A woodworking adhesive with long open time based on maltose syrup modified polyvinyl acetate emulsion

A polyvinyl acetate, open time technology, applied in the direction of monocarboxylate copolymer adhesives, adhesive types, polymer adhesive additives, etc., can solve the problem of short open time of adhesives

Active Publication Date: 2021-01-12
TAIZHOU UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a woodworking adhesive with a long open time based on maltose starch modified polyvinyl acetate emulsion for the short open time of traditional polyvinyl acetate emulsion adhesives

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A woodworking adhesive with long open time based on maltose syrup modified polyvinyl acetate emulsion
  • A woodworking adhesive with long open time based on maltose syrup modified polyvinyl acetate emulsion

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] Embodiment one total amount=1000kg

[0021] (1) 1 kilogram of ammonium persulfate is dissolved in 50 kilograms of water, obtains the ammonium persulfate initiator solution of 51 kilograms of polyreactions;

[0022] (2) 250 kilograms of vinyl acetate and 20 kilograms of methacrylic acid are mixed and stirred evenly to make 270 kilograms of mixed monomers;

[0023] (3) Add 525 kilograms of water, 1 kilogram of defoamer F681, 1 kilogram of buffering agent sodium bicarbonate, 2 kilograms of emulsifier AEO-9 in the reaction kettle, add 30 kilograms of Chuanwei polyvinyl alcohol 1788,10 under the condition of dispersing and stirring Kg of maltose syrup, stir and disperse for 10 minutes, heat up to 90°C, keep warm for 60 minutes, then cool down to 60°C, add 100 kg of vinyl acetate and 15 kg of ammonium persulfate initiator solution prepared in step (1), stir and disperse for 10 minutes ;

[0024] (4) Heat up to 78°C, keep warm for 20 minutes until there is no reflux, and the...

Embodiment 2

[0025] Embodiment two total amount=1000kg

[0026] (1) 1 kilogram of ammonium persulfate is dissolved in 50 kilograms of water, obtains the ammonium persulfate initiator solution of 51 kilograms of polyreactions;

[0027] (2) 280 kilograms of vinyl acetate and 20 kilograms of methacrylic acid are mixed and stirred evenly to make 2300 kilograms of mixed monomers;

[0028] (3) Add 495 kilograms of water, 1 kilogram of defoamer F681, 1 kilogram of buffer sodium bicarbonate, 2 kilograms of emulsifier AEO-9 in the reaction kettle, add 25 kilograms of Chuanwei polyvinyl alcohol 1788 under the condition of dispersion and stirring, 15 Kg of maltose syrup, stir and disperse for 10 minutes, heat up to 90°C, keep warm for 60 minutes, then cool down to 60°C, add 100 kg of vinyl acetate and 15 kg of ammonium persulfate initiator solution prepared in step (1), stir and disperse for 10 minutes ;

[0029] (4) Heat up to 78°C, keep warm for 20 minutes until there is no reflux, and then add 2...

Embodiment 3

[0030] Embodiment three total amount=1000kg

[0031] (1) 1 kilogram of ammonium persulfate is dissolved in 50 kilograms of water, obtains the ammonium persulfate initiator solution of 51 kilograms of polyreactions;

[0032] (2) 280 kilograms of vinyl acetate and 20 kilograms of methacrylic acid are mixed and stirred evenly to make 2300 kilograms of mixed monomers;

[0033] (3) Add 495 kg of water, 1 kg of defoamer F681, 1 kg of buffer sodium bicarbonate, 2 kg of emulsifier AEO-9 in the reactor, add 20 kg of Chuanwei polyvinyl alcohol 1788, 20 Kg of maltose syrup, stir and disperse for 10 minutes, heat up to 90°C, keep warm for 60 minutes, then cool down to 60°C, add 100 kg of vinyl acetate and 15 kg of ammonium persulfate initiator solution prepared in step (1), stir and disperse for 10 minutes ;

[0034] (4) Heat up to 78°C, keep warm for 20 minutes until there is no reflux, and then add 270 kg of mixed monomers in the step (2) with the constant flow pump, and control the d...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the technical field of adhesives, and relates to a long-open-time woodworking adhesive based on maltose syrup modified polyvinyl acetate emulsion. When the adhesive is prepared, firstly, polyvinyl alcohol and maltose syrup serve as a protective colloid, vinyl acetate serves as a monomer, ammonium persulfate serves as an initiator, the polyvinyl acetate emulsion is preparedby a seed emulsion polymerization process, and secondly, edible seaweed powder is added into copolymer emulsion. According to the polyvinyl acetate woodworking adhesive, water serves as a dispersionmedium, use is convenient, environments cannot be polluted, and the woodworking adhesive has the advantage of long open time as compared with a traditional polyvinyl acetate woodworking adhesive withthe same solid content.

Description

technical field [0001] The invention relates to a special-performance woodworking adhesive preparation technology, in particular to the preparation of a polyvinyl acetate woodworking adhesive with long open time. Background technique [0002] my country is a big country in the production and consumption of wood products, which has led to the vigorous development of wood adhesives. Water-based polyvinyl acetate (PVAc) adhesive is currently one of the most widely used and used environmentally friendly adhesives. It is obtained by emulsion polymerization with water as the dispersion medium, and is a water-based environmentally friendly adhesive. It is widely used in wood, furniture, decoration, printing, textiles, etc. , leather, paper and other industries, is a very environmentally friendly adhesive. [0003] With the development of the national economy and the development of application fields, its usage will increase significantly. However, there are many disadvantages i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09J131/04C09J11/06C09J11/08C08F218/08C08F220/06
CPCC08F218/08C09J11/06C09J11/08C09J131/04C08F220/06C08L1/28C08K5/1545
Inventor 刘维均何志才
Owner TAIZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com