Iron tailing micro-powder mortar dry powder for building mortar and preparation method thereof

A technology of mortar dry powder and iron tailings, which is applied in the field of building materials, can solve the problems of low fly ash and slag content, high mortar compression ratio, and low flexural strength, and achieve energy saving, simple production process, and high production efficiency. The effect of low cost and energy consumption

Active Publication Date: 2019-11-01
TIANJIN VOCATIONAL & TECHNICAL COLLEGE OF MECHANICAL & ELECTRICAL ENG
View PDF4 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to solve the technical problems existing in the known technology, the present invention provides a dry powder of iron tailings micropowder mortar for construction mortar and its preparation method, which solves the problem of low fly ash and slag content when the cementitious material is used in construction mortar, and the cost requirement Further reduce the problem, and solve the technical problems of low early strength, low flexural strength, high crushing ratio of mortar and poor crack resistance when fly ash and slag cementitious materials are used in construction mortar

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Iron tailing micro-powder mortar dry powder for building mortar and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0017] In order to further describe the present invention in detail, it will be described below in conjunction with the accompanying drawings and specific embodiments. In particular, the following examples are only for explanation of the present invention and the present invention is not limited to the following examples.

[0018] The present invention is a dry powder of iron tailings micropowder mortar for construction mortar, which is characterized in that: it includes the powder obtained by mixing the raw materials according to the following weight percentages and then homogenizing them twice: iron tailings micropowder: 70%-85%; P. O42.5R cement: 15%-30%; active stimulant: 0.1%-0.15%; the fineness of the iron tailings micropowder is 45μm square hole sieve not more than 5%, and the specific surface area is more than 500m 2 / kg; the cement is at least one of ordinary portland cement, aluminate cement, and sulphoaluminate cement of label 42.5R; Surface area greater than 360m ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention relates to iron tailing micro-powder mortar dry powder for building mortar. The iron tailing micro-powder mortar dry powder is obtained by mixing the following raw materials and carryingout two-time homogenization. The raw materials comprise, by weight, 70%-85% of iron tailing micro-powder, 15%-30% of P.O 42.5R cement, and 0.1%-0.15% of an active activator. The fineness of the irontailing micro-powder is that the screen residue of a 45 [mu]m square hole screen is not greater than 5%, and the specific surface area is greater than 500m <2> / kg. The cement is at least one of ordinary Portland cement, aluminate cement and sulphoaluminate cement with the label of 42.5R. The fineness of the cement is that the screen residue of a 45 [mu]m square hole screen is not greater than 3%.The specific surface area is greater than 360 m<2> / kg. The active excitant is a mixture of triethanolamine and potassium sulfate. According to the invention, the problem that the cost of the cementingmaterial for the building mortar needs to be further reduced is solved, and the technical problems of low early strength, low breaking strength, high mortar breaking ratio and poor crack resistance when the fly ash cementing material is used for the building mortar are solved. The industrial solid waste iron tailing micro powder can be comprehensively utilized, so that the environmental pollutionis reduced. Because the waste utilization amount is large, cement and lime are saved.

Description

technical field [0001] The invention belongs to the technical field of building materials, in particular to a dry iron tailings powder mortar powder for building mortar and a preparation method thereof. Background technique [0002] Construction mortar is widely used in masonry, plastering, repairing, grouting and pasting facing materials, etc. %-40% cement is used to prepare construction mortar. Due to the low strength grade of most construction mortars, there are very few low-strength grade cements for the preparation of mortars. In actual engineering, only higher-strength grade cements such as 32.5 or 42.5 grades are often used to prepare low-strength grade mortars. In order to improve the consistency It is convenient for construction, so cement has to be added in excess, resulting in waste of cement. [0003] In the traditional technology, when fly ash is used as raw material to produce cementitious materials, the amount of fly ash is usually below 35%, and when the am...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B28/06
CPCC04B28/04C04B28/06C04B40/0042C04B2201/50C04B18/12C04B24/121C04B22/147
Inventor 石光纪红李卫兵
Owner TIANJIN VOCATIONAL & TECHNICAL COLLEGE OF MECHANICAL & ELECTRICAL ENG
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products