An early-strength prefabricated component laminated plate and its processing method
A technology of prefabricated components and processing methods, which is applied in the direction of manufacturing tools and ceramic molding machines, etc., can solve the problems of restricting the development of prefabricated building components, the inability to quickly demould, and the low turnover rate of molds, so as to achieve good promotion significance and shorten demoulding The effect of simple mold time and processing method
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0043] An early-strength prefabricated composite panel is made of the following components in parts by weight: 200 parts of cement, 110 parts of secondary fly ash, 120 parts of mineral powder, 6 parts of water reducing agent, and 3 parts of calcium nitrate Parts, 4 parts of sodium silicate, 150 parts of water.
[0044] Wherein, the water reducer is prepared by the following method:
[0045] (A) Diatomaceous earth is pretreated and ball-milled with dihydrate gypsum, triethanolamine and water to obtain crystal nuclei for subsequent use;
[0046] (B) Add water and acrylamide to the reaction kettle, stir until they are all dissolved, add 20% aqueous hydrogen peroxide solution with a mass concentration and the crystal nuclei obtained in step (A), then add dropwise 20% aqueous acrylic acid solution with a mass concentration of 1 % mercaptopropionic acid aqueous solution and mass concentration of 20% ferrous sulfate aqueous solution, after the dropwise addition was completed, they w...
Embodiment 2
[0063] An early-strength prefabricated composite panel is made of the following components in parts by weight: 240 parts of cement, 130 parts of secondary fly ash, 140 parts of mineral powder, 9 parts of water reducing agent, and 5 parts of calcium nitrate Parts, 6 parts of sodium silicate, 180 parts of water.
[0064] Wherein, the water reducer is prepared by the following method:
[0065] (A) Diatomaceous earth is pretreated and ball-milled with dihydrate gypsum, triethanolamine and water to obtain crystal nuclei for subsequent use;
[0066] (B) Add water and acrylamide to the reaction kettle, stir until they are completely dissolved, add 30% aqueous hydrogen peroxide solution with a mass concentration and the crystal nuclei obtained in step (A), then add dropwise a 30% aqueous acrylic acid solution with a mass concentration of 2 % mercaptopropionic acid aqueous solution and mass concentration of 30% ferrous sulfate aqueous solution, after the dropwise addition was complete...
Embodiment 3
[0083] An early-strength prefabricated composite panel is made of the following components in parts by weight: 200 parts of cement, 130 parts of secondary fly ash, 120 parts of mineral powder, 9 parts of water reducing agent, and 3 parts of calcium nitrate Parts, 6 parts of sodium silicate, 150 parts of water.
[0084] Wherein, the water reducer is prepared by the following method:
[0085] (A) Diatomaceous earth is pretreated and ball-milled with dihydrate gypsum, triethanolamine and water to obtain crystal nuclei for subsequent use;
[0086] (B) Add water and acrylamide to the reaction kettle, stir until they are completely dissolved, add 30% hydrogen peroxide aqueous solution and the crystal nuclei obtained in step (A), then add dropwise 20% acrylic acid aqueous solution, 2 % mercaptopropionic acid aqueous solution and mass concentration of 20% ferrous sulfate aqueous solution, after the dropwise addition was completed, they were incubated at 45°C for 30 minutes;
[0087]...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com