Cement composition, foamed cement slurry, foamed concrete pouring material and preparation method thereof

A technology of cement composition and mud, which is applied in the field of foam concrete, can solve the problems of limited distribution of fast-hardening and quick-setting special cement, reduced foaming ability of foaming agent, poor sealing and toughness, etc., so as to shorten the curing time and foam The effect of enhanced stability and low cost

Inactive Publication Date: 2019-11-12
HENAN UNIV OF URBAN CONSTR
View PDF8 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

When Portland cement is used to make foam concrete, due to the poor sealing and toughness of the bubbles in the foam slurry, and the thin thickness of the bubble liquid film, the foam will burst during the block or in-situ casting process, resulting in the collapse of the new cast body. mold
In view of this problem, in the prior art, rapid-hardening and quick-setting special cement is used instead of Portland cement to prevent mold collapse by shortening the setting and hardening time of the cementitious material. This method has fast hardening speed and good foam-fixing effect, but the fast-hardening and quick-setting special The distribution of cement is not wide, the cost is high, and the strength is lower than that of ordinary portland cement
Another method to prevent mold collapse is to add a large amount of viscosifying substances such as carboxy cellulose and gelatin to the foaming agent to prevent mold collapse by increasing the foam viscosity. This method improves the stability of the foam, but due to the increase in the viscosity of the system , the foaming ability of the foaming agent decreases with the addition of viscosifying substances

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cement composition, foamed cement slurry, foamed concrete pouring material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The cement composition of this embodiment consists of the following components by weight fraction: 100 parts of Portland cement, 0.5 parts of foaming agent, 0.2 part of thixotropic agent, 0.5 part of tackifier, and 3 parts of early strength agent; The foaming agent is dodecylbenzenesulfonic acid, the thixotropic agent is zinc stearate, the tackifier is hydroxyethyl cellulose, and the early strength agent is lithium carbonate.

Embodiment 2

[0034] The cement composition of this embodiment is composed of the following components in parts by weight: 100 parts of Portland cement, 3 parts of foaming agent, 2 parts of thixotropic agent, 2 parts of tackifier, and 5 parts of early strength agent; The foaming agent used is ethoxylated alkyl sodium sulfate, the thixotropic agent is montmorillonite, the thickening agent is hydroxyethyl cellulose, and the early strengthening agent is lithium chloride.

Embodiment 3

[0036] The cement composition of this embodiment is composed of the following components by weight fraction: 100 parts of Portland cement, 1 part of foaming agent, 1.3 parts of thixotropic agent, 0.8 part of tackifier, 4 parts of early strength agent; The foaming agent is sodium α-alkenyl sulfonate, the thixotropic agent is fumed silica, the tackifier is gelatin, and the early strength agent is lithium carbonate.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a cement composition, a foamed cement slurry, a foamed concrete pouring material and a preparation method thereof, belonging to the technical field of foamed concrete. The cement composition of the invention comprises the following components in parts by weight: 100 parts by weight of Portland cement, 0.5 to 3 parts by weight of foaming agent, 0.2 to 2 parts by weight of thixotropic agent, 0.5 to 2 parts by weight of viscosifier and 3 to 5 parts by weight of early strength agent. By adding thixotropic agent, viscosifier and early strength agent, the thixotropy, viscosity and setting time of the foamed concrete can be changed, the mixing pulping process is beneficial to the foaming agent to foam and can ensure the stability of the foaming which is not easy to crack,thereby avoiding the problem of collapse mode of the foamed concrete pouring material adopting the Portland cement and making the foamed concrete have lower dry density.

Description

technical field [0001] The invention relates to a cement composition, foamed cement slurry, foamed concrete pouring material and a preparation method thereof, belonging to the technical field of foamed concrete. Background technique [0002] Concrete is currently the most widely used man-made building structure material. As a special variety of concrete, foam concrete has the advantages of light weight, heat preservation, heat insulation, sound insulation, non-combustibility, earthquake resistance, waste utilization, etc., and can well meet the requirements of building energy saving and building safety. Therefore, the application of foam concrete is becoming more and more more extensive. When foam concrete is prepared, the foaming agent is generally made into foam by mechanical foaming method, and then the foam is added to the cement slurry to form a foam slurry, which is cured after block or pouring. When Portland cement is used to make foam concrete, due to the poor seal...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B38/10
CPCC04B28/04C04B2201/20C04B2201/50C04B24/20C04B24/085C04B24/383C04B22/10C04B38/10C04B24/16C04B22/08C04B22/124C04B22/06C04B24/14
Inventor 李翔李子涵陈春耀陈群良许若翊任海波苏箐刘向云张艳花徐辉郭静怡夏学莲李辉
Owner HENAN UNIV OF URBAN CONSTR
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products