Synthetic resin tile and preparation method thereof

A technology of synthetic resin and polyvinyl chloride resin, which is applied in the field of resin tiles, can solve the problems of short service life of synthetic resin tiles, and achieve the effects of prolonging service life, high strength and good toughness

Pending Publication Date: 2019-04-09
LESHAN JIACHENG BUILDING MATERIAL
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The purpose of the present invention is to provide a synthetic resin tile and its preparation method to solve the problem of short service life of the existing synthetic resin tile

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The synthetic resin tile of this embodiment includes: an upper surface layer, a middle layer and a lower bottom layer; the upper surface layer, the middle layer and the lower bottom layer are stacked. The thickness of the upper surface layer is 0.1 mm, the thickness of the middle layer is 2.5 mm, and the thickness of the lower bottom layer is 0.5 mm. in:

[0027] The upper surface layer is polysulfone engineering resin;

[0028] The middle layer comprises: in parts by weight, 900 parts of polyvinyl chloride resin powder, 500 parts of calcium carbonate powder with particle diameter of 1200 objects, 40 parts of chlorinated polyethylene, 30 parts of composite stabilizer, 5 parts of stearic acid, 2 parts of PE wax 15 parts, 2 parts of paraffin wax and 15 parts of chopped E-glass fiber with a length of 4mm;

[0029] The lower bottom layer includes: in parts by weight, 800 parts of waste pure white plastic steel materials with a particle size of 30 meshes, 400 parts of calc...

Embodiment 2

[0032] The synthetic resin tile of this embodiment includes: an upper surface layer, a middle layer and a lower bottom layer; the upper surface layer, the middle layer and the lower bottom layer are stacked. The thickness of the upper surface layer is 0.2mm, the thickness of the middle layer is 3.5mm, and the thickness of the lower bottom layer is 1mm. in:

[0033] The upper surface is polyarylsulfone engineering resin;

[0034] The middle layer comprises: in parts by weight, 1100 parts of polyvinyl chloride resin powder, 1000 parts of calcium carbonate powder with particle diameter of 1300 objects, 50 parts of chlorinated polyethylene, 40 parts of composite stabilizer, 10 parts of stearic acid, 6 parts of PE wax 6 parts of paraffin wax and 25 parts of short-cut alkali-free glass fibers with a length of 5 mm;

[0035] The lower bottom layer includes: in parts by weight, 1200 parts of waste pure white plastic steel material with a particle size of 50 mesh, 600 parts of calciu...

Embodiment 3

[0038] The synthetic resin tile of this embodiment includes: an upper surface layer, a middle layer and a lower bottom layer; the upper surface layer, the middle layer and the lower bottom layer are stacked. The thickness of the upper surface layer is 0.15mm, the thickness of the middle layer is 3mm, and the thickness of the lower bottom layer is 0.7mm. in:

[0039] The upper surface is polyarylethersulfone engineering resin;

[0040] The middle layer comprises: in parts by weight, 1000 parts of polyvinyl chloride resin powder, 750 parts of calcium carbonate powder with particle diameter of 1250 objects, 45 parts of chlorinated polyethylene, 35 parts of composite stabilizer, 8 parts of stearic acid, 4 parts of PE wax 4 parts of paraffin wax and 20 parts of chopped E-glass fiber with a length of 4.5 mm.

[0041] The lower bottom layer includes: in parts by weight, 1000 parts of waste plastic steel materials with a particle size of 40 mesh, 500 parts of calcium carbonate powde...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a synthetic resin tile and a preparation method thereof, belonging to the technical field of resin tiles. According to the preparation method, chopped alkali-free glass fibersare added into a polyvinyl chloride resin base material so as to form a network skeleton structure in the base material, so that the aging of the resin is delayed, and the service life of the synthetic resin tile is prolonged. Meanwhile, the synthetic resin tile is divided into three layers, namely an upper surface layer, a middle layer and a lower surface layer which have different effects, so that the resin tile has multiple properties of weather resistance, ultraviolet resistance and the like further has relatively high practicability and high product quality on the basis that basic properties (lightness, high strength, good tenacity, corrosion resistance and the like) of the resin tile are guaranteed.

Description

technical field [0001] The invention relates to the technical field of resin tiles, in particular to a synthetic resin tile and a preparation method thereof. Background technique [0002] Synthetic resin tiles are tiles produced by synthetic resin technology. Synthetic resin tile has the advantages of long-lasting color, light weight, self-waterproof, toughness, thermal insulation, sound insulation, corrosion resistance, wind and shock resistance, hail resistance, pollution resistance, green environmental protection, fire prevention, insulation, convenient installation, etc., and has a beautiful and three-dimensional shape Strong sense. But the performance of the existing synthetic resin tile is poor, the resin tile is easy to age, and the service life is short. Contents of the invention [0003] The object of the present invention is to provide a synthetic resin tile and its preparation method to solve the problem of short service life of the existing synthetic resin ti...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B27/08B32B27/30B32B27/18C08L27/06C08L23/28C08L101/00C08K13/04C08K3/26C08K5/09C08K7/14B29C48/21B29C48/92B29L9/00
CPCB29L2009/00B32B27/08B32B27/18B32B27/304B32B2250/24B32B2307/71B32B2307/712B32B2307/714B32B2419/02C08K2003/265C08K2201/004C08L27/06C08L101/00C08L2205/035C08L2207/20C08L23/286C08K13/04C08K3/26C08K5/09C08K7/14
Inventor 李镇江
Owner LESHAN JIACHENG BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap