An alloy coating and preparation process technology, applied in the field of stainless steel alloys, can solve the problems of difficulty in enhancing the surface of the coating, large residual stress of the coating, cracking or even peeling, etc., to achieve small surface roughness, large thickness variation range, The effect of improving wear resistance

Inactive Publication Date: 2019-04-30
淮北市菲美得环保科技有限公司
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the large mismatch of thermal expansion coefficient and elastic modulus between tungsten carbide and nickel-based alloys, the coatings prepared by flame spraying and explosive spraying are prone to cracking or even peeling off due to the weak bonding force between the coating and the substrate during use; The residual stress of

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The technical solutions in the embodiments of the present invention will be clearly and completely described below. Obviously, the described embodiments are only some of the embodiments of the present invention, but not all of them. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0020] A preparation process for a wear-resistant stainless steel alloy coating, comprising the following steps:

[0021] S1, the selection of raw materials: the selected raw materials are tungsten carbide powder, NiCrBSi self-fluxing brazing alloy powder, polytetrafluoroethylene, 316L stainless steel plate, and the particle size of the tungsten carbide powder is 40- 70um, the particle diameter of described NiCrBSi self-fluxing brazing alloy powder is 50-80um;

[0022] S2. Alloy powder embedded in polytetrafluoroethylene: mix NiCrB...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation technology of an abrasion-resistant stainless steel alloy coating. The preparation technology includes the following steps that S1, raw materials are selected; S2, alloy powder is embedded into polytef; S3, a metal cloth is prepared and stacked; S4, brazing is conducted; and S5, the stainless steel surface is covered with the alloy coating. According to the preparation technology of the abrasion-resistant stainless steel alloy coating, tungsten carbide hard alloy powder and NiCrBSi self-fluxing brazing alloy powder are treated as hard phases and are rolledinto the cloth with the polytef, then the cloth adheres to the surface of stainless steel, then brazing is conducted to form a metallurgical bonded complex coating, and the flexible metal cloth can be adhered to the surface of a part of a complex structure; and thermal residual stress of the coating is small due to the fact that the metal cloth and a substrate are heated at the same time during brazing, the variation range of the thickness of the coating is large, surface roughness of the coating is small, thus the surface of the stainless steel has high abrasion resistance and erosion resistance, the grinding material abrasion resistant performance of the obtained coating is much higher than the grinding material abrasion resistant performance of a flame surfacing coating, and abrasion resistance and strength of extension of the stainless steel substrate are remarkably improved.

Description

technical field [0001] The invention belongs to the technical field of stainless steel alloys, and in particular relates to a preparation process of a wear-resistant stainless steel alloy coating. Background technique [0002] Stainless steel is the abbreviation of stainless acid-resistant steel, and the steel grades that are resistant to weak corrosive media such as air, steam, water, or have stainless properties are called stainless steel; The steel grade is called acid-resistant steel. Due to the difference in chemical composition of the two, their corrosion resistance is different. Ordinary stainless steel is generally not resistant to chemical medium corrosion, while acid-resistant steel is generally stainless. Stainless steel alloy coating refers to the protective layer coated on the surface of the workpiece. The protective layer protects the stainless steel and improves the wear resistance and corrosion resistance of the stainless steel. [0003] Tungsten carbide re...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22F7/02C23C24/10
CPCB22F7/02B22F2007/045C23C24/103
Inventor 刘永飞马敏
Owner 淮北市菲美得环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap