Preparation method of matte antifouling dry granule glaze and glaze slurry, ceramic tile and preparation method

A technology of dry glaze and glaze slurry, which is applied in the field of ceramics, which can solve the problems of rough surface texture and low surface gloss, and achieve the effect of low gloss, good antifouling effect, and less glass phase

Active Publication Date: 2021-11-02
FOSHAN DONGPENG CERAMIC +2
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The above-mentioned antifouling technologies are intelligently applied to products with high gloss, but wood-like, stone-like and antique ceramic tiles require the surface gloss to be as low as possible, and some products require rough surface texture. The above-mentioned antifouling technology Difficult to apply to these ceramic tile products

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of matte antifouling dry granule glaze and glaze slurry, ceramic tile and preparation method
  • Preparation method of matte antifouling dry granule glaze and glaze slurry, ceramic tile and preparation method
  • Preparation method of matte antifouling dry granule glaze and glaze slurry, ceramic tile and preparation method

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0058] The above-mentioned matte preparation method of the mute anti-staining dry grain glaze, including the following steps:

[0059] (1), the raw material of the glaze A is added to the ball mill, and the hydroxymethylcellulose, sodium tripolyphosphate and water are mixed into the ball mill, and obtain the glazed pulp A;

[0060] (2), the raw material of the glaze B is added to the ball mill according to the ratio, and the hydroxymethylcellulose, sodium tripolyphosphate and water are mixed into the ball mill, and the glazed pulp B;

[0061] (3), the glaze pulp A and the glaze B b are mixed with a volume ratio 1: (3 ~ 4), and the glazed pulp is the glaze pulp of the matte anti-polluating glaze, prohibiting the grinding of the glazed pulp C.

[0062] (4) Mix the glazed pulp A and the high temperature melt block D, prohibit the grinding of the glaze pulp D. The glazed pulp D and the high temperature melt block weight ratio are 1: (5-7).

[0063] The antifouling dry particles matt g...

Embodiment

[0096] Group B antifouling dry granulation embodiment matt ceramic tiles

[0097] The antifouling dry particles matte tile Example B1-B6 comprises a brick layer are sequentially disposed from bottom to top, a first glaze layer and a second glaze layer, a first layer of enamel glaze slurry C prepared in Example A1-A6 one baked baked, the second fired glaze layer in Example D glaze slurry was prepared from one of A1-A6; tile gloss matte tile antifouling dry particles of 2 to 3 degrees , grainy sand tile there. The method for preparing an antifouling dry granulation matte tile follows:

[0098] (1) Preparation of bricks;

[0099] (2), applying the glaze pulse C to the surface of the brick, the grain is 500 ~ 670 g / m 2 ;

[0100] (3), the glaze pulse D is applied to the glazed pulp C of the brick, the grain is 224 ~ 300g / m 2 ;

[0101] (4), the brick billet of the glaze coating C will be branched, and the kiln is burned, the firing temperature is 1192 to 1205 ° C, and the fire is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
glossaaaaaaaaaa
glossaaaaaaaaaa
Login to View More

Abstract

The invention discloses a matte antifouling dry granular glaze, which comprises a glaze C for forming a first glaze layer and a glaze D for forming a second glaze layer, and the glaze C consists of glaze A and glaze B Combination, glaze D is made by mixing glaze A and high-temperature frit; the raw materials of glaze A make the glaze locally produce a liquid phase at 950-1050°C; glaze B uses barium carbonate, calcite and zirconia Regulates glass phase formation. Correspondingly, the invention also discloses a preparation method of the above-mentioned glaze material, a matte antifouling dry grain tile and a preparation method thereof. The matte antifouling dry grain ceramic tile of the present invention is an antique tile, and the surface glaze layer is composed of a first glaze layer formed by glaze material C and a second glaze layer formed by glaze material D, and the first glaze layer has low gloss and compactness Good characteristics, the second glaze layer has the characteristics of good compactness, so that the glaze layer of the antique brick glaze has the characteristics of low gloss and good antifouling performance as a whole, and the subsidence of the sandstone graininess of the glaze layer of the antique brick glaze can improve its antique effect .

Description

Technical field [0001] The present invention relates to the field of ceramic technologies, and more particularly to a matte anti-polluating dry grain glaze and a preparation method of glaze pulp, a tile and preparation method. Background technique [0002] As people's living standards have improved, the quality requirements of the product are getting higher and higher. Based on the current tile products epidemic imitation marble or wood effect, in order to pursue a more realistic effect and touch, the design of the tile product will be lowered, the surface texture is rough, the surface gloss of the tile product is low, rough Along with the anti-fouling problem. If the product is very poor, the user uses a period of time, the product surface will remain a lot of dirt, affecting the visual sense, the user experience is not good. [0003] The anti-fouling glaze tiles made in the market are now: (for example, China Patent ZL201710714237.X) is made of sodium longstone, quartz powder, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/00C03C8/14C04B41/89
CPCC03C8/00C03C8/14C04B41/52C04B41/89C04B41/4539
Inventor 祁明钟保民徐瑜
Owner FOSHAN DONGPENG CERAMIC