Household environment-friendly weather-resistant true stone-based light-weight coating and manufacturing method thereof

A manufacturing method and an environmentally friendly technology, applied in the field of decorative coatings, can solve the problems of slow drying, difficult to regular molding, low reflectivity, etc., and achieve the effects of good elasticity, high foaming stability, and high foaming temperature.

Inactive Publication Date: 2019-07-05
QINGDAO TIANDICAI PAINT
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The real stone-based coating in the prior art must be used with a curable emulsion. The real stone-based coating is very hard after drying and solid, and the nails cannot be picked, but the surface is rough and sharp, and it is easy to hurt the human body when used for interior decoration.
[0003] The coating of real stone coating in the prior art is relatively mature, and if it is used for interior decoration, there are still some technical difficulties: one is that the surface of the real stone-based coating in the prior art is hard and sharp, and when children are playing The real stone-based coating will even cause more damage than directly hitting the uncoated cement wall; second, the emulsion with strong adhesive ability often contains more harmful volatiles, which is not conducive to environmental protection and living. It is relatively inconspicuous, but it cannot be used indoors; third, the density of the paint is high but it dries slowly. Due to poor indoor ventilation, the refined stone-based paint is more likely to fall off or difficult to shape; fourth, it is easy to accumulate dust and is difficult to clean. The outer wall is good, but it is difficult to clean the interior after a long time of decoration; fifth, because the surface is rough, the reflectivity is low, the decorative effect is relatively poor, the application value is low, and the market promotion is difficult

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] A household environment-friendly weather-resistant real stone-based light coating, the household environmental protection weather-resistant real stone-based light coating consists of 11.8Kg by weight of physical foaming microcapsules, 19.2Kg of hydroxylated bamboo fiber, and 7.6 kg of polysaccharide colloid decomposed from high polysaccharides. Kg, Eastman C-12 film-forming aid 0.6Kg, starch 5Kg, activated carbon powder 5Kg, 500-800 mesh fine quartz sand 75Kg;

[0032] The manufacture method of above-mentioned composite lightweight real stone-based coating, comprises the following steps:

[0033] 1) Raw material preparation

[0034] ① Raw material preparation: Prepare 9Kg of acrylonitrile, 1.2Kg of methyl methacrylate, 0.2Kg of benzoyl peroxide, 0.2Kg of isooctane, 0.3Kg of magnesium hydroxide, 0.8Kg of glycidyl methacrylate, three 0.3Kg of hydroxymethyl propane trimethacrylate, 35Kg of dried jute bamboo, 8Kg of citrus fruit peel, 75Kg of quartz sand, 8Kg of wood chips...

Embodiment 2

[0056] The whole is consistent with Example 1, the difference is:

[0057] A household environment-friendly weather-resistant real stone-based light coating, the household environmental protection weather-resistant real stone-based light coating is composed of 8.3Kg of physical foaming microcapsules by weight, 15.6Kg of hydroxylated bamboo fiber, and 4.4 kg of polysaccharide colloid decomposed from high polysaccharides. Kg, Eastman C-12 film-forming aid 0.4Kg, starch 3Kg, activated carbon powder 3Kg, 500-800 mesh fine quartz sand 80Kg;

[0058] The manufacture method of above-mentioned composite lightweight genuine stone-based coating, comprises the following steps:

[0059] 1) Raw material preparation

[0060] ① Raw material preparation: Prepare 7Kg of acrylonitrile, 0.8Kg of methyl methacrylate, 0.1Kg of benzoyl peroxide, 0.1Kg of isooctane, 0.2Kg of magnesium hydroxide, 0.6Kg of glycidyl methacrylate, and three 0.2Kg of hydroxymethylpropane trimethacrylate, 30Kg of dried ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
particle diameteraaaaaaaaaa
lengthaaaaaaaaaa
Login to view more

Abstract

The invention discloses a household environment-friendly weather-resistant true stone-based light-weight coating and a manufacturing method thereof. The household environment-friendly weather-resistant true stone-based light-weight coating is composed of, in parts by weight, 8-12 parts of physically-foamed microcapsules, 15-20 parts of hydroxylation bamboo fiber, 4-8 parts of polysaccharide gum resolved from polysaccharide, 0.4-0.6 part of an Eastman C-12 film-forming aid, 3-5 parts of starch, 3-5 parts of activated carbon powder and 75-80 parts of fine quartz sand of 500-800 meshes. The coating has the characteristics of soft and elastic surfaces, prevention of injury to the human body, environmental protection, light weight, large binding force, good true stone texture, self cleaning anda high aqueous reflective index.

Description

technical field [0001] The invention relates to the technical field of decorative coatings, in particular to a household environment-friendly weather-resistant real stone-based lightweight coating and a manufacturing method thereof. Background technique [0002] The real stone-based coating in the prior art generally refers to a coating with a stone-like effect applied to the exterior wall of a building, so it is also called liquid stone. The real stone-based coating in the prior art must be used with a curable emulsion. The real stone-based coating is very hard after drying and solid, and the nails cannot be picked, but the surface is rough and sharp, and it is easy to hurt the human body when used for interior decoration. . [0003] The coating of real stone coating in the prior art is relatively mature, and if it is used for interior decoration, there are still some technical difficulties: one is that the surface of the real stone-based coating in the prior art is hard a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B38/10C04B26/28
CPCC04B26/28C04B2111/00482C04B2111/40C04B24/045C04B24/125C04B24/00C04B22/066C04B22/08C04B18/265C04B18/26C04B18/24C04B14/022C04B14/06C04B2103/0068C04B24/008C04B22/062C04B22/124C04B24/14C04B38/10
Inventor 刘凯旋刘英武刘丰毓
Owner QINGDAO TIANDICAI PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products