Preparation method for waterproof and heat-insulating self-leveling material

A technology of self-leveling and preparation steps, applied in the direction of cement coating, coating, etc., can solve the problems of poor heat insulation performance and waterproof performance, and achieve the effect of enhancing heat insulation performance and broad application prospects

Inactive Publication Date: 2019-01-29
佛山齐安建筑科技有限公司
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention is to provide a method for preparing a waterproof and heat-insulating self-leveling material in view of the defects of poor heat insulation and waterproof performance of the current self-leveling materials

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] In parts by weight, weigh 3 to 5 parts of metasequoia bark, 7 to 9 parts of reed bamboo poles, 6 to 8 parts of umbrella grass leaves and 3 to 5 parts of red maple bark and put them into a planetary ball mill. Mix and grind for 2-3 hours under the condition of ~100r / min to obtain the mixed product; put the mixed product in a steam explosion tank, and send water vapor at a temperature of 260-300°C to the steam explosion tank until the pressure in the steam explosion tank rises As high as 3-4MPa, seal the mouth of the tank, let it stand at constant temperature and pressure for 30-40 minutes, open the mouth of the tank after standing to obtain the steam explosion product; mix the above steam explosion product with the sulfuric acid solution with a mass fraction of 40-50% in a mass ratio of 1 : 10 drops into the beaker, mixes and stirs 30~40min with the rotating speed of 500~600r / min with agitator and makes mixed slurry, drops into the acetic acid solution that the mass fract...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method for a waterproof and heat-insulating self-leveling material, belonging to the technical field of building materials. According to the invention, Metasequoia glyptostroboides barks, nalgrass poles, Cyperus alternifolius leaves and red maple barks are mixed and ground; water molecules are pressed into tissue fibers at a high temperature and a high pressure; sodium ferrate oxidized lignin is added to generate carboxyl groups with hydroxyl groups on cellulose; meanwhile, ester groups have good heat-insulating performance and facilitate reinforcing hydrophobicity of a self-leveling material; modified and decomposed plant fibers are mixed with glucose for a reaction, and the glucose has rich hydroxyl groups which can react with the plant fibers withsurface grafted with a large number of carboxyl groups to form stable covalent bond adsorption; through a granular structure, the self-leveling material forms a plurality of micropores in a microstructure after construction curing, and gas is filled in pores to facilitate reinforcing the heat-insulating performance of the self-leveling material; thus, the self-leveling material has broad application prospects.

Description

technical field [0001] The invention relates to a preparation method of a waterproof and heat-insulating self-leveling material, which belongs to the technical field of building materials. Background technique [0002] Self-leveling is a solvent-free, self-leveling, high-build epoxy floor coating with dense particles. Self-leveling solves the six major problems in floor installation. It is a ground construction technology. It is a liquid substance mixed with multiple materials and water. After being poured into the ground, this substance can flow along the ground according to the unevenness of the ground to automatically level the ground. The self-leveling floor engineering surface coating is beautiful, high cleanliness, high wear resistance and load-bearing, the most important thing is the beautiful decorative effect, because the first reaction of people's vision is the color and effect of the surface. The quality disadvantages of self-leveling floor engineering surface c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D1/08C09D7/61
CPCC09D1/08C09D7/61
Inventor 战英权蒋东明王素香
Owner 佛山齐安建筑科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap