Waterborne polyurethane coating adhesive for textile and fabric treatment method

A technology of water-based polyurethane and textiles, applied in the field of nylon fabrics, to achieve the effects of excellent air permeability, low volatility, and high temperature volatility

Active Publication Date: 2019-04-12
LIAONING FIXED STAR FINE CHEM
View PDF8 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] At present, there is no technical disclosure of fabric coating glue and fabric coating treatment method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Waterborne polyurethane coating adhesive for textile and fabric treatment method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] (1) Mix 30 parts of deionized water and 2.0 parts of silicone modified elastic microspheres and stir evenly;

[0057] (2) Add 70 parts of water-based polyurethane emulsion, 2.0 parts of antistatic agent, 0.5 parts of ultraviolet absorber, and 0.2 parts of water-based defoamer, and stir evenly;

[0058] (3) Add 2.0 parts of associative water-based polyurethane thickener, stir evenly, and filter to obtain water-based polyurethane coating glue; the solid content is 28.87%, and the viscosity is 1730mPa·s;

[0059] (4) Waterproof the 20D / 380T nylon fabric base fabric: soak and roll with C6 waterproof agent (10g / L), dry at 165-170°C for 1 minute;

[0060] (5) Calendering treatment: pressure 10MPa, 80°C;

[0061] (6) Coating treatment: use the water-based polyurethane coating glue obtained in the above step (3) to dry-coat the base cloth obtained in the above step (5), with a knife thickness of 1.5mm, and place it in an oven at 150-165°C Dry for 1 minute, dry weight gain 7.0...

Embodiment 2

[0064] (1) Mix 33 parts of deionized water and 4.0 parts of silicone modified elastic microspheres and stir evenly;

[0065] (2) Add 67 parts of water-based polyurethane emulsion, 3.0 parts of antistatic agent, 0.75 parts of ultraviolet absorber, and 0.3 parts of water-based defoamer, and stir evenly;

[0066] (3) Add 2.5 parts of associative water-based polyurethane thickener, stir evenly, and filter to obtain water-based polyurethane coating glue; solid content 28.77%, viscosity 1680mPa·s;

[0067] (4) Waterproof the 20D / 380T nylon fabric base fabric: soak and roll with C6 waterproof agent (10g / L), dry at 165-170°C for 1 minute;

[0068] (5) Calendering treatment: pressure 10MPa, 100°C;

[0069] (6) Coating treatment: use the water-based polyurethane coating glue obtained in the above step (3) to dry-coat the base cloth obtained in the above step (5), with a knife thickness of 0.5mm, and place it in an oven at 150-165°C Dry for 1 minute, dry weight gain 5.0g / m 2 .

[007...

Embodiment 3

[0072] (1) Mix 35 parts of deionized water and 3.0 parts of silicone modified elastic microspheres and stir evenly;

[0073] (2) Add 65 parts of water-based polyurethane emulsion, 3.0 parts of antistatic agent, 1.0 part of ultraviolet absorber, and 0.2 parts of water-based defoamer, and stir evenly;

[0074] (3) Add 3.0 parts of associative water-based polyurethane thickener, stir evenly, and filter to obtain water-based polyurethane coating glue; the solid content is 27.16%, and the viscosity is 1750mPa·s;

[0075] (4) Waterproof the 20D / 380T nylon fabric base fabric: soak and roll with C6 waterproof agent (10g / L), dry at 165-170°C for 1 minute;

[0076] (5) Calendering treatment: pressure 10MPa, 90°C;

[0077] (6) Coating treatment: use the water-based polyurethane coating glue obtained in the above step (3) to dry-coat the base cloth obtained in the above step (5), with a knife thickness of 1.0mm, and place it in an oven at 150-165°C Dry for 1 minute, dry weight gain 6.0g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Viscosityaaaaaaaaaa
Particle sizeaaaaaaaaaa
Air permeabilityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a waterborne polyurethane coating adhesive for a textile and a fabric treatment method. The waterborne polyurethane coating adhesive is prepared by compounding 60-70 parts byweight of waterborne polyurethane emulsion, 2.0-4.0 parts by weight of organic silicon modified elastic microspheres, 2.0-4.0 parts by weight of an anti-static agent, 0.5-1.0 part by weight of an ultraviolet absorbent, 0.2-0.3 part by weight of a waterborne de-foaming agent, 2.0-4.0 parts by weight of an association type waterborne polyurethane thickener and 30-40 parts by weight of deionized water. The fabric achieves the functions of air permeability, water pressure resistance, ultraviolet resistance, static electricity resistance and downproofness after being coated with the waterproof, glossy and waterborne polyurethane adhesive.

Description

technical field [0001] The invention relates to a water-based polyurethane coating adhesive for textiles and a post-treatment method for textile fabrics, in particular to a water-based polyurethane coating adhesive for textiles with the characteristics of air permeability, water pressure resistance, ultraviolet resistance, antistatic, and anti-drilling functions. And post-processing method of textile fabrics, especially suitable for nylon fabrics. Background technique [0002] At present, there are various styles of down jackets on the market. With the improvement of living standards, the functionality of down jackets is not limited to keeping warm. People also have more fashionable pursuits for the feel and style of down jackets. There is also a broader demand for functionality. [0003] For the functionality of down jacket fabrics, anti-drill down is the first demand for down jacket fabrics, and what is currently needed in the market is not only down jacket fabrics with a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D06N3/00D06N3/14
CPCD06N3/0034D06N3/0059D06N3/0061D06N3/0088D06N3/146D06N3/147D06N2205/10D06N2209/046D06N2209/103D06N2209/123D06N2209/128D06N2209/16D06N2209/1678
Inventor 陈剑冰唐丽荣星陈龙
Owner LIAONING FIXED STAR FINE CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap