Preparation method of mould proof ceramic artwork

A technology of ceramic handicrafts and coloring agents, applied in chemical instruments and methods, fibrous fillers, dyeing polymer organic compounds, etc., can solve the problems of easy brittleness, mildew, uneven color, etc., and achieve cold and heat resistance Improved performance, better stability, and uniform color results

Inactive Publication Date: 2019-03-08
桐城市鸿江包装有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Traditional ceramic handicrafts generally use more traditional colors such as blue, bright red, etc. Handicrafts are usually products processed by hand or machine from raw materials or semi-finished products. The existing preparation methods of ceramic handicrafts are too complicated and the surface gloss Insufficient, uneven color, not bright color, easy to break under sudden cold and hot conditions, affecting the appreciation value of porcelain
Some handicrafts are prone to mildew in a humid environment due to their storage place or climate problems, making their appearance ugly and affecting people's health

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of mould proof ceramic artwork
  • Preparation method of mould proof ceramic artwork

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] 1) Toner preparation: 20 parts of potassium dichromate, 5 parts of calcium oxide, 8 parts of calcium carbonate, nano silicon oxide (particle size 20nm, specific surface area 160m 2 / g) 20 parts, mix evenly and grind finely, add 2 parts of maleic anhydride grafted polypropylene and 1 part of calcium fluoride, mix evenly, put into the kiln for calcination within the temperature range of 1000 ℃, grind after calcination, rinse until yellow water, reprocessing and grinding, extruding and granulating with an extruder under vacuum, the temperature of the extruder is 180°C, after the granulation is completed, pulverize and grind to obtain a colorant;

[0018] 2) Prepare the glaze: weigh 10% of the colorant and 90% of the lime glaze obtained in step 1), dilute the colorant and lime glaze, mix them evenly and pass through a 500-mesh sieve to obtain the glaze;

[0019] 3) Soak the bisque-fired ceramic handicraft in the soaking solution for 1 hour, air-dry it naturally, put it in a...

Embodiment 2

[0023] 1) Toner preparation: 21 parts of potassium dichromate, 6 parts of calcium oxide, 9 parts of calcium carbonate, nano silicon oxide (particle size 23nm, specific surface area 165m 2 / g) 25 parts, mix evenly and grind finely, add 3 parts of maleic anhydride grafted polypropylene, 1.5 parts of calcium fluoride and mix evenly, put into the kiln and calcined in the temperature range of 1100 ℃, crush after calcining, rinse until yellow water, reprocessing and grinding, extruding and granulating with an extruder under vacuum, the temperature of the extruder is 190°C, after the granulation is completed, pulverize and grind to obtain a colorant;

[0024] 2) Prepare the glaze: weigh 13% of the colorant and 87% of the lime glaze obtained in step 1), dilute the colorant and lime glaze, mix them evenly and pass through a 500-mesh sieve to obtain the glaze;

[0025] 3) Soak the bisque-fired ceramic handicraft in the soaking liquid for 1.5 hours, air-dry it naturally, put it in a free...

Embodiment 3

[0029] 1) Toner preparation: 22 parts of potassium dichromate, 7 parts of calcium oxide, 10 parts of calcium carbonate, nano silicon oxide (particle size 26nm, specific surface area 170m 2 / g) 30 parts, mix evenly and grind finely, add 4 parts of maleic anhydride grafted polypropylene and 2 parts of calcium fluoride, mix evenly, put into the kiln for calcination within the temperature range of 1200 ℃, grind after calcination, and rinse until yellow water, reprocessing and grinding, extruding and granulating with an extruder under vacuum, the temperature of the extruder is 200°C, after the granulation is completed, pulverize and grind to obtain a colorant;

[0030] 2) Prepare the glaze: weigh 16% of the colorant and 84% of the lime glaze obtained in step 1), dilute the colorant and lime glaze, mix them evenly and pass through a 500-mesh sieve to obtain the glaze;

[0031] 3) Soak the bisque-fired ceramic handicraft in the soaking solution for 2 hours, air-dry it naturally, put ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a mould proof ceramic artwork. The method comprises the following steps: 1) preparing a colorant; 2) preparing a glaze, namely, weighing 10-16% of the colorant obtained in step 1), and 84-90% of lime glaze; diluting and uniformly mixing the colorant and the lime glaze; then sieving through 500 meshes to obtain the glaze; 3) soaking the biscuited ceramic artwork in a soaking solution for 1-2h; naturally drying by air; freezing in a freezing warehouse under the temperature of -10 to 20 DEG C for 8-12h; moving out; and standing under normal temperature for 12-16h; glazing; and roasting through a kiln under the temperature of 1000-1200 DEG C to obtain the ceramic artwork. The prepared artwork is bright in color, hard to mould, uniform in color, and good to human health after long-term use, and is particularly used in humid coastal regions.

Description

technical field [0001] The invention relates to ceramic handicrafts, in particular to a method for preparing mildew-proof ceramic handicrafts. Background technique [0002] Green glaze, also known as malachite green glaze, is red in a reducing atmosphere and green in an oxidizing atmosphere, and is widely used in the field of ceramics. [0003] Traditional ceramic handicrafts generally use more traditional colors such as blue, bright red, etc. Handicrafts are usually products processed by hand or machine from raw materials or semi-finished products. The existing preparation methods of ceramic handicrafts are too complicated and the surface gloss Insufficient, uneven color, not bright color, easy to break under sudden cold and hot conditions, affecting the appreciation value of porcelain. Some handicrafts are prone to mildew in a humid environment due to their storage places or climate problems, making their appearance ugly and affecting people's health. Contents of the in...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/14C04B41/89C09C1/00C09C3/00C09C3/06C09C3/10
CPCC03C8/14C04B41/009C04B41/52C04B41/89C09C1/0009C09C3/006C09C3/06C09C3/10C04B2103/67C04B41/5022C04B35/00
Inventor 李涛程文斌朱扬刘先银
Owner 桐城市鸿江包装有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com