Cementing material with coal gangue as raw material and preparation method of cementing material

A cementitious material and coal gangue technology, applied in cement production, etc., can solve the problems of weathered coal gangue not being effectively utilized, occupying land resources, fires, landslides, etc., to achieve flexible and adjustable composition and performance, improve the environment, and utilize high rate effect

Active Publication Date: 2019-03-19
YANGZHOU UNIV
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the comprehensive utilization rate of coal gangue in my country is only 64%, which is mainly used for power generation fuel, production of building materials, land reclamation and subsidence backfill, etc. A large amount of weathered coal gangue has not been effectively utilize

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cementing material with coal gangue as raw material and preparation method of cementing material
  • Cementing material with coal gangue as raw material and preparation method of cementing material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] A cementitious material (by mass parts) using coal gangue as raw material contains the following components:

[0022] 75 parts of coal gangue

[0023] Quicklime 25 parts

[0024] Sodium hydroxide 1.3 parts

[0025] Digestion water 50 parts

[0026] Forming water 40 parts

[0027] Grind the weathered coal gangue to 4.5% of the 80 μm sieve, and then microwave activation for 5 minutes to form activated coal gangue powder. Mix 75 parts of activated coal gangue powder, 25 parts of quicklime, 1.3 parts of sodium hydroxide, and 50 parts of water. Digest at room temperature for 6h. Add 40 parts of water to the digested raw materials to form pellets, put the pelleted regular samples into a steam curing box at 97°C for 12 hours, and then put the steamed materials into a kiln for calcination at 800°C for 1 hour, and then cool them quickly. Take 92 parts of clinker, mix with 8 parts of natural gypsum and 0.5 parts of polycarboxylate superplasticizer, mix evenly, and grind it w...

Embodiment 2

[0029] A cementitious material (by mass parts) using coal gangue as raw material contains the following components:

[0030] Coal gangue 70 parts

[0031] Quicklime 30 parts

[0032] Sodium Sulfate 2 parts

[0033] Digestion water 50 parts

[0034] Forming water 40 parts

[0035] Grind the weathered coal gangue to 4.0% of the 80 μm sieve, and then microwave activation for 4 minutes to form activated coal gangue powder. Mix 70 parts of activated coal gangue powder, 30 parts of quicklime, 2 parts of sodium sulfate, and 50 parts of water evenly. Digest at room temperature for 6h. Add 40 parts of water to the digested raw materials to form pellets, put the pelleted regular samples into a steam curing box at 99°C for 12 hours, and then put the steamed materials into a kiln for calcination at 750°C for 1 hour, and then cool them quickly. Take 94 parts of clinker, mix with 6 parts of natural gypsum and 1.0 part of calcium lignosulfonate, mix evenly, and grind it with ultra-fine ...

Embodiment 3

[0037] A cementitious material (by mass parts) using coal gangue as raw material contains the following components:

[0038] 65 parts of coal gangue

[0039] Quicklime 35 parts

[0040] Sodium hydroxide 1.94 parts

[0041] Digestion water 50 parts

[0042] Forming water 40 parts

[0043] Grind the weathered gangue to 4.4% of the 80 μm sieve, and then activate it by microwave for 8 minutes to form activated gangue powder. Mix 65 parts of activated coal gangue powder, 35 parts of quicklime, 1.94 parts of sodium hydroxide, and 50 parts of water. Digest at room temperature for 6h. Add 40 parts of water to the digested raw materials to form pellets, put the pelleted regular samples into a steam curing box at 97°C for 12 hours, and then put the steamed materials into a kiln for calcination at 850°C for 0.5 hours, and then cool them down quickly. Take 93 parts of clinker, mix with 7 parts of natural gypsum and 1.5 parts of nano-based superplasticizer, mix them evenly, and grind ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Specific surface areaaaaaaaaaaa
Login to view more

Abstract

The invention discloses a cementing material with coal gangue as a raw material and a preparation method of the cementing material. The cementing material contains the following components in parts bymass: 92-95 parts of clinker, 3-7 parts of gypsum and 0.5-1.5 parts of water reducer, wherein raw materials of the clinker include the following components in parts by mass: 60-75 parts of activatedcoal gangue powder, 25-40 parts of quick lime, 0.5-2 parts of exciting agent and 70-90 parts of water. The novel cementing material is prepared by carrying out mechanical-microwave combined activationon coal gangue, then, uniformly mixing coal gangue with the quick lime, and grinding the mixture by using a superfine cement grinding mill by using chemical strengthening, hydrothermal synthesis andlow-temperature calcination methods. A great deal of piled and stored coal gangue is utilized, so that the land occupied by the coal gangue is reduced; natural resources can be saved, and the deterioration of an ecological environment due to exploitation of cement raw materials is effectively solved; and the preparation method is simple, low in energy consumption, high in coagulation speed, high in strength and good in corrosion resistance, and the strength of the cementing material at each age meets a corresponding strength requirement of P.F 32.5 cement.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a cementitious material using coal gangue as a raw material and a preparation method thereof. Background technique [0002] At present, there are about 2,600 large-scale coal gangue dumps in my country, covering an area of ​​about 1.5×10 8 m 2 , the total amount of stored coal gangue exceeds 5 billion tons, and is still increasing at a rate of 150 million to 200 million tons per year. However, the comprehensive utilization rate of coal gangue in my country is only 64%, which is mainly used for power generation fuel, production of building materials, land reclamation and subsidence backfill, etc. A large amount of weathered coal gangue has not been effectively utilized. If a large amount of weathered coal gangue is not treated, it will not only occupy a large amount of land resources, but also generate dust and pollute the atmosphere. If it is discharged ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B7/14
CPCC04B7/14Y02P40/10
Inventor 龚泳帆刘淼葛晨杨鼎宜张鸣
Owner YANGZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap