Epoxy floor coating and preparation method thereof

An epoxy floor and coating technology, applied in epoxy resin coatings, coatings, etc., can solve the problems of limited application, difficult to disperse, easy to agglomerate, etc., and achieve the effect of improving mechanical properties

Inactive Publication Date: 2019-10-01
江苏道蓬科技有限公司
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high specific surface area of ​​graphene, there is van der Waals force between layers of graphene materials, so it is easy to agglomerate; in practical applications, graphene materials need to be dispersed in the medium, but graphene materials are hydrophobic and oleophobic, and easily Agglomeration, making it difficult to disperse in various media, greatly limiting its application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] As another embodiment of the present invention, the preparation method of above-mentioned embodiment epoxy floor paint is shown, comprises the following steps:

[0036] Dispersing graphene microflakes and zinc powder in xylene to obtain dispersion system A;

[0037] Add dibutyl phthalate to the dispersion A while stirring to form a uniform dispersion system B;

[0038] The homogeneous dispersion system B adopts the method of distillation to separate xylene, obtains the mixture C that Zn and dibutyl phthalate are bonded between graphene layers;

[0039] Mix mixture C with 10-12 parts of bisphenol A epoxy resin solution to obtain mixed system D;

[0040] Polyamide wax slurry is dissolved in n-butyl alcohol, and remaining bisphenol A type epoxy resin and polydimethylsiloxane are added to obtain mixed solution E; and

[0041] Fully mix the mixed system D and the mixed solution E to obtain the main ingredient.

[0042]When performing the step of dispersing the graphene mi...

Embodiment 1

[0050] This embodiment shows a kind of preparation technology of epoxy floor paint, specifically comprises the following steps:

[0051] Step 1): Prepare the following raw material components, in parts by weight:

[0052] 100 parts of bisphenol A type epoxy resin solution

[0053] Graphene microflakes 10 parts

[0054] Zinc powder 2 parts

[0055] 0.5 parts of polyamide wax slurry

[0056] 3 parts n-butanol

[0057] 25 parts xylene

[0058] 0.08 parts of dibutyl phthalate

[0059] 0.1 parts of polydimethylsiloxane

[0060] Step 2): Disperse the graphene microflakes and zinc powder in xylene, stir with a disperser, the speed of the disperser is 1000rpm, and the stirring time is 50min, and the dispersion liquid system A is obtained.

[0061] Step 3): Add dibutyl phthalate to the dispersion A while stirring with a disperser, the speed of the disperser is 500rpm, and the stirring time is 2.5h to form a uniform dispersion system B.

[0062] Step 4): The homogeneous dispersi...

Embodiment 2

[0067] This embodiment shows a kind of preparation technology of epoxy floor paint, specifically comprises the following steps:

[0068] Step 1): Prepare the following raw material components, in parts by weight:

[0069] 100 parts of bisphenol A type epoxy resin solution

[0070] Graphene microflakes 15 parts

[0071] 6 parts zinc powder

[0072] 1 part polyamide wax paste

[0073] 8 parts of n-butanol

[0074] 60 parts xylene

[0075] 0.2 parts of dibutyl phthalate

[0076] 0.2 parts of polydimethylsiloxane

[0077] Step 2): Disperse the graphene microflakes and zinc powder in xylene, stir with a disperser, the speed of the disperser is 2000rpm, and the stirring time is 10min, and the dispersion liquid system A is obtained.

[0078] Step 3): Add dibutyl phthalate to the dispersion A while stirring with a disperser, the speed of the disperser is 1500rpm, and the stirring time is 1.5h to form a uniform dispersion system B.

[0079] Step 4): The homogeneous dispersion s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides an epoxy floor coating, which comprises the following raw materials in parts by weight: 100 parts of a bisphenol A epoxy resin solution, 10-15 parts of a graphene microchip, 2-6parts of zinc powder, 0.5-1 part of polyamide wax slurry, 3-8 parts of n-butanol, 25-60 parts of xylene, 0.08-0.2 part of dibutyl phthalate and 0.1-0.2 part of polydimethylsiloxane. The graphene of the epoxy floor coating is uniformly dispersed and highly dispersed, so that the mechanical property of the graphene is brought into play, the impact resistance of the epoxy floor coating is effectively improved, the problem of electrical corrosion of the graphene is avoided, and the service life of the floor coating layer is effectively prolonged.

Description

technical field [0001] The invention belongs to the field of epoxy coatings, and relates to a formula and a preparation method of epoxy floor coatings. Background technique [0002] Floor coatings are ground decoration materials that use epoxy resin raw materials as the main agent, adding pigments, solvents, and auxiliary curing agents. The research and production of epoxy oily floor paints all become floor coatings. Since the epoxy floor coating entered the Chinese market in the late 1980s, it has shown advantages that other types of coatings cannot achieve due to its excellent adhesion, mechanical strength and anti-corrosion performance, so it has won the welcome of the majority of users. with recognition. Epoxy floor coatings are one of the fastest growing areas of epoxy resin application technology in recent years. The modern industrial environment has various requirements for floor coatings (materials). For example, electronics, food, medicine and other industrial fie...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/00C09D7/61C09D7/63C09D7/65
CPCC08K2003/0893C08L2205/03C09D7/61C09D7/63C09D7/65C09D7/70C09D163/00C08L83/04C08L77/00C08K13/04C08K7/00C08K3/04C08K3/08C08K5/12
Inventor 周海燕宋建新
Owner 江苏道蓬科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap