Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of manual argon arc welding and welding wire steel, which is applied in the field of metallurgy, can solve problems such as increasing product costs, and achieve the effects of ensuring performance, meeting welding requirements, and stable quality
Active Publication Date: 2019-10-29
TANGSHAN NORMAL UNIV +1
View PDF14 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
[0003] However, according to statistics, currently in the welding consumables market, most of the welding 690MPa low-alloy high-strength steels use the Mn-Ni-Mo alloy system. Since Ni is a precious metal, adding too much will inevitably increase the product cost
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0028] Welding wire steel for manual argon arc welding, the mass percentage composition is: C is 0.03%, Mn is 1.15%, Si is 0.80%, S is 0.005%, P is 0.010%, Cr is 0.25%, Mo is 0.25%, Ni is 0.15%, Microalloy: 0.015% Ti, 0.025% Nb, 0.010% Zr, 97.305% Fe and unavoidable impurity elements.
Embodiment 2
[0030] Welding wire steel for manual argon arc welding, the mass percentage composition is: C is 0.06%, Mn is 1.50%, Si is 0.70%, S is 0.010%, P is 0.020%, Cr is 0.10%, Mo is 0.20%, Ni is 0.20%, Microalloy: 0.010% for Ti, 0.020% for Nb, 0.010% for Zr, 97.170% for Fe and unavoidable impurity elements.
Embodiment 3
[0032]Welding wire steel for manual argon arc welding, the mass percentage composition is: C is 0.04%, Mn is 0.80%, Si is 0.70%, S is 0.005%, P is 0.015%, Cr is 0.05%, Mo is 0.10%, Ni is 0.10%, microalloying: Ti is 0.005%, Nb is 0.010%, Zr is 0.010%, Fe and unavoidable impurity elements are 98.165%.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
tensile strength
aaaaa
aaaaa
yield strength
aaaaa
aaaaa
impact absorption energy
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses welding wire steel for manual argon arc welding. The welding wire steel comprises, by mass, 0.0001%-0.08% of C, 0.80%-1.50% of Mn, 0.70%-0.95% of Si, 0.0001%-0.010% of S, 0.0001%-0.020% of P, 0.0001%-0.40% of Cr, 0.10-0.30% of Mo, 0.0001%-0.40% of Ni, and the balance Fe and inevitable impurity elements. The welding wire steel is low in cost, high in welding seam strength and toughness, stable in quality and good in welding performance, and can meet the use requirements of welding wire manufacturers. According to the welding wire steel, the welding performance of the low-alloy high-strength welding wire is improved in a limited mode while the high-strength of weld metal is ensured, the occurrence of cold cracks is controlled, the splashing rate is small, and the welding requirements of the low-alloy high-strength steel are met.
Description
technical field [0001] The invention relates to the technical field of metallurgy, in particular to a welding wire steel for manual argon arc welding. Background technique [0002] At present, with the rapid development of energy, petroleum, chemical industry, hydropower and other industries, engineering structures are becoming more and more large-scale and lightweight, and the demand for steel plates is also increasing, such as large crude oil storage tanks, large spherical Tanks, offshore oil production platforms, long-span bridge dyeing, large pipelines, etc. Low-alloy high-strength steel has good weldability, excellent formability and low manufacturing cost, so it is widely used in pressure vessels, vehicles, bridges, construction, construction machinery, mining machinery, textile machinery, marine structures and other fields. Among them, 690MPa low-alloy high-strength steel has been widely used. With the development of modern industry, the welding structure is developi...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.