A kind of preparation method of metal-nonmetal hollow janus particle

A non-metallic, hollow technology, applied in metal material coating process, liquid chemical plating, coating and other directions, can solve the problems of the preparation of Janus particles that are not suitable for large particle size, the preparation process is complicated, and the preparation method is simple and fast. , high activity, high metal activity effect

Active Publication Date: 2021-09-21
XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] For the defects and deficiencies of the prior art, the purpose of the present invention is to provide a method for preparing hollow Janus glass microspheres, which solves the problem that the existing preparation method has a complicated preparation process and is not suitable for the preparation of large-sized Janus particles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of metal-nonmetal hollow janus particle
  • A kind of preparation method of metal-nonmetal hollow janus particle
  • A kind of preparation method of metal-nonmetal hollow janus particle

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] The invention discloses a method for preparing metal-nonmetal hollow Janus particles. The method mainly includes the following steps:

[0034] Step 1: Pretreat the hollow glass microspheres, the pretreatment process is:

[0035] Flotation treatment: the hollow glass beads are subjected to ultrasonic and centrifugal static treatment to reduce the impact of debris on the quality of subsequent coating particles;

[0036] Hydroxylation treatment: add the flotation hollow glass microspheres into the NaOH solution, heat and stir at 40-120°C for 20-60 minutes, stand still to take the upper layer mixture, and filter until the filtered water is neutral; among them, the NaOH solution The concentration is 20-40g / L;

[0037] Amination treatment: Add the hydroxylated hollow glass microspheres to the mixture of silane coupling agent, ethanol and deionized water, stir at 30-100°C for 40-90min, after the reaction is completed, filter and wash with ethanol , and then cleaned with deio...

Embodiment 1

[0045] Weigh 10 g of hollow glass microspheres with a diameter distribution of φ40-120 μm (H60, Sinosteel Ma’anshan Mining Institute New Material Technology Co., Ltd.), add the hollow glass microspheres to deionized water and ultrasonicate for 5 minutes to form a milky suspension. Centrifuge and separate, take the upper layer of glass microbead mixture, and dry it at 110°C for later use. Add the dried hollow glass microspheres into 250ml, 30g / L NaOH solution, heat and stir, and treat at 80°C for 40min. Stand still to take the upper layer mixture, and filter it with deionized water until the filtered water is neutral, and dry the glass beads for later use. Then the hydroxylated hollow glass microspheres are added to the mixed solution of silane coupling agent, ethanol and deionized water, wherein the amount of silane coupling agent Kh550 is 1% of the mass of hollow glass microspheres, ethanol and deionized water The volume ratio of water is 1:1, and it is stirred at 60°C for 6...

Embodiment 2

[0057] The difference between this example and Example 1 is that the silane coupling agent is Kh560, and the morphology and properties of the prepared Janus particles are the same as those in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
concentrationaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing metal-nonmetal hollow Janus particles. The method comprises: pretreating hollow glass microspheres; injecting the pretreated hollow glass microspheres into molten liquid paraffin and high-temperature deionized water Formed interface; stand and cool until the paraffin solidifies to obtain a paraffin template embedded with hollow glass microbeads; put the paraffin template into the pre-configured plating solution, and let it stand for reaction; separate the paraffin template from the plated hollow Glass microspheres, washable to obtain metal-nonmetal hollow Janus particles with different chemical compositions and properties of two hemispheres. The preparation method of the present invention is simple and fast, and can continuously prepare metal-nonmetal hollow Janus particles with a large particle size and micron order in batches. The microspheres have a wide application range, good particle dispersibility, and are easy to directly conduct applicable research.

Description

technical field [0001] The invention belongs to the technical field of materials, in particular to the field of hollow glass microspheres, and in particular to a method for preparing hollow Janus particles. Background technique [0002] High-performance hollow glass microsphere is a hollow spherical powdery ultra-light inorganic non-metallic material, which has the characteristics of light weight, low thermal conductivity, high compressive strength and good fluidity. Its true density is 0.2-0.60g / cm 3 , with a particle size between 2 and 120 μm, is a new type of lightweight material with wide application and excellent performance developed in recent years. The technology of coating metal on its surface to meet different functional requirements is also gradually developing. The surface of hollow glass microspheres is coated with metal, which not only has the functional properties of metals such as electrical conductivity and magnetism, but also has the characteristics of li...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C17/10C23C18/18C23C18/31
CPCC03C17/001C03C17/10C03C2217/254C03C2218/115C23C18/1893C23C18/31
Inventor 王磊王雷磊邓立强王旭东
Owner XI'AN UNIVERSITY OF ARCHITECTURE AND TECHNOLOGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com