Polyethersulfone ultrafiltration membrane and application of polyethersulfone ultrafiltration membrane in field of hematodialysis

A technology of polyethersulfone ultrafiltration membrane and polyethersulfone membrane, applied in ultrafiltration, dialysis systems, membrane technology, etc., can solve problems such as poor compatibility, reduced membrane separation performance, and easy generation of membrane defects, so as to prevent agglomeration , Good hydrophilic effect

Active Publication Date: 2019-03-08
青岛市中医医院
View PDF5 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although it is often mentioned in patents that nano-inorganic particles can be molecular sieves, especially NaA molecular sieves, molecular sieves are rarely used in practical applications.
The main reason is that the particle size of molecul...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0042] (1) Mix in-situ synthesized NaA molecular sieves (average particle size of 1.5 μm) and ethanol at a mass ratio of 1:50, and send them into a zirconia ball mill tank for ball milling. Set the ball milling speed to 450rpm, and the ball milling time for 6h. After the ball milling, the sample was dried and tested to have a particle size of 120nm;

[0043] (2) Evaporate the ball-milled NaA molecular sieve particle suspension to remove part of the ethanol solvent to obtain the ball-milled NaA molecular sieve particle additive solution. At this time, the mass ratio of NaA molecular sieve to ethanol in the additive solution is 1:4;

[0044] (3) Mix 5wt% of the above ball-milled NaA molecular sieve particle addition solution, 40wt% polyethersulfone and 55% dimethylformamide, mechanically stir for 1 hour, and ultrasonically disperse for 2 hours to prepare a polyethersulfone casting solution;

[0045] (4) Coat the polyethersulfone casting liquid on the non-woven fabric carrier, s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Particle sizeaaaaaaaaaa
Particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention provides a high-flux polyethersulfone membrane. A polyethersulfone ultrafiltration membrane blended with hydrophilic molecular sieves is prepared by mixing ball-milled NaA molecular sieves with a conventional polyethersulfone casting membrane solution; the membrane is placed in a NaA molecular sieve synthesis solution for carrying out hydrothermal crystallization, so that ball-milledNaA molecular sieve particles at the edges of pore passages are used for inducing and synthesizing integrated NaA molecular sieves, and the water flux of the membrane is obviously improved. The prepared polyethersulfone membrane material can be used in the field of hematodialysis.

Description

technical field [0001] The application relates to an organic membrane, in particular to a polyethersulfone ultrafiltration membrane material with large flux and its application in the field of hemodialysis. Background technique [0002] Polyethersulfone is a polymer material with excellent comprehensive properties. It has good chemical stability, acid and alkali resistance, heat resistance and aging resistance. It is used in ultrafiltration, microfiltration, reverse osmosis, gas separation, alcohol It has been widely used in water separation, olefin / alkane separation, immobilized carrier, hemodialysis and so on. Especially in the field of hemodialysis, due to the strong hydrophobicity of the surface of the polyethersulfone membrane material, it is easy to generate adsorption and deposition on the membrane surface, which hinders the membrane pores, causes membrane pollution, reduces the performance of the membrane, and shortens the service life. In order to further improve t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B01D71/68B01D61/14B01D67/00A61M1/16
CPCA61M1/16B01D61/145B01D67/0079B01D71/68
Inventor 不公告发明人
Owner 青岛市中医医院
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap