A kind of preparation method of layered functional material calcium sulfoaluminate

A technology of calcium sulfoaluminate and functional materials, applied in chemical instruments and methods, aluminum compounds, aluminum sulfur compounds, etc., can solve problems such as troublesome operation and long reaction time, and achieve convenient operation, good batch stability, and application wide range of effects

Active Publication Date: 2021-07-09
JIANGSU LONGCHANG CHEM
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] After retrieval, Feng Xiuji, Liao Guanglin, etc. according to the molar ratio of CaCO 3 :Al 2 o 3 : CaSO 4 . 2H 2 O=3:3:1 mixed raw materials, kept at 1350°C for 2 hours, cooled rapidly to obtain anhydrous calcium sulfoaluminate powder crystals; then according to the mass ratio C 4 A 3 S: PbCl 2 =5:100 mixed, put into a platinum crucible and heat up to 850°C for 24 hours, then heat up to 950°C for 48 hours to prepare anhydrous calcium sulfoaluminate single crystals with a size of 50-100µm; the reaction time of this preparation method is relatively short. Long, the raw materials are fed in batches, and the operation is more troublesome

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of layered functional material calcium sulfoaluminate
  • A kind of preparation method of layered functional material calcium sulfoaluminate

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0021] The preparation method of the layered functional material calcium sulfoaluminate in this example, the fully back-mixed explosive nucleation reactor used in the preparation method includes a reaction cylinder 1, a stirrer 2 and a mixer 3; a stirrer 2 and a mixer 3 are all arranged in the reaction cylinder 1, and the stirrer 2 is driven by a stirring motor.

[0022] The reaction cylinder 1 includes an inner cylinder 11 and an outer cylinder 12; a heat exchange cavity is formed between the inner cylinder 11 and the outer cylinder 12, and an outlet of the heat exchange cavity is provided on the upper side of the outer cylinder 12 13. A heat exchange cavity inlet 14 is provided on the lower side of the outer cylinder 12; the reaction cylinder 1 is divided into an upper reaction cylinder 15 and a lower reaction cylinder 16 by a mixer 3 in the reaction cylinder 1; The reaction cylinder 1 is provided with a cylinder cover 17 and the cylinder cover 17 is provided with a first fe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of calcium sulfoaluminate, a layered functional material. The preparation method comprises the following steps: (1) mixing a certain proportion of calcium sulfate, aluminum hydroxide and calcium oxide into a fully back-mixed explosive nucleation reactor , and add water higher than that of each material for mixing; (2) Use a fully back-mixed explosive nucleation reactor to synthesize sulfur under the conditions of a rotor speed of 4000-6000rpm, a voltage of 220-330V, and nucleation of 8-16min Calcium aluminate gel, then crystallize calcium sulfoaluminate gel at 90-150°C for 12-16h, cool down to 30-50°C, stir for 12-16h, then heat up to 90-150°C, cycle 3-5 times, can The layered functional material calcium sulfoaluminate is prepared. The advantage of the present invention is: the preparation method of the layered functional material calcium sulfoaluminate of the present invention, calcium sulfate, aluminum hydroxide and calcium oxide are nucleated and grown in a full back-mixing explosive nucleation reactor through a "one-pot method" , which effectively simplifies the preparation process of calcium sulfoaluminate, shortens the preparation time, simplifies the reaction operation, and improves the production efficiency.

Description

technical field [0001] The invention belongs to the technical field of layered functional inorganic materials, in particular to a method for preparing layered functional material calcium sulfoaluminate. Background technique [0002] Calcium sulfoaluminate has a layered structure, and its structural formula can be written as [Ca 2 Al(OH) 6 ](SO 4 )0 3 , which is the main component of sulphoaluminate cement, sulphoaluminate expansion agent, etc. The properties of quick hardening, dry strength and micro expansion of minerals are closely related to the crystal sister of anhydrous calcium sulfoaluminate. [0003] After retrieval, Feng Xiuji, Liao Guanglin, etc. according to the molar ratio of CaCO 3 :Al 2 o 3 : CaSO 4 . 2H 2 O=3:3:1 mixed raw materials, kept at 1350°C for 2 hours, cooled rapidly to obtain anhydrous calcium sulfoaluminate powder crystals; then according to the mass ratio C 4 A 3 S: PbCl 2 =5:100 mixed, put into a platinum crucible and heat up to 850°C...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01F7/68B01J19/18B01J19/00
CPCB01J19/0013B01J19/0066B01J19/18C01F7/68B01J2219/00094C01F7/78
Inventor 张剑宇吴春江佘卫民
Owner JIANGSU LONGCHANG CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com