Method for preparing modified environment-friendly corn starch adhesive
A technology of corn starch and adhesives, applied in the direction of starch adhesives, adhesive types, unsaturated alcohol copolymer adhesives, etc., can solve the problems of weak adhesion and poor water resistance, and achieve adhesive performance Strong, short curing time, the effect of improving the cross-linking effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0020] A modified environment-friendly corn starch adhesive, comprising the following components by weight: 30 parts of corn starch, 360 parts of water, 0.4 parts of potassium permanganate, 100 parts of polyvinyl alcohol, 3 parts of modified boric acid crosslinking agent, 4 parts of calcium chloride, 0.8 part of urea, 0.3 part of Q-119 type silicone defoamer, appropriate amount of sodium hydroxide (adjust pH value);
[0021] The preparation method of described modified environment-friendly cornstarch adhesive comprises the steps:
[0022] (1) Boric acid crosslinking agent modification: mix 100g of water, 25g of boric acid, 3g of epichlorohydrin and 1g of citric acid according to the mass ratio, add sodium hydroxide to adjust the pH value to 8-10, and heat up to 90°C for reaction After 60 minutes, after the reaction was completed, 20 mL of ethanol was added, stirring was continued for 15 minutes, and the modified boric acid crosslinking agent was obtained by filtering and dryin...
Embodiment 2
[0025] A modified environment-friendly cornstarch adhesive, comprising the following parts by weight: 30 parts of cornstarch, 360 parts of water, 1 part of potassium permanganate, 100 parts of polyvinyl alcohol, 3 parts of modified boric acid crosslinking agent, 4 parts of calcium chloride, 0.8 part of urea, 0.3 part of Y-610 type silicone defoamer, appropriate amount of sodium hydroxide (adjust pH value);
[0026] The preparation method of described modified environment-friendly cornstarch adhesive comprises the steps:
[0027] (1) Boric acid crosslinking agent modification: mix 100g of water, 21g of boric acid, 3g of epichlorohydrin and 0.8g of citric acid according to the mass ratio, add sodium hydroxide to adjust the pH value to 8-10, and heat up to 90°C React for 60 minutes. After the reaction is completed, add 15 mL of ethanol, continue to stir for 25 minutes, and filter and dry to obtain a modified boric acid crosslinking agent.
[0028] (2) Add 350g of water to the th...
Embodiment 3
[0030] A modified environment-friendly corn starch adhesive, comprising the following components by weight: 30 parts of corn starch, 380 parts of water, 0.6 parts of potassium permanganate, 110 parts of polyvinyl alcohol, 4 parts of modified boric acid crosslinking agent, 4 parts of calcium chloride, 2 parts of urea, 0.3 part of Y-610 type silicone defoamer, appropriate amount of sodium hydroxide (adjust pH value);
[0031] The preparation method of described modified environment-friendly cornstarch adhesive comprises the steps:
[0032] (1) Boric acid crosslinking agent modification: mix 100g of water, 28g of boric acid, 3g of epichlorohydrin and 1g of citric acid according to the mass ratio, add sodium hydroxide to adjust the pH value to 8-10, and heat up to 90°C for reaction After 60 minutes, after the reaction was completed, 15 mL of ethanol was added, stirring was continued for 25 minutes, and the modified boric acid crosslinking agent was obtained by filtering and drying...
PUM
Property | Measurement | Unit |
---|---|---|
adhesion strength | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com