A method for preparing mullite fiber-based porous ceramics by environmentally friendly gel injection molding

A technology of mullite fiber and gel injection molding, which is applied in the field of porous ceramics, can solve problems such as toxicity, increased production costs, and damage to the nervous system, and achieve the effects of high porosity, low thermal conductivity, and excellent high-temperature performance

Active Publication Date: 2021-06-11
NORTHEASTERN UNIV LIAONING
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In the above prior art, the organic monomers used in the gel system have different degrees of toxicity, which can cause irreversible damage to the human nervous system; at the same time, the use of a large amount of organic matter in the gel system not only increases the production cost, but also During the debinding and sintering process, a large amount of environmentally harmful gases will be released

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A method for preparing mullite fiber-based porous ceramics by environmentally friendly gel injection molding
  • A method for preparing mullite fiber-based porous ceramics by environmentally friendly gel injection molding

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] In this example, the raw material adopts ρ-Al 2 o 3 powder, kaolin powder and mullite fiber, ρ-Al 2 o 3 The particle size of the powder is 5 μm, the particle size of the kaolin powder is 25 μm, and the specification size range of the mullite fiber is 5-10 μm in diameter and 50-125 μm in length. Firstly, ρ-Al with a mass percentage of 23.5% 2 o 3 powder, 26.5% kaolin powder for mixing and batching, adding deionized water with 150% of the total mass of raw materials, stirring in a mechanical stirrer and ultrasonic oscillation for 5 minutes to obtain a stable and uniform ceramic slurry, and then adding a mass percentage of 50% % mullite fiber is evenly added to the ceramic slurry, and the stirring and vibration are continued for 30 minutes to obtain a gel-type ceramic-fiber slurry, which is then injection molded and solidified at room temperature, and the molded green body is placed in a 70°C Dry in a constant temperature drying oven for 96 hours, place in a high-temp...

Embodiment 2

[0024] In this example, the raw material adopts ρ-Al 2 o 3 powder, kaolin powder and mullite fiber, ρ-Al 2 o 3 The particle size of the powder is 3 μm, the particle size of the kaolin powder is 45 μm, and the specification size range of the mullite fiber is 5-10 μm in diameter and 50-125 μm in length. First, ρ-Al with a mass percentage of 15.7% 2 o 3 powder, 17.7% kaolin powder for mixing and batching, adding deionized water with 170% of the total mass of raw materials, stirring in a mechanical stirrer and ultrasonic oscillation for 5 minutes to obtain a stable and uniform ceramic slurry, and then adding a mass percentage of 66.6 % mullite fiber is evenly added to the ceramic slurry, and the stirring and vibration are continued for 30 minutes to obtain a gel-type ceramic-fiber slurry, which is then injection molded and solidified at room temperature, and the molded green body is placed in a 70°C Dry it in a constant temperature drying oven for 72 hours, place it in a high...

Embodiment 3

[0027] In this example, the raw material adopts ρ-Al 2 o 3 powder, zircon powder and mullite fiber, ρ-Al 2 o 3 The particle size of the powder is 10 μm, the particle size of the zircon powder is 45 μm, and the standard size range of the mullite fiber is 5-10 μm in diameter and 50-125 μm in length. Firstly, ρ-Al with a mass percentage of 11.9% 2 o 3 powder, 13.1% zircon powder for mixing and batching, adding deionized water with 160% of the total mass of raw materials, stirring in a mechanical stirrer and performing ultrasonic oscillation for 5 minutes to obtain a stable and uniform ceramic slurry, and then the mass percentage Add 75% mullite fiber evenly into the ceramic slurry, continue to stir and vibrate for 30 minutes to obtain a gel-type ceramic-fiber slurry, then injection mold and solidify at room temperature, and mold the green body at 70 ℃ in a constant temperature drying oven for 48 hours, after demoulding, put it in a high-temperature furnace and sinter at a te...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
lengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of porous ceramics, in particular to an environment-friendly method for preparing mullite fiber-based porous ceramics by gel injection molding. Raw material and mass percentage: 11-32% ρ-Al 2 o 3 Powder, 13-36% kaolin or zircon powder, 33-75% mullite fiber. Take ρ-Al 2 o 3 , kaolin or zircon powder, add a certain amount of deionized water, mechanically stir and perform ultrasonic oscillation to obtain a stable and uniform ceramic slurry; then add mullite fibers evenly into the ceramic slurry, continue to stir and oscillate to obtain Gel-type ceramic-fiber slurry; then injection molded and solidified at room temperature, the molded green body is dried in a constant temperature drying oven, placed in a high-temperature furnace after demoulding, and sintered in an air atmosphere to obtain mulai Stone bound or ZrO 2 ‑Mullite-bonded mullite fiber-based porous ceramics. The process of the invention is simple and easy, and is friendly to the environment, and the prepared mullite fiber-based porous ceramic has high porosity, low thermal conductivity and high strength.

Description

technical field [0001] The invention belongs to the field of porous ceramics, in particular to an environment-friendly method for preparing mullite fiber-based porous ceramics by gel injection molding. Background technique [0002] Mullite fiber-based porous ceramics are widely used in high-temperature kilns because of their good thermal stability, low thermal conductivity and thermal expansion coefficient, excellent mechanical strength and excellent chemical stability, and their low cost. Furnace insulation refractories, chemical catalyst carriers, high-temperature flue gas filters and oil-water separation ceramic carriers and other fields. At present, mullite fiber-based porous ceramics are mostly prepared by gel injection molding. This is because the porous ceramics prepared by gel injection molding have the advantages of uniform body, reasonable pore structure, and complex components with near-net shape dimensions. . [0003] However, the currently used gel casting pro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/00C04B35/80C04B35/185C04B35/624
CPCC04B35/803C04B35/185C04B35/624C04B38/00C04B2235/3217C04B2235/349C04B2235/77C04B2235/96C04B2235/9607C04B38/0074C04B38/0067
Inventor 袁磊刘震丽刘宗泉田晨于景坤
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More