Anti-oxidization film and preparation method

An anti-oxidation and thin-film technology, applied in liquid chemical plating, metal material coating process, coating and other directions, can solve the loss of silver protection, the unsatisfactory weather resistance of anti-silver discoloration agent, and the aging degradation of protective film. and other problems, to achieve the effect of improving antioxidant capacity, strong antioxidant capacity and good film-forming performance

Active Publication Date: 2019-09-17
CHENZHOU CITY JINGUI SILVER IND CO LTD
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the weather resistance of this anti-silver discoloration agent is still unsatisfactory, and the protective film formed by it still undergoes aging and degradation behavior under the joint action of light, water vapor and air, and loses its protective effect on silver parts.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Anti-oxidization film and preparation method
  • Anti-oxidization film and preparation method
  • Anti-oxidization film and preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Inorganic nano film of the present invention, SiO 2 , B 2 o 3 , ZnO and K 2 The weight ratio of O is 45:10:15:30.

[0027] Its specific preparation process includes the following steps:

[0028] 1) Preparation of precursor solution: weigh 20g TESO (tetraethyl orthosilicate), 200g H 2 O and 40g polyethylene glycol, after mixing uniformly in a 500ml beaker, adjust PH=9 with ammonia water, stir at room temperature for 12h, slowly add 0.97g (CH 3 O) 3 B, 0.57g Na 2 [Zn(OH) 4 ] and 1 g K 2 O, after the stirring is completed, a transparent sol-like solution is obtained, which is the precursor.

[0029] 2) Preparation of anti-oxidation silver: immerse pure silver in the precursor solution, coat with a pull coater, dry naturally, and perform heat treatment according to the following heating procedure:

[0030]

[0031] After the heat treatment, the anti-oxidation silver is obtained. The anti-oxidation silver will not be corroded and discolored in the atmosphere, sw...

Embodiment 2

[0033] Inorganic nano film of the present invention, SiO 2 , B 2 o 3 , ZnO and K 2 The weight ratio of O is 50:10:10:30.

[0034] Its specific preparation process includes the following steps:

[0035] 1) Preparation of precursor solution: weigh 100g TESO, 1000g H 2 O and 200g polyethylene glycol, after mixing uniformly in a 2500ml beaker, adjust PH=9 with ammonia water, stir at room temperature for 12h, slowly add 4.5g (CH 3 O) 3 B, 1.74gNa 2 [Zn(OH) 4 ] and 5g K 2 O, after the stirring is completed, a transparent sol-like solution is obtained, which is the precursor.

[0036] 2) Preparation of anti-oxidation silver: immerse pure silver in the precursor solution, coat with a pull coater, dry naturally, and perform heat treatment according to the following heating procedure:

[0037]

[0038] After the heat treatment, the anti-oxidation silver is obtained. The anti-oxidation silver will not be corroded and discolored in the atmosphere, sweat, hydrogen sulfide atmo...

Embodiment 3

[0040] Inorganic nano film of the present invention, SiO 2 , B 2 o 3 , ZnO and K 2 The weight ratio of O is 60:5:15:20.

[0041] Its specific preparation process includes the following steps:

[0042] 1) Preparation of precursor solution: weigh 200g TESO, 2000g H 2 O and 400g polyethylene glycol, after mixing uniformly in a 5000ml beaker, adjust PH=9 with ammonia water, stir at room temperature for 12h, slowly add 3.7g (CH 3 O) 3 B, 4.2gNa 2 [Zn(OH) 4 ] and 4.9 g K 2 O, after the stirring is completed, a transparent sol-like solution is obtained, which is the precursor.

[0043] 2) Preparation of anti-oxidation silver: immerse pure silver in the precursor solution, coat with a pull coater, dry naturally, and perform heat treatment according to the following heating procedure:

[0044]

[0045] After the heat treatment, the anti-oxidation silver is obtained. The anti-oxidation silver will not be corroded and discolored in the atmosphere, sweat, hydrogen sulfide atm...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to an anti-oxidization material, and particularly to an anti-oxidization film and a preparation method. The anti-oxidization film comprises, by weight, 45-60 parts of silicon dioxide, 5-10 parts of boric oxide, 5-15 parts of zinc oxide and 20-30 parts of potassium oxide. The film is in a nanoscale and is compact, transparent, uniform and continuous, oxidization resistance, high temperature resistance and weather fastness are good, and the problem that a carrier material is prone to being oxidized and discolored is effectively solved.

Description

technical field [0001] The invention belongs to an anti-oxidation material, and in particular relates to an anti-oxidation film and a preparation method. Background technique [0002] Sterling silver is a beautiful silvery-white metal with attractive metallic luster and collection value. It is favored by people, so it has the reputation of women's metal and is widely used as jewelry, decorations, silverware, tableware, congratulations Gifts, medals and coins. There are mainly three grades of silver for traditional decoration: sterling silver, 958 silver and 925 silver, among which 958 silver and 925 silver are binary alloys composed of copper as an alloying element. No matter what brand of silver it is, there is a problem of easy discoloration. In the atmospheric atmosphere, the surface of the jewelry will lose its white luster after a period of time and turn yellow and black, which seriously affects the ornamental effect of the jewelry. [0003] In order to improve the an...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C18/12
CPCC23C18/1208C23C18/1241C23C18/1291
Inventor 代林涛李贵覃小龙陈兰谭霖
Owner CHENZHOU CITY JINGUI SILVER IND CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products