the metal chromium waterborne mirror-likesilver pigment containing the metal chromium slice particles, the dispersing agent and the aid. According to the pigment, chromium is taken as metal chromium mirror-like silver of the material, the same mirror surface effect is preserved, and meanwhile, the problems that existing mirror surface aluminum cannot resist water and corrosion are solved, so that the application field of the mirror-likesilver pigment is extended from a waterborne system to a UV system, and the pigment is accordant with the environment-friendly demands.

Description

technical field [0001] The invention relates to the technical fields of ink and paint, in particular to a metallic chromium water-based mirror silver pigment and a manufacturing method thereof. Background technique [0002] Mirror silver is a high-grade metal pigment made of aluminum with nano-thick aluminum flake particles dispersed in organic solvents. After printing or spraying the mirror ink / paint prepared with it on the printing surface, the nano-aluminum flakes are arranged parallel to each other. , thus forming a light reflection effect like a silver mirror, hence the name "mirror silver". [0003] Because aluminum will undergo a hydrogen release reaction when it meets water, the existing mirror silver is only used in oily ink / coating systems and cannot be used in water-based systems; in addition, aluminum is not resistant to acids and alkalis, even in oily systems, mirror silver is not suitable for the preparation Resins and solvents used in inks / coatings are also v...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C23C14/35C23C14/20C23C14/56C09D11/101C09D11/037C09D5/10
CPCC09D5/10C09D11/037C09D11/101C23C14/205C23C14/352C23C14/562
Inventor 瞿晓岳雷庆昌瞿祥慧
Owner 深圳市崯彩特殊金属颜料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap