A processing aid and plastic technology, applied in the field of PVC plastic processing aids, can solve the problems of slow melt relaxation, poor PVC melt ductility, melt breakage, etc. , the effect of saving production costs

Inactive Publication Date: 2019-03-19
遵义宏龙塑料有限责任公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The ductility of PVC melt is poor, which can easily lead to melt breakage; PVC melt can relax slowly, which can easily lead to rough surface, dull and shark skin, etc.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] A kind of PVC plastic processing aid, it is made of the raw material of following parts by weight:

[0011] 2 parts of talcum powder, 1 part of lubricant, 0.8 parts of modified chitosan, 0.6 parts of alginate, 0.3 parts of sodium fluoride, 10 parts of galvanized carbon black, 4 parts of sodium carbonate, 6 parts of tertiary vinyl acetate resin, 20 parts of deionized water, 10 parts of butyl acrylate, 2 parts of pentaerythritol triacrylate, 2 parts of polystyrene, 0.5 parts of maleic anhydride, 1 part of glycerin, 6 parts of zinc stearate.

Embodiment 2

[0013] A kind of PVC plastic processing aid, it is made of the raw material of following parts by weight:

[0014] 6 parts of talcum powder, 3 parts of lubricant, 2.5 parts of modified chitosan, 1.2 parts of alginate, 0.8 part of sodium fluoride, 20 parts of galvanized carbon black, 7 parts of sodium carbonate, 8 parts of tertiary vinyl acetate resin, 35 parts of deionized water, 16 parts of butyl acrylate, 3 parts of pentaerythritol triacrylate, 4 parts of polystyrene, 1.5 parts of maleic anhydride, 3 parts of glycerin, and 9 parts of zinc stearate.

Embodiment 3

[0016] A kind of PVC plastic processing aid, it is made of the raw material of following parts by weight:

[0017] 4 parts of talcum powder, 2 parts of lubricant, 1.7 parts of modified chitosan, 0.9 part of alginate, 0.5 part of sodium fluoride, 15 parts of galvanized carbon black, 5.5 parts of sodium carbonate, 7 parts of tertiary vinyl acetate resin, 27 parts of deionized water, 13 parts of butyl acrylate, 2.5 parts of pentaerythritol triacrylate, 3 parts of polystyrene, 1 part of maleic anhydride, 2 parts of glycerin, 7.5 parts of zinc stearate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to a PVC plastic processing aid. The PVC plastic processing aid is prepared from the following raw materials in parts by weight: 2-6 parts of talcum powder, 1-3 parts of a lubricant, 0.8-2.5 parts of modified chitosan, 0.6-1.2 parts of alginate, 0.3-0.8 part of sodium fluoride, 10-20 parts of galvanized carbon black, 4-7 parts of sodium carbonate, 6-8 parts of ternary vinyl chloride-vinyl acetate resin, 20-35 parts of deionized water, 10-16 parts of butyl acrylate, 2-3 parts of pentaerythritol triacrylate, 2-4 parts of polystyrene, 0.5-1.5 parts of maleic anhydride, 1-3 parts of glycerin and 6-9 parts of zinc stearate. The PVC plastic processing aid has the beneficial effects that the heat resistance and the weather resistance are very good, the aging of the plastic can be effectively delayed, the production cost is saved, and the PVC plastic processing aid is suitable for being widely applied.

Description

technical field [0001] The invention relates to a PVC plastic processing aid. Background technique [0002] PVC is one of the five general-purpose plastics in the world. In recent years, with the rapid development of my country's national economy, PVC products have grown at a rate of more than 20% every year. By 2005, the annual output of PVC has reached 7.5 million tons. It is predicted that by 2007 PVC demand will exceed 10 million tons. Polyvinyl chloride (PVC) is a general-purpose plastic with a wide range of uses. It has an irreplaceable position in the fields of chemical building materials, chemical anti-corrosion and daily products. The ductility of PVC melt is poor, which can easily lead to melt breakage; PVC melt can relax slowly, which can easily lead to rough, dull and shark skin on the surface of the product. Therefore, it is often necessary to add processing aids during PVC processing to improve the above-mentioned defects of its melt. Processing aids are main...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08L27/06C08L25/06C08L5/08C08L5/04C08K13/06C08K9/10C08K3/04C08K3/34C08K5/098C08K3/26
CPCC08L27/06C08K2003/262C08L2201/08C08L2205/025C08L2205/035C08L25/06C08L5/08C08L5/04C08K13/06C08K9/10C08K3/04C08K3/34C08K5/098C08K3/26
Inventor 章严刘
Owner 遵义宏龙塑料有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap