A kind of rubber composition for coating radial tire cap ply

A rubber composition and a technology for radial tires are applied in the field of rubber compositions for coating radial tire cap layers to achieve the effects of good rubber permeability, simplified production process, and reduced production strength and production cost.

Active Publication Date: 2021-06-04
PRINX CHENGSHAN (SHANDONG) TIRE COMPANY LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The composition has better adhesion to larger diameter steel cords, so it is suitable for belts with larger steel cords, but not suitable for caps where small diameter steel cords and moderate surface viscosity are required

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] 1) Take 225kg of natural rubber, 3.4kg of binder RE, 2.5kg of cobalt boroacylate (cobalt ion accounts for 0.56kg), 1.2kg of tackifying resin TKM-M, 95kg of N326 carbon black, 15.8kg of zinc oxide, and 1.1kg of stearin Acid, 4.5kg anti-aging agent 6PPD, 5.6kg anti-aging agent RD, 0.21kg pentachlorothiophenol and 3.4kg naphthenic oil and mix evenly, mix at 100°C for 3min at a speed of 30r / min, and control the debinding temperature at 150°C to obtain Mixed Rubber A;

[0039] 2) Add 38.5kg of N326 carbon black to rubber compound A and mix evenly, mix at 100°C for 1.5min at a speed of 45r / min, and control the discharge temperature at 150°C to obtain compound B;

[0040] 3) Add 1.2kg sulfenamide accelerator DCBS, 0.1kg anti-scorch agent CTP, 4.5kg insoluble sulfur, 1.8kg ordinary sulfur and 4.5kg binder RA to the rubber compound B and mix evenly. Knead at a speed of 30 r / min for 1.5 min, and control the discharge temperature at 95° C. to obtain a rubber composition.

Embodiment 2

[0042] 1) Take 206kg natural rubber, 23kg isoprene rubber, 3.4kg binder B-18-S, 2.5kg boroacylated cobalt (cobalt ion accounts for 0.56kg), 3.4kg tackifying resin TKM-M, 94kg N330 carbon black , 16.0kg zinc oxide, 1.2kg stearic acid, 4.6kg anti-aging agent 6PPD, 5.7kg anti-aging agent RD, 0.21kg pentachlorothiophenol and 3.4kg naphthenic oil and mix well, at 80 ℃, at 50r / min Mix at a rotational speed for 2 minutes, and control the discharge temperature at 145°C to obtain compound A;

[0043] 2) Add 39.3kg of N330 carbon black to rubber compound A and mix evenly, mix at 120°C for 2.5min at a speed of 30r / min, and control the discharge temperature at 140°C to obtain compound B;

[0044] 3) Add 1.2kg sulfenamide accelerator DCBS, 0.1kg anti-scorch agent CTP, 6.7kg insoluble sulfur and 4.5kg binder RA to the rubber compound B and mix evenly. Mix at a rotational speed for 2 minutes, and control the debinding temperature at 100° C. to obtain a rubber composition.

Embodiment 3

[0046] 1) Take 229kg of natural rubber, 3.4kg of adhesive SL-3019F, 2.5kg of cobalt boroacylate (cobalt ion accounts for 0.56kg), 2.29kg of tackifying resin TKM-M, 91.6kg of N375 carbon black, 16.0kg of zinc oxide, 1.2kg of stearic acid, 4.6kg of anti-aging agent 6PPD, 5.7kg of anti-aging agent RD, 0.21kg of pentachlorothiophenol and 3.4kg of naphthenic oil were mixed evenly, and mixed at 120°C for 2.5min at a speed of 40r / min. The debinding temperature is controlled at 160°C to obtain compound A;

[0047] 2) Add 38.5kg of N375 carbon black to rubber compound A and mix evenly, mix at 80°C for 2 minutes at a speed of 40r / min, and control the discharge temperature at 145°C to obtain rubber compound B;

[0048] 3) Add 1.2kg sulfenamide accelerator DCBS, 0.1kg anti-scorch agent CTP, 3.3kg insoluble sulfur, 2.7kg ordinary sulfur, 4.5kg binder RA to the rubber compound B and mix evenly, at 60°C, Knead at a speed of 25 r / min for 2 minutes, and control the debinding temperature at 10...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
peel strengthaaaaaaaaaa
particle diameteraaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention provides a rubber composition for coating the cap layer of a radial tire, relates to the field of tire rubber materials, including raw rubber and an adhesive system, and the adhesive system includes 0.1-6 parts by weight of resorcinol A binder, 1-15 parts by weight of a methyl donor binder, 0.1-6 parts by weight of white carbon black and a cobalt salt with a cobalt content of 0.01-2 parts by weight. The rubber composition provided by the invention has good glue penetration, fluidity and rubber rigidity, and the radial tire cap layer coated with the rubber composition has relatively moderate surface viscosity, which can ensure the viscosity during lamination, It can also play a very good anti-adhesion effect. In actual production and preparation, it can be directly wound and coiled without using fiber pads or polyethylene film pads for inter-layer isolation, avoiding the surface of the crown layer from being affected by external pollution. Surface stickiness , Reduce production costs, simplify production processes, and improve production efficiency.

Description

technical field [0001] The invention relates to the field of tire rubber materials, in particular to a rubber composition used for coating a crown layer of a radial tire. Background technique [0002] The cap layer inside the radial tire plays the role of restraining the belt layer, enhancing the mechanical properties and dimensional stability of the shoulder of the radial tire. The steel cord crown strip with an angle of 0° can be applied to truckbus radial tires (TBR). The rubber material used to coat the steel cord itself and the cord must have good adhesion and adhesion rate, so as to ensure the quality of the obtained cap belt used in radial tires. [0003] After the cord of the cap layer is coated with the rubber coating, it relies on its surface to bond the crown and the belt layer. When the surface is dry or the viscosity is poor, the cap layer is easily separated from other parts. Subsequent pressure roller rolling process or during the use of tires will cause dis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L7/00C08L9/00C08L91/00C08K3/36C08K5/55C08K3/22C08K5/09C08K3/06
CPCC08K2003/2296C08L7/00C08L9/00C08L91/00C08K3/36C08K5/55C08K3/22C08K5/09C08K3/06
Inventor 谭建良许建欣孙蕾郭星
Owner PRINX CHENGSHAN (SHANDONG) TIRE COMPANY LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com