Method for measuring sulphur content in witherite

A technology for sulfur content and witherite, applied in measuring devices, color/spectral characteristic measurement, sampling, etc., can solve the problems of difficult replacement of standard samples and no national standard samples for witherite, and achieve reliable technical support, easy operation, and solution Measuring the effect of puzzles

Inactive Publication Date: 2019-10-18
WUKUN STEEL
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Witherite is in a powder state, so how to choose a suitable fluxing material to ensure the complete release of sulfur is particularly important. How to determine the working co

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] 1. The spare parts used in the measurement process are as follows:

[0031] 1.1 Barium carbonate: benchmark pure;

[0032] 1.2 Standard substance Prepare standard substance with blast furnace slag and reference barium carbonate in a weight ratio of 7+3 as follows:

[0033] The first standard material: blast furnace slag YSBC28851-98, the sulfur content is 1.03%, and the sulfur content after preparation is 0.72%;

[0034] The second standard substance: blast furnace slag BH191-1, the sulfur content is 0.55%, and the sulfur content after preparation is 0.39%;

[0035] The third reference material: blast furnace slag BH191-2, the sulfur content is 1.56%, and the sulfur content after preparation is 1.09%;

[0036] 1.3 Porcelain crucible: PT type ￠25mm×25mm;

[0037] 1.4 High-purity tungsten particle flux: C: <0.0008%, S: <0.0005%;

[0038] 1.5 Ultra-low sulfur blank value pure iron flux: C: <0.0005%, S: <0.0005%;

[0039] The instrument used in the determination proces...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for measuring a sulphur content in witherite. The method is used for measuring the sulfur content by using a high-frequency infrared carbon and sulfur analyzer and a high-frequency induction combustion-infrared absorption method, and specifically comprises the following steps: preparing a reserve part for measurement, measuring a sulphur content blank value, calibrating the high-frequency infrared carbon and sulfur analyzer, sampling, and preparing a sample, preparing a test material, and measuring the sulphur content in a witherite powder sample to be tested.The working conditions of the instrument are as follows: the measurement flow rate is 3+/-0.5 L/min, the oxygen pressure is 0.2-0.4 MPa, the power barometric pressure is 0.2-0.4 MPa, and the minimum analysis time is 60 s. The method has the advantages of having good reproducibility and accuracy of measurement result, solving the problem of measuring the sulfur content in the witherite, and providing a reliable technical guarantee for steel smelting quality control.

Description

technical field [0001] The invention belongs to the technical field of element quantitative analysis, and in particular relates to a method for determining the content of sulfur in witherite. Background technique [0002] In converter steelmaking, dephosphorization is one of the main tasks in the steelmaking process. Although phosphorus can increase the strength of steel, with the increase of phosphorus content, the plasticity and toughness of steel decrease, making steel "cold brittle". Activated lime is widely used as dephosphorization agent. With the continuous exploration of new technologies and new materials, some manufacturers have explored the use of witherite in active lime as a dephosphorization agent for steelmaking. The main component of witherite is barium carbonate, which decomposes into barium oxide at 1297°C. Barium oxide is an effective basic oxide to increase the alkalinity of the slag system, and high alkalinity is a favorable condition for dephosphorizati...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N21/3563G01N21/27
CPCG01N21/3563G01N21/274G01N2001/2893
Inventor 李文生王磊曾海梅许涯平
Owner WUKUN STEEL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap