Brush-shaped block polymer and synthesis method and application thereof

A synthesis method and block copolymer technology are applied in the field of preparation of brush-shaped block copolymers, which can solve the problems of difficulty in preparing a wide range of photonic crystal materials and complicated processes, and achieve obvious temperature responsiveness and great practical value. Effect

Active Publication Date: 2019-07-16
TIANJIN UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the photonic crystal materials prepared by this method have obvious temperature-responsive behavior, the process is complicated and it is difficult to prepare a wide range of photonic crystal materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Brush-shaped block polymer and synthesis method and application thereof
  • Brush-shaped block polymer and synthesis method and application thereof
  • Brush-shaped block polymer and synthesis method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] The preparation method of brush block copolymer BCP1-6: its preparation route is as follows figure 1 as shown,

[0039] The general structural formula of BCP1-6 is:

[0040]

[0041] The synthesis steps of BCP1 (m=200, n=200) are as follows:

[0042] Add NBPM (57.6mg, 91.2μmol) to 10mL polymerization bottle, 1mL dry dichloromethane, add G-3 (0.41mg, 0.46×10 -3 mmol) in dichloromethane solution 0.1mL, stirred and reacted at room temperature for 30 minutes, then added 1.1mL of dichloromethane solution containing NDM (72.2mg, 91.2μmol) into the above reaction solution to continue the reaction for 1 hour, the entire addition Both reactions were carried out in a glove box. After the reaction was complete, 1 mL of vinyl ether was added to quench the reaction. Remove the glove box, precipitate in anhydrous methanol, centrifuge, and vacuum dry to obtain the brush-like block copolymer BCP1 with a main chain polymerization degree of 400, wherein the polymerization degree o...

Embodiment 2

[0055] Solvent volatilization self-assembly and heat treatment conditions of the synthesized series of brush-like block copolymers (BCP1-BCP6):

[0056] The synthesized brush-like block copolymers (BCP1-BCP6) were respectively prepared with 10 mg / mL tetrahydrofuran solution, and the mixed solution was applied drop by drop on a clean horizontal glass slide, and six different polymer films were obtained after the solvent evaporated completely. , which is the one-dimensional photonic crystal material. Then the prepared one-dimensional photonic crystal thin film was heat-treated at 130°C for 30 minutes to study its temperature-sensitivity characteristics. like figure 2 Shown are the self-assembly pictures of BCP1-BCP6 before and after heat treatment, showing obvious light reflection phenomenon and obvious temperature-sensitive behavior. The self-assembly of BCP1 was dark purple before heating and blue after heating; the self-assembly of BCP2 was blue before heating and bright g...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a brush-shaped block polymer and a synthesis method and application thereof. The synthesis method of the brush-shaped block copolymer comprises the following steps: dissolvinga norbornene monomer NBPM with a biphenyl structure into an organic solvent, adding a G-3 catalyst, performing a stirring reaction at 20-40 DEG C to homo-polymerize the monomer NBPM, then adding a dissolved norbornene monomer NDM with a decyl structure into the above reaction solution and performing continuous reaction to realize the copolymerization of NBPM and NDM, and adding a terminator to quench the reaction after the reaction is finished to obtain the target brush-shaped block copolymer PNBPM-b-PNDM. The block copolymer makes photonic crystal materials can be applied to light sensors, light valves, pigments, dyes and other aspects, and has great practical value.

Description

technical field [0001] The invention relates to the technical field of preparation of brush-like block copolymers, in particular to a brush-like block polymer and its synthesis method and application. Background technique [0002] Due to the existence of the internal photonic bandgap structure, photonic crystals can regulate the propagation of light waves, so that they have great application value, such as making special pigments, waveguides and reflective coatings, etc. Responsive photonic crystals are a class of materials whose reflection wavelength can change with changes in external physical or chemical conditions. In addition to the periodic structure necessary for traditional photonic crystals, this material must also have responsive groups. There are two common ways to introduce responsive groups: (1) Use responsive materials as substrates to directly construct photonic crystal structures, such as using block polymer self-assembly to prepare one-dimensional photonic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F293/00C08F232/08
CPCC08F293/005C08F232/08
Inventor 任丽霞张同周袁晓燕
Owner TIANJIN UNIV