Seaweed polyester fiber and preparation method thereof

A polyester fiber and seaweed technology, applied in the field of fibers, can solve the problems of unsustainable functionality, affecting spinning performance, disappearing, etc., and achieve the effects of low boiling water shrinkage, good dyeing uniformity, and good hygroscopicity.

Inactive Publication Date: 2019-05-17
ZHONGKE TEXTILE RES INST QINGDAO CO LTD
View PDF6 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

As seen from the above-mentioned prior art, most of the seaweed polyester fibers are attached to the textile fibers through post-treatment, but with daily use, washing, etc., the modification effect of the fiber surface will gradually decrease. or even disappear, functionality is not durable
[0006] At the same time, due to the addition of seaweed extract, the high hydrophilic property of seaweed extract causes the abnormal problems of high boiling water shrinkage and uneven dyeing of the prepared polyester fiber, which affects the spinning performance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Seaweed polyester fiber and preparation method thereof
  • Seaweed polyester fiber and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0033] Embodiment 1 A kind of seaweed polyester fiber, its raw material comprises polyester chip, seaweed extract, modifier, regulator; The mass ratio of described polyester chip, seaweed extract, modifier, regulator is 90: 3.3:4.5:5;

[0034] The polyester chips mentioned above: water content ≤0.2%, acetaldehyde content ≤1%, acid value max.35Meq / kg, intrinsic viscosity 0.865±0.015dl / g, purchased from Suzhou Lijuncheng Plastics Import & Export Co., Ltd. , item number: LJC-CB-608S; said seaweed extract: seaweed polysaccharide content ≥ 50%, water content ≤ 0.5%;

[0035] Described modifying agent is made up of triethyl citrate, bismuth molybdate, simethicone, sodium dodecylbenzene sulfonate; Preferably, in described modifying agent, triethyl citrate, molybdic acid The preferred ratio of bismuth, simethicone, and sodium dodecylbenzenesulfonate is 12:1:5:0.3.

[0036] The preferred mass ratio of sodium acetate, sodium alginate and isopropanol in the conditioner is 5:2:3.

[00...

Embodiment 2

[0046] Embodiment 2 A kind of seaweed polyester fiber, its raw material comprises polyester chip, seaweed extract, modifier, regulator; The mass ratio of described polyester chip, seaweed extract, modifier, regulator is 110: 4.5:5.0:3.5;

[0047] The polyester chips mentioned above: water content ≤0.2%, acetaldehyde content ≤1%, acid value max.35Meq / kg, intrinsic viscosity 0.865±0.015dl / g, purchased from Suzhou Lijuncheng Plastics Import & Export Co., Ltd. , item number: LJC-CB-608S; said seaweed extract: seaweed polysaccharide content ≥ 50%, water content ≤ 0.5%;

[0048] Described modifying agent is made up of triethyl citrate, bismuth molybdate, simethicone, sodium dodecylbenzene sulfonate; Preferably, in described modifying agent, triethyl citrate, molybdic acid The preferred ratio of bismuth, simethicone and sodium dodecylbenzenesulfonate is 15:1:8:0.2.

[0049] Described conditioning agent is made up of sodium acetate, sodium alginate, isopropanol;

[0050] Preferably...

Embodiment 3

[0060] Embodiment 3 A kind of seaweed polyester fiber, its raw material comprises polyester chip, seaweed extract, modifier, regulator; The mass ratio of described polyester chip, seaweed extract, modifier, regulator is 95: 3.8:5.5:3.0;

[0061] The polyester chips mentioned above: water content ≤0.2%, acetaldehyde content ≤1%, acid value max.35Meq / kg, intrinsic viscosity 0.865±0.015dl / g, purchased from Suzhou Lijuncheng Plastics Import & Export Co., Ltd. , item number: LJC-CB-608S; said seaweed extract: seaweed polysaccharide content ≥ 50%, water content ≤ 0.5%;

[0062] Described modifying agent is made up of triethyl citrate, bismuth molybdate, simethicone, sodium dodecylbenzene sulfonate; Preferably, in described modifying agent, triethyl citrate, molybdic acid The preferred ratio of bismuth, simethicone, and sodium dodecylbenzenesulfonate is 16:1:6:0.3.

[0063] Described conditioning agent is made up of sodium acetate, sodium alginate, isopropanol;

[0064] The prefer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
shrinkageaaaaaaaaaa
Login to View More

Abstract

The invention provides seaweed polyester fiber. The fiber is characterized in that the raw materials comprise polyester slices, seaweed extract, a modifier and a regulator which are in a mass ratio being (90-110):(3.3-5.7):(4.1-6.2):(3-5). According to the seaweed polyester fiber, the seaweed extract is added, so that the prepared seaweed polyester fiber has good moisture absorption and skin affinity, has lower boiling water shrinkage rate besides good moisture absorption, the boiling water shrinkage rate is lower than or equal to 0.5%, and the problem of technical prejudice is solved.

Description

technical field [0001] The invention relates to a seaweed polyester fiber and a preparation method thereof, belonging to the field of fiber technology. Background technique [0002] As one of the three main fibers in synthetic fibers, polyester is widely used in clothing fabrics and other non-clothing fields because of its excellent physical and chemical properties. Since its inception, polyester products have also been used by downstream users as the main textile raw material for weaving various textiles due to their good drapability, high strength and crispness. With the globalization of the economy and the internationalization of the market, people's requirements for clothing are getting higher and higher. Not only must they be comfortable, but they must also be functional. It is necessary to continuously improve performance to meet weaving requirements. The polyester industry in my country has developed rapidly. The output of polyester fiber has grown from 5.165 million ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D01F6/92D01F1/10
Inventor 黄效华甄丽刘洁
Owner ZHONGKE TEXTILE RES INST QINGDAO CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com