A low-sensitivity wet-mix mortar plasticizer and preparation method thereof

A wet-mixed mortar and plasticizer technology, applied in the field of construction admixtures, can solve the problems of insufficient plasticizer water retention rate and plasticity retention ability for long-term stability, and achieve enhanced steric hindrance effects, reduced sensitivity, and good retention plastic effect

Active Publication Date: 2022-04-22
KZJ NEW MATERIALS GROUP CO LTD
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The existing wet-mix mortar additives use plasticizers, but the existing plasticizers are insufficient in terms of water retention, plasticity retention and long-term stability

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A low-sensitivity wet-mix mortar plasticizer and preparation method thereof
  • A low-sensitivity wet-mix mortar plasticizer and preparation method thereof
  • A low-sensitivity wet-mix mortar plasticizer and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] (1) The first esterification reaction: add 50g of 2-amino-3-p-hydroxyphenylpropionic acid and 50g of butenol into the reaction vessel, heat up to 80°C, then add 1g of aluminum sulfate octahydrate, and react After 3 hours, excess butenol was removed by reflux to obtain butenyl 2-amino-3-p-hydroxyphenylpropionate.

[0030] (2) The second esterification reaction:

[0031] Add 100g of 3-hydroxyphenylphosphonopropionic acid and cyclohexane into the reaction kettle, then add 100g of dihydromyrcenol, add 732 cation exchange resin and hydroquinone at the same time, stir evenly, and then raise the temperature to 30°C, react for 2 hours, filter and distill at atmospheric pressure to get 3-hydroxyphenyl phosphatopropionate dihydromyrcenyl;

[0032] Wherein, the dosage of 732 cation exchange resin is 0.5% of the mass of 3-hydroxyphenylphosphorylpropionic acid, the dosage of hydroquinone is 0.5% of the mass of 3-hydroxyphenylphosphorylpropionic acid, and the atmospheric distillatio...

Embodiment 2

[0036] (1) The first esterification reaction: 50g of 2-amino-3-p-hydroxyphenylpropionic acid and 100g of propylene alcohol were added to the reaction vessel, the temperature was raised to 90°C, and then 1g of ferric ammonium sulfate dodecahydrate was added, After reacting for 3 hours, excess propenol was removed by reflux to obtain 2-amino-3-propenyl p-hydroxyphenylpropionate.

[0037] (2) The second esterification reaction:

[0038] Add 100g of 3-hydroxyphenylphosphonopropionic acid and cyclohexane into the reactor, then add 200g of dihydromyrcenol, add 732 cation exchange resin and hydroquinone at the same time, stir evenly, and then raise the temperature to 50°C, react for 3 hours, filter and distill at atmospheric pressure to get 3-hydroxyphenyl phosphatopropionate dihydromyrcenyl;

[0039] Wherein, the dosage of 732 cation exchange resin is 1% of the mass of 3-hydroxyphenylphosphorylpropionic acid, the dosage of hydroquinone is 0.5% of the mass of 3-hydroxyphenylphosphor...

Embodiment 3

[0043] (1) The first esterification reaction: Add 50g of 2-amino-3-p-hydroxyphenylpropionic acid and 150g of prenyl alcohol into the reaction vessel, raise the temperature to 120°C, and then add 2g of sodium bisulfate monohydrate , reacted for 4 hours, and refluxed to remove excess prenyl alcohol to obtain prenyl 2-amino-3-p-hydroxyphenylpropionate.

[0044] (2) The second esterification reaction:

[0045] Add 100g of 3-hydroxyphenylphosphonopropionic acid and cyclohexane into the reactor, then add 250g of dihydromyrcenol, add 732 cation exchange resin and hydroquinone at the same time, stir evenly, and then raise the temperature to 60°C, react for 3 hours, filter and distill under normal pressure to get 3-hydroxyphenyl phosphatopropionate dihydromyrcenyl;

[0046] Wherein, the dosage of 732 cation exchange resin is 1.5% of the mass of 3-hydroxyphenylphosphorylpropionic acid, the dosage of hydroquinone is 1% of the mass of 3-hydroxyphenylphosphorylpropionic acid, and the atmo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of building admixtures, in particular to a low-sensitivity wet-mixed mortar plasticizer and a preparation method thereof. The preparation method comprises the following steps: adding 4-hydroxybutyl vinyl polyoxyethylene ether monomer to react In the kettle, after warming up to 20~30 ℃, the aqueous solution A of oxidizing agent is added successively; Mixed solution B composed of dihydromyrcenol propionate; solution C composed of reducing agent and chain transfer agent; after mixing reaction, continue to add 30% sodium hydroxide solution to adjust to pH=7~8, namely The wet mix mortar plasticizer is obtained. Compared with the prior art, the mortar synthesized by using the low-sensitivity wet-mixed mortar plasticizer provided by the invention has the advantages of low consistency loss, good water retention, high compressive strength and long-term stability of mortar, and has the advantages of Significant progress.

Description

technical field [0001] The invention relates to the technical field of building admixtures, in particular to a low-sensitivity wet-mix mortar plasticizer and a preparation method thereof. Background technique [0002] With the acceleration of the development of new urbanization in China, the number of urban municipal infrastructure and residential buildings will increase significantly, and building energy consumption has already accounted for a considerable part of the overall energy consumption. As a bulk building material second only to wall materials and concrete, building mortar is used in hundreds of millions of tons every year. Wet-mixed mortar will gradually replace the traditional on-site preparation mortar with its advantages of stable quality, energy saving and environmental protection, and centralized clean production; wet-mixed mortar is an inevitable result of industry development with its characteristics of energy saving, environmental protection, and sustainab...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08F283/06C08F220/06C08F230/08C08F230/02C08F218/12C08F4/40C04B24/24C04B103/30
CPCC08F283/065C08F4/40C04B24/246C04B2103/30C08F220/06C08F230/08C08F230/02
Inventor 林添兴柯余良方云辉张小芳钟丽娜桂苗苗郭元强朱少宏
Owner KZJ NEW MATERIALS GROUP CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com