Bamboo-wood combined building die plate and grinding technology thereof

Abstract

The invention discloses a bamboo-wood combined building die plate and a grinding technology thereof. The bamboo-wood combined building die plate is characterized in that poplar, megaphanerophyte, bamboo-wood fiber powder, calcium carbonate, plastic resin, a polymer nano-fusion agent, melamine resin glue and dynea brown film are treated as the raw materials and subjected to a series of processes including the processes of mixing and storing, extruding and forming, drying and cutting, gluing and splicing, pressing and processing, grinding, film paving and thermal pressing, and grooving and edgesealing; the building die plate can be further processed; a semi-finished fiber plate is added into the building die plate, so that the building die plate with the semi-finished fiber plate is moisture-proof; in addition, megaphanerophyte is treated as the raw material in the building die plate, and thus the building die plate is good in bearing effect after being mounted in a building; and moreover, the building die plate is subjected to secondary gluing and pressing, so that clearances in an existing building die plate can be decreased; in addition, the strength of the bamboo-wood combined building die plate can be improved; and the bamboo-wood combined building die is wide in practicable scope in the technical field of processing and preparation of building die plates.

Description

technical field [0001] The invention relates to the technical field of bamboo and wood production, in particular, the invention relates to the technical field of a bamboo and wood composite building formwork preparation process. [0002] technical background [0003] Bamboo wood is made of bamboo, which is processed by peeling, cooking, gluing, hot pressing and other processes to produce industrial bamboo plywood, or bamboo flooring for decoration. The building formwork is a temporary support structure. Bamboo-wood composite buildings The formwork is a building formwork made of bamboo and wood through a series of processes. It is usually used in the construction field. The bamboo-wood composite building formwork is a kind of wood-based panel. The slab is pressed under heating or without heating. The number of layers is generally odd, and a few are even. The difference in physical and mechanical properties in the vertical and horizontal directions is small. Commonly used are t...

AI Technical Summary

Problems solved by technology

[0005] Aiming at the technical status quo at home and abroad about the poor moisture-proof effect, poor load-bearing effect and poor sealing performance of the bamboo-wood composite building formwork at home and abroad, the present invention aims to provide a bamboo-wood composite building formwork and its polishing process. Arbor, bamboo and wood fiber powder, calcium carbonate, plastic resin, polymer nano-fusion agent, melamine glue and Taier palm film are used as raw materials, which are mixed and stirred, extruded, dried and cut, glued, pressed, polished, A series of process steps such as film laying, hot pressing and slotting and edge sealing make it possible to further process the building formwork, adding bamboo and wood fiber powder, calcium carbonate, plastic resin and polymer nano-fusion agent to the inside of the building formwork and stirring for 45 minutes. And the semi-finished fiberboard made by extruding inside the high-pressure boiler at 210°C can make the building formwork moisture-proof through the semi-finished fiberboard, and use a dryer inside the building formwork at a temperature of 75°C and bake it for 55 hours. The big arbor is used as a raw material , so that the hardness of the building formwork can be increased to 0.75g / cm through the large arbor 3 , so that the load-bearing effect of this kind of building formwork is better after it is installed inside the building, and through the secondary glue coating and pressing of the building formwork, it can reduce the internal gaps of the existing building formwork and increase the strength of the bamboo-wood composite building formwork. It has wide applicability in the technical field of building formwork processing and preparation