SPR (Surface Plasmon Resonance) sensor made with graphene/gold/D-type plastic optical fiber and preparation method thereof

A technology of plastic optical fiber and graphene, which is applied in the direction of instruments, scientific instruments, analytical materials, etc., can solve the problems such as difficult to grow graphene structure, achieve the effect of improving chemical stability, improving sensitivity and reducing contact resistance

Active Publication Date: 2019-03-29
SHANDONG NORMAL UNIV
View PDF8 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when this method prepares the plastic optical fiber whose core layer is PMMA, it is not suitable to add the graphene layer by removing PMMA in the wet transfer, and it is even more unsuitable to cover it directly with a layer of metal in a tube furnace with too high temperature. The method of growing graphene; in addition, this method grows graphene directly on gold or silver, but in CVD growing graphene, only growing on copper foil can guarantee the quality of graphene enough, and can grow large-area single Crystalline graphene, it is difficult to grow ideal graphene structure on gold and silver

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • SPR (Surface Plasmon Resonance) sensor made with graphene/gold/D-type plastic optical fiber and preparation method thereof
  • SPR (Surface Plasmon Resonance) sensor made with graphene/gold/D-type plastic optical fiber and preparation method thereof
  • SPR (Surface Plasmon Resonance) sensor made with graphene/gold/D-type plastic optical fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A preparation method of graphene / gold / D-type plastic optical fiber SPR sensor, comprising the following preparation steps:

[0041] (1) Make D-type optical fiber: a section of 15cm plastic optical fiber (material is PMMA) with a diameter of 1 micron, remove the fiber cladding and part of the core in the sensing area by side polishing method, and open a length of 1cm, depth Groove-shaped sensing area 30% of fiber diameter. The D-type sensing area is then rinsed with deionized water to remove impurities;

[0042] (2) growth graphene: the copper foil after polishing is put into tube furnace, by passing into the mixed gas of the hydrogen of 50sccm and 50sccm methane in tube furnace, keep 30min under 1000 °, graphene layer number is monolayer, then cut the graphene / copper foil into small rectangular stripes (1.2cm×0.5cm);

[0043] (3) The gold film is directly thermally evaporated onto the graphene: put a 7.5cm high-purity gold wire into a molybdenum boat (length: 100mm, w...

Embodiment 2

[0046] A preparation method of graphene / gold / D-type plastic optical fiber SPR sensor, comprising the following preparation steps:

[0047] (1) Make D-shaped optical fiber: a section of 15cm plastic optical fiber (material is PMMA) with a diameter of 1 micron, remove the fiber cladding and part of the core in the sensing area by side polishing, and open a length of 2cm, depth Groove-shaped sensing area 45% of fiber diameter. The D-type sensing area is then rinsed with deionized water to remove impurities;

[0048] (2) growth graphene: the copper foil after polishing is put into tube furnace, by passing into the mixed gas of the hydrogen of 60sccm and 40sccm methane in tube furnace, keep 30min under 1000 °, graphene layer number is 3 layers, then cut the graphene / copper foil into small rectangular stripes (2cm×0.5cm);

[0049] (3) Gold film is directly thermally evaporated onto graphene: put 8.5cm high-purity gold wire into a molybdenum boat (100mm in length, 10mm in width, an...

Embodiment 3

[0052] A preparation method of graphene / gold / D-type plastic optical fiber SPR sensor, comprising the following preparation steps:

[0053] (1) Make a D-type optical fiber: a section of 15cm, a plastic optical fiber (material is PMMA) with a diameter of 1 micron, remove the fiber cladding and part of the core in the sensing area by side polishing, and set a length of 1.2cm, Groove-shaped sensing zone with a depth of 20% of the fiber diameter. The D-type sensing area is then rinsed with deionized water to remove impurities;

[0054] (2) growth graphene: the copper foil after polishing is put into tube furnace, by passing into the mixed gas of the hydrogen of 50sccm and 50sccm methane in tube furnace, keep 30min under 1000 °, graphene layer number is monolayer, then cut the graphene / copper foil into small rectangular stripes (1.2cm×0.5cm);

[0055] (3) Gold film is directly thermally evaporated onto graphene: put 6.5cm high-purity gold wire into molybdenum boat (length 100mm, w...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
thicknessaaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of SPR sensors, and particularly relates to a SPR sensor made with a graphene/gold/D-type plastic optical fiber and a preparation method. The method comprises the following steps of: (1) forming a groove shaped sensing area in the fiber, and preparing a D-type fiber; (2) growing the graphene on a copper foil by using a chemical vapor deposition method,and directly evaporating a gold film onto the graphene through a thermal evaporation method, to obtain a gold/graphene/copper foil composite layer; (3) corroding the copper foil in the gold/graphene/copper foil composite layer, and moving the obtained graphene/gold film to a D-type optical fiber, to obtain the sensor. According to the preparation method, the gold is directly evaporated onto the graphene through the thermal evaporation method, so that the graphene and the gold film are perfectly laminated; and then the graphene/gold etched off the copper foil is moved to the D-type plastic optical fiber, so that the structure of the gold plus graphene is realized on the plastic optical fiber. The prepared SPR sensor made with the graphene/gold/D-type plastic optical fiber has the characteristic of a high recognition sensitivity of complementary and non-complementary DNA strands.

Description

technical field [0001] The invention belongs to the technical field of surface plasmon resonance (SPR) sensors, in particular to a graphene / gold / D-type plastic optical fiber SPR sensor and a preparation method. Background technique [0002] Since the fiber-optic SPR sensor was proposed in 1993, this technology has attracted increasing research interest. Optical fiber surface plasmon sensor, which can track and study the subtle changes on the surface of the medium, realizes ultra-sensitive and label-free chemical and biological analysis, and has important applications in food detection and disease diagnosis. [0003] So far, research scholars have made many efforts to improve the performance of fiber optic SPR sensors. For example, various optical fiber structures have been proposed: tapered, D-shaped, U-shaped, etc. The cylindrical fiber geometry is not suitable for the transfer of large-area material layer films. Meanwhile, the film is not easy to stabilize on the cylind...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G01N21/552G01N21/01
CPCG01N21/01G01N21/554G01N21/553
Inventor 张超姜守振徐纪华修显武
Owner SHANDONG NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap