Hot pressing process for environmental-protection oriented particle boards

A technology of oriented strand board and hot pressing process, which is applied in the field of sheet material manufacturing, can solve the problems of unstable quality of oriented strand board, high formaldehyde content of oriented strand board, easy sticking of slab to steel belt, etc., and achieve low scrap rate and high press speed Fast, high-efficiency heat-pressing effect

Active Publication Date: 2019-08-09
寿光市鲁丽木业股份有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] (1) In the existing hot-pressing process, the slab is easy to stick to the steel belt during hot-pressing, resulting in downtime for maintenance, low speed of the press, and reduced yield of slabs;
[0006] (2) The quality of oriented strand board prepared by the existing hot pressing process is unstable, prone to bubbling and delamination, and the scrap rate is high;
[0007] (3) The oriented strand board prepared by the existing hot pressing process has a high formaldehyde content

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Hot pressing process for environmental-protection oriented particle boards
  • Hot pressing process for environmental-protection oriented particle boards
  • Hot pressing process for environmental-protection oriented particle boards

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0023] Embodiment A kind of heat-pressing process of environment-friendly type oriented strand board

[0024] The invention provides a hot-pressing process for environment-friendly oriented strand board, which includes pre-pressing, water spraying, roller coating of release agent, and hot pressing;

[0025] (1) Preload:

[0026] The lower surface slab, the core layer slab and the upper surface slab are respectively pre-pressed by the rubber roller's own weight, and pre-pressed several times;

[0027] When paving the upper fine material layer slab, use the pre-pressing machine to pre-press the lower fine material layer slab, lower surface layer slab, core layer slab, upper surface layer slab and upper fine material layer slab five-layer slab , The pressure of the pre-compressor is 1.5MPa.

[0028] (2) Water spray:

[0029] The pre-pressed slab is sprayed with water to increase the moisture content of the upper and lower surfaces of the slab;

[0030] The amount of water spr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention provides a hot pressing process for environmental-protection oriented particle boards. The hot pressing process comprises the steps of prepressing, water spraying, roller coating of demolding agents and hot pressing; in hot pressing, the speed of a press is 250-350 mm/s; the temperatures of pressing plates of the press are 240-245 DEG C, 230-240 DEG C, 215-225 DEG C, 175-185 DEG C and 155-165 DEG C; in prepressing, the pressure is 1.5 MPa; in water spraying, the water spraying quantity is 30-40 g/m2; after water spraying, the water content of surface layers of slabs is 8-12%, thewater content of core layers of slabs is 4-5%, and the water content of fine material layers of slabs is 12-18%; and in roller coating of the demolding agents, the spraying quantity of the demoldingagents is 15-20 g/m2. The hot pressing process improves the spraying uniformity, saves the use level of the demolding agents, and achieves higher environmental protection; the thickness deviation of aplain plates obtained by hot pressing is low; and the deviation is within -0.3-0 mm.

Description

technical field [0001] The invention belongs to the technical field of plate manufacturing, and relates to a hot-pressing process, in particular to a hot-pressing process for an environment-friendly oriented particle board. Background technique [0002] With the recovery of the economy in Asia, the consumption of wood products is on the rise. The development of western China, the rise of urban agglomerations in the Central Plains, the promotion of small town construction in coastal provinces of China, the implementation of the Three Gorges Project and the South-to-North Water Diversion, and the expansion of higher education , a large number of agricultural population will be stationed in cities and towns, the construction industry will develop extremely fast, and the consumption of wood products such as furniture and floors will rise rapidly. In particular, the development of China's rural economy and the increasing affluence of farmers have also led to a linear increase in ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B27N3/10B27N3/18
CPCB27N3/10B27N3/18
Inventor 薛茂林钟笃章国智武葛立军郑凤山
Owner 寿光市鲁丽木业股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap