A new type of modified bitumen waterproof membrane and its preparation method

A technology for modifying asphalt and waterproofing membranes, applied in asphalt layered products, chemical instruments and methods, and roofing using flexible materials, etc. High, the effect of improving the scope of application and service life

Active Publication Date: 2021-06-22
包头市草原驼峰防水材料有限公司
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The present invention proposes a novel modified asphalt waterproofing membrane and its preparation method, which solves the problem of defects in the high and low temperature resistance of elastomer-modified asphalt and plastomer-modified asphalt waterproofing membranes in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A new type of modified bitumen waterproof membrane and its preparation method
  • A new type of modified bitumen waterproof membrane and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] A preparation method of a novel modified bitumen waterproof coiled material, comprising the following steps:

[0027] S1. According to the following formula by weight, take each component for later use: 5 parts of 10# asphalt, 40 parts of 90# asphalt, 6 parts of softening oil, 4 parts of rubber powder, 3 parts of SBS, 2 parts of high-density polyethylene, three parts 0.2 parts of allyl isocyanurate, 0.6 parts of dicumyl peroxide, 10 parts of light calcium;

[0028] S2. Pour 10# asphalt and 90# asphalt into the batching tank, add softened oil when the temperature rises to 160±5°C, raise the temperature to 180±5°C, and stir for 30 minutes until evenly mixed;

[0029] S3. Control the temperature at 180-190°C, then add tire rubber powder, stir for 60 minutes until evenly mixed, then open the colloid mill, and grind for the first time to completely blend the rubber powder and oil;

[0030] S4. After the first grinding is completed, add SBS, stir for 30 minutes until it is e...

Embodiment 2

[0035] A preparation method of a novel modified bitumen waterproof coiled material, comprising the following steps:

[0036] S1. According to the following formula by weight, take each component for later use: 6 parts of 10# asphalt, 43 parts of 90# asphalt, 8 parts of softening oil, 5 parts of rubber powder, 4 parts of SBS, 3 parts of high-density polyethylene, three parts 0.3 parts of allyl isocyanurate, 1.0 parts of dicumyl peroxide, 13 parts of light calcium;

[0037] S2. Pour 10# asphalt and 90# asphalt into the batching tank, add softened oil when the temperature rises to 160±5°C, raise the temperature to 180±5°C, and stir for 30 minutes until evenly mixed;

[0038] S3. Control the temperature at 180-190°C, then add tire rubber powder, stir for 60 minutes until evenly mixed, then open the colloid mill, and grind for the first time to completely blend the rubber powder and oil;

[0039] S4. After the first grinding is completed, add SBS, stir for 30 minutes until it is e...

Embodiment 3

[0044]A preparation method of a novel modified bitumen waterproof coiled material, comprising the following steps:

[0045] S1. According to the following formula by weight, take each component for later use: 7 parts of 10# asphalt, 45 parts of 90# asphalt, 9 parts of softening oil, 5 parts of rubber powder, 4 parts of SBS, 3 parts of high-density polyethylene, three parts 0.4 parts of allyl isocyanurate, 1.2 parts of dicumyl peroxide, 15 parts of fly ash;

[0046] S2. Put 10# asphalt, 90# or 100# asphalt into the batching tank, add softening oil when the temperature rises to 160±5°C, heat up to 180±5°C, stir for 30 minutes until the mixture is uniform;

[0047] S3. Control the temperature at 180-190°C, then add tire rubber powder, stir for 60 minutes until evenly mixed, then open the colloid mill, and grind for the first time to completely blend the rubber powder and oil;

[0048] S4. After the first grinding is completed, add SBS, stir for 30 minutes until it is evenly mixe...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
softening pointaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of building materials, and proposes a novel modified asphalt waterproof coiled material, which includes a modified asphalt coating layer, a base layer and an isolation layer. The material of the modified asphalt coating layer is modified asphalt, modified asphalt It consists of the following components by weight: 5-10 parts of 10# asphalt, 40-50 parts of 90# or 100# asphalt, 6-12 parts of softening oil, 4-6 parts of rubber powder, 3-5 parts of SBS, high density 2 to 4 parts of polyethylene, 0.2 to 0.6 parts of triallyl isocyanurate, 0.6 to 2 parts of dicumyl peroxide, and 10 to 20 parts of filler. Grinding and preparing modified asphalt, and then coating the modified asphalt on the upper and lower surfaces of the base layer to obtain a base layer coated with modified asphalt coating layers on both sides, and then coating an isolation film to obtain an isolation layer, cooling and forming, and obtaining A new type of modified bitumen waterproof membrane. The invention solves the problem of defects in the high and low temperature resistance of elastomer modified asphalt and plastic body modified asphalt waterproof coiled materials in the prior art.

Description

technical field [0001] The invention belongs to the technical field of building materials, and relates to a novel modified asphalt waterproof coiled material and a preparation method thereof. Background technique [0002] Waterproof membrane is a kind of building material commonly used in building construction. In the construction of roads, bridges, roofs, basements and other buildings that need waterproofing, waterproof membranes need to be pre-paved. According to its main waterproof composition, it can be divided into: asphalt Waterproof membrane, polymer waterproof membrane, synthetic polymer waterproof and coating waterproof four categories. Among them, modified asphalt waterproofing membrane is the most commonly used waterproofing membrane, accounting for nearly 70% of the total market. At present, domestic modified asphalt waterproofing membranes are divided into two types: one is elastomer modified asphalt waterproofing membranes; the other is plastic modified asphal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B32B11/10E04D5/10E04B1/66E02D31/02C08L95/00C08L91/00C08L21/00C08L53/02C08L23/06C08K5/14
Inventor 王军鹏邢帅刘凯邢畅
Owner 包头市草原驼峰防水材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap